Synthesis of MgO–MgAl2O4 refractory aggregates for application in MgO–C slide plate
Source abstract
Abstract
Abstract This work provides an effective method for synthesis of MgO–MgAl2O4 (MgO-MA) aggregates with good thermal shock resistance (TSR) using lightly calcined magnesia and α-Al2O3 micro-powder as the starting materials. The effect of α-Al2O3 micro-powder amount and calcination temperature on TSR and microstructure of the synthesized MgO-MA aggregates was investigated. The optimum amount of α-Al2O3 micro-powder was 15 wt%, and the obtained aggregates had the highest density after calcination at 1650 °C. The synthesized MgO-MA aggregates had excellent TSR which was attributed to the thermal mismatch of MgO and MA grains as well as the pinning effect of MA grains on the periclase grain boundaries. TSR of MgO–C slide plate materials was improved significantly by introducing appropriate amount of the synthesized MgO-MA aggregates.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Magnesium Oxide Properties and Applications · Microwave Dielectric Ceramics Synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (24)
Show source-provided references
1. Improvement in alumina-carbon SN plates refractory durability with transition metal addition
2. Reaction mechanism of silicon and carbon in alumina carbon slide gate plate
3. Microstructures and mechanical properties of Al2O3-ZrO2-C refractories using silicon, microsilica or their combination as additive10.1016/j.msea.2012.03.013 ↗
4. Thermo-mechanical properties of Al/Si incorporated low carbon Al2O3-C slide plate materials
5. Evolution of phase composition and microstructure of Al2O3-Si-Al composite at high temperature in reducing atmosphere
6. Wear of Al2O3-C sliding nozzle plates by Ca-alloy treatment steel
7. Interaction between calcium and Al2O3-ZrO2-C slide gate plates10.1016/S2238-7854(12)70019-4 ↗
8. The basic slide gate plate for casting of Ca-alloy treated & High oxygen steel
9. Study on the improvement of thermal shock stability of carbon and oxide-based refractories by adding nanoparticles in terms of microstructures
10. Effect of micro and nano-Al2O3 addition on the microstructure and properties of MgO-C refractory ceramic composite10.1016/j.matchemphys.2016.12.068 ↗
11. Influence of Nanocrystalline MgAl2O4 spinel addition on the properties of MgO-C refractories10.1080/10426914.2010.544958 ↗
12. Improved thermal shock resistance of magnesia-graphite refractories by the addition of MgO-C pellets10.1016/j.matdes.2017.03.054 ↗
13. Functionalized cellular Carbon-MgO composites: from interface processing to thermal shock resistant low-carbon MgO-C refractories10.1002/adem.201300052 ↗
14. Effects of nanometer carbon black on performance of low-carbon MgO-C composites10.1016/S1006-706X(10)60187-2 ↗
15. Influence of microporous magnesia-rich spinel aggregates on properties of low carbon MgO-C refractories
16. Thermal shock resistance of mullite–cordierite refractories10.1179/096797803225001542 ↗
17. Improvement in spalling resistance of low carbon MgO-C bricks
18. Development of a low thermal conductivity MgO-C brick
19. Fracture behaviour of magnesia and magnesia-spinel composites before and after thermal shock10.1016/j.jeurceramsoc.2003.07.005 ↗
20. Thermal shock behaviour of high alumina aggregates derived from sillimanite beach sand with and without Fe2O3 doping10.1016/S0272-8842(99)00010-3 ↗
21. Thermal shock behaviour of magnesia-spinel composites10.1016/j.jeurceramsoc.2003.07.017 ↗
22. Materials science and engineering handbook
23. Effect of in situ spinel seeding on synthesis of MgO-rich MgAl2O4 composite10.1007/s10853-007-1546-5 ↗
24. Preparation and thermal shock behavior of nanoscale MgAl2O4 spinel-toughened MgO-based refractory aggregates10.1016/j.ceramint.2019.03.107 ↗