Carbide phases formed in WC–M (M=Fe/Ni/Cr) systems
Source abstract
Abstract
Abstract The effect of composition in the formation of carbides in the WC–M (M = Fe/Ni/Cr) system has been studied. Three conventional compositions have been prepared with 10 wt.% of metallic binder. Fe as a metallic binder was first studied and its partial substitution by Ni and Cr was also investigated. A WC powder coated with a similar binder (Fe/Ni/Cr) amount was also investigated. The XRD results, after thermal treatment at 1400 °C, reveal that the substitution of half percent of the iron content by Ni stabilized the austenite Fe(γ) formation. The introduction of Cr in the binder composition induces the formation of Cr2C carbide. With the decrease of Cr amount in the binder composition of the coated powder, Cr2C carbide was not formed, but instead other carbide, M6C, was detected. In order to eliminate this carbide a small excess of carbon (3.6 wt.%) was added to the coated powder. The results are discussed in terms of the phases formed, the binder composition and the final carbon content.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced materials and composites · Tunneling and Rock Mechanics · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. Production and indentation of WC/Fe–Mn as an alternative to cobalt-bonded hardmetals10.1016/S1044-5803(02)00181-X ↗
2. Martensitic transformations in cermets with a metastable austenitic binder. I. WC–(Fe–Ni–C)10.1016/0921-5093(91)90771-E ↗
3. Tungsten carbide hard metals cemented with ferroalloys
4. Phase diagrams as a tool for production and development of cemented carbides and steels10.1179/pom.1992.35.3.203 ↗
5. WC–(Fe, Ni, C) hardmetals with improved toughness through isothermal treatments10.1007/BF00349891 ↗
6. On the composition of Fe–Ni–Co–WC-based cemented carbides10.1016/S0263-4368(96)00023-6 ↗
7. Transformation-toughening in cemented carbides. Part I. Binder composition control10.1007/BF02647089 ↗
8. Abrasion resistant iron–nickel bonded tungsten carbide
9. Sintering of submicron WC–10wt.% Co hard metals containing nickel and iron10.1016/0025-5416(88)90503-4 ↗
10. Nickel in hardmetals10.1016/0263-4368(92)90056-8 ↗
11. Alternative binders for hardmetals
12. Aspects on nickel as a binder metal in WC-based cemented carbides
13. Stainless steel coatings sputter-deposited on tungsten carbide powder particles10.1016/S0257-8972(03)00021-5 ↗
14. Particle surface properties of stainless steel-coated tungsten carbide powders10.1016/j.powtec.2006.03.005 ↗
15. Sintering of tungsten carbide particles sputter-deposited with stainless steel10.1016/S0263-4368(03)00029-5 ↗
16. Control of eta carbide formation in tungsten carbide powders sputter-deposited with (Fe/Ni/Cr)10.1016/j.ijrmhm.2006.07.004 ↗
17. The Co–Fe–Ni–W–C phase diagram: a thermodynamic description and calculated sections for (Co–Fe–Ni) bonded cemented WC tools
18. Use of phase-diagram calculations in selecting the composition of Fe–Ni bonded WC tools
19. An assessment in the Fe–Ni–W–C phase diagram
20. A thermodynamic evaluation of the C–Fe–W system10.1007/BF02825699 ↗