Synthesis of CeO2/Pd nanocomposites by pulsed laser ablation in liquids for the reduction of 4-nitrophenol to 4-aminophenol

Abstract CeO 2 /Pd nanocomposites with high catalytic activity were synthesized by pulsed laser ablation in liquids. The size distribution, morphology, crystallinity, and optical properties of these nanostructures were determined by careful characterization using transmission electron microscopy (TEM), X-ray diffraction (XRD), UV−visible spectroscopy, and photoluminescence. The CeO 2 /Pd composites consisted of two-dimensional (2D) CeO 2 nanoplates with an average size of approximately 20 nm and spherically shaped Pd nanostructures with diameters of 9 nm. The synthesized composite showed a dual-band absorption spectrum with absorption maxima at 266 and 343 nm. The absorption band at 266 nm was assigned to typical inter-band transitions of a metallic Pd system. The other absorption peak, located at 343 nm, was the characteristic band of CeO 2 . The photoluminescence spectra showed more significant quenching of the blue emission from the CeO 2 /Pd composite compared with that of CeO 2 . The CeO 2 /Pd composite showed much higher catalytic activity than bare CeO 2 nanostructures toward the reduction of 4-nitrophenol to 4-aminophenol. The significant enhancement of the catalytic activity could be ascribed to the interaction between the CeO 2 and Pd nanostructures. The unique structure, high catalytic performance, and durability make these materials highly promising candidates for diverse applications in the area of catalysis.