Crystal structure and near-infrared reflective properties of Fe 3+ doped AlPO 4 pigments

Abstract Novel non-toxic orange yellow inorganic pigments Al1−xFexPO4(x=0.00, 0.03, 0.05, 0.08) with high near-infrared reflectance (NIR) have been synthesized by a coprecipitation method. The structures of samples were investigated by XRD and Raman spectroscopy, and the reflective properties were tested by UV–vis–NIR spectrophotometer. Results demonstrated that with more Fe3+ added, the color of the powder samples changed from white to orange yellow and the near-infrared reflectance decreased from 98.03% to 72.56%, which is higher than the commercial orange yellow pigment (61.99%). The near-infrared reflectance of corresponding coatings decreased from 69.35% to 59.10%, which is higher than the commercial coating with the similar color (51.88%). From the XRD diffraction spectrogram, we can see the peaks did not change with more Fe3+ added. However, because of ionic radius of Fe3+(0.63 A) is a little larger than Al3+(0.53 A), the cell volume increases a little when more Fe3+ is added. Furthermore, from the Raman spectrogram, we can see that doping with Fe3+, there is a new Raman peak which is assigned to the asymmetric [FeO4] stretch. In addition, replacing Fe3+ for Al3+ in AlPO4 caused the band gap decreased from 5.98eV to 3.60 eV, which can cause the absorption of more near-infrared radiation and that is the reason of the decrease of near-infrared reflectance.