Mechanisms governing the thermal shock and tensile fracture of PS-PVD 7YSZ TBC
Source abstract
Abstract
Abstract Thermal barrier coating (TBC) system including NiCoCrAlYTa metallic bond coating and 7YSZ (7 wt%Y2O3-ZrO2) ceramic top coating was deposited on nickel-based superalloy by plasma spray-physical vapor deposition (PS-PVD). Thermal shock property of 7YSZ TBC was characterized by water-quenching test at 1100 ℃ and its failure behaviors were investigated in detail. Besides, tensile test was performed for TBC sample and its cross-sectional fracture microstructure was studied as well. The results showed that after water-quenching test lots of pitting spallation took place in TBC surface, but no obvious microcracks were observed. Additionally, the tensile test indicated that fracture occurred in 7YSZ coating near the interface of ceramic-bond coating. After conduction of water-quenching and tensile testing, a lot of spherical particles and nano-sized agglomerated clusters were observed in the quasi-columnar structured 7YSZ coating. These lead to the formation of weak inter-column bonding and the failure of PS-PVD 7YSZ TBC. Moreover, in order to better understand the failure process, a deposition mechanism of coating was proposed.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Nuclear Materials and Properties · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Materials design for the next generation thermal barrier coatings10.1146/annurev.matsci.33.011403.113718 ↗
2. Thermal barrier coatings for enhanced efficiency of gas turbine engines10.1016/j.surfcoat.2006.06.026 ↗
3. Damage mechanisms, life prediction, and development of EB-PVD thermal barrier coatings for turbine airfoils10.1016/j.surfcoat.2007.06.067 ↗
4. Thermal cycling behavior of EB-PVD TBCs on CVD platinum modifiedaluminide coatings10.1016/j.jallcom.2015.02.177 ↗
5. Plasma spray-CVD: a new thermal spray process to produce thin films from liquid or gaseous precusors10.1007/s11666-011-9655-8 ↗
6. PS-PVD deposition of thermal barrier coatings10.1016/j.surfcoat.2013.09.028 ↗
7. plasma spray-PVD: plasma characteristics and impact on coating properties
8. Improved thermal cycling durability of thermal barrier coatings manufactured by PS-PVD10.1007/s11666-013-9971-2 ↗
9. Toughness and elasticity behaviors in nano-structured 7 wt% Y2O3-stablized ZrO2 coating10.1016/j.surfcoat.2015.07.005 ↗
10. Gas-deposition mechanisms of 7YSZ coating based on plasma spray-physical vapor deposition10.1016/j.jeurceramsoc.2015.10.041 ↗
11. Thermal cycling of EB-PVD MCrAlY thermal barrier coatings: microstructural development and spallation mechanisms10.1016/S0257-8972(01)01478-5 ↗
12. Tensile fracture behavior of thermal barrier coatings on superalloy10.1016/j.surfcoat.2011.02.005 ↗
13. Structure and durability evaluation of YSZ+Al2O3 composite TBCs with APS and HVOF bond coats under thermal cycling conditions10.1016/j.surfcoat.2011.04.081 ↗
14. Influence of cracks in APS-TBCs on stress around TGO during thermal cycling: a numerical simulation study10.1016/j.surfcoat.2015.11.036 ↗
15. Thermal shock behavior of EB-PVD thermal barrier coatings10.1016/j.surfcoat.2007.02.003 ↗
16. Numerical study on generation mechanism of vertical cracks in top coat of TBCs during APS deposition10.1007/s11666-015-0232-4 ↗
17. Investigation of the failure mechanism of thermal barrier coatings prepared by electron beam physical vapor deposition10.1016/S0257-8972(00)00693-9 ↗
18. Thermal cycling behavior of quasi-columnar YSZ coatings deposited by PS-PVD10.1007/s11666-016-0491-8 ↗
19. Microstructural characterization of PS-PVD ceramic thermal barrier coatings with quasi-columnar structures10.1016/j.surfcoat.2016.12.117 ↗
20. Investigations on the nature of ceramic deposits in plasma spray–physical vapor deposition10.1007/s11666-016-0513-6 ↗
21. Process conditions and microstructures of ceramic coatings by gas phase deposition based on plasma spraying10.1007/s11666-012-9838-y ↗
22. Z.Q. Deng, X.F. Zhang, K.S. Zhou, M. Liu, C.M. Deng, J. Mao, Z.K. Chen, 7YSZ Coating Prepared by PS-PVD Based on Heterogeneous Nucleation, Chin. J. Aeronaut., 〈http://dx.doi.org/10.1016/j.cja.2017.07.007〉.10.1016/j.cja.2017.07.007 ↗
23. Process-structure-property relations for the erosion durability of plasma spray-physical vapor deposition (PS-PVD) thermal barrier coatings10.1016/j.surfcoat.2016.04.029 ↗
24. Plasma characteristics and plasma-feedstock interaction under PS-PVD process conditions10.1007/s11090-014-9563-z ↗
25. Homogeneous nucleation of particles from the vapor phase in thermal plasma synthesis10.1007/BF01083672 ↗
26. Evaporation of droplets in plasma spray-physical vapor deposition based on energy compensation between self-cooling and plasma heat transfer10.1007/s11666-017-0610-1 ↗
27. Microstructures and deposition mechanisms of quasi-columnar structured yttria-stabilized zirconia coatings by plasma spray physical vapor deposition10.1016/j.ceramint.2017.06.190 ↗