Structural parameters and oxygen ion conductivity of Y2O3–ZrO2 and MgO–ZrO2 at high temperature

Abstract The oxygen ion conductivity of zirconia-based solid electrolytes doped with 8 mol% Y2O3–ZrO2 (YSZ) and 9 mol% MgO–ZrO2 (Mg-PSZ) at high temperature was investigated in terms of their thermal behavior and structural changes. At room temperature, YSZ showed a single phase with a fluorite cubic structure, whereas Mg-PSZ had a mixture of cubic, tetragonal and some monoclinic phases. YSZ exhibited higher ionic conductivity than Mg-PSZ at temperatures from 600 °C to 1250 °C because of the existence of the single cubic structure and low activation energy. A considerable increase in the conductivity with increasing temperature was observed in Mg-PSZ, which showed higher ionic conductivity than YSZ within the higher temperature range of 1300–1500 °C. A monoclinic-to-tetragonal phase transformation was found in Mg-PSZ and the lattice parameter of the cubic phase increased at 1200 °C. The phase transformation and the large lattice free volume contributed to the significant enhancement of the ionic conductivity of Mg-PSZ at high temperatures.