Preparation of porous TiO2 by a novel freeze casting

Abstract Highly porous and open interconnected pore structural TiO 2 were prepared by a novel freeze casting method. In the experiment, the well-dispersed aqueous slurries were first frozen, and then dried at a reduced vacuum. Since the sublimation of ice crystals developed in the freezing process, the green bodies with highly porous were obtained. The phase composition and the microstructure of the sintered samples were characterized by XRD, SEM, porosity and the pore size distribution was measured by mercury porosimetry. The results demonstrated that the PVA concentration in the slurries remarkably affect the microstructure of TiO 2 ceramics. The pore morphology of TiO 2 ceramics with 3 wt.% polyvinyl alcohol (PVA) addition was dendritic, and however, the pore morphology of TiO 2 ceramics with 6 wt.% PVA addition changed into columnar. The reason for the variation of the pore morphology was ascribed to the effect of the PVA gelation on the growth behavior of the ice crystals.