Effect of segmented cracks on TGO growth and life of thick thermal barrier coating under isothermal oxidation conditions
Source abstract
Abstract
Abstract This paper is devoted to a comparative study on the isothermal oxidation of thick thermal barrier coating (TTBC) with and without segmented cracks produced by atmospheric plasma spray (APS) process. Accordingly, the growth of thermally grown oxide (TGO) and its effect on the degradation of the coating were investigated. Thick top coat in both segmented crack and conventional thick TBC reduced the double layered TGO growth rate slightly. The segmented crack thick TBC demonstrated longer isothermal oxidation life in comparison with that of the conventional thick TBC at 1100 °C. The dominant failure mechanism was spallation due to lateral cracking within the TGO and/or within TBC near the TGO layer, called mixed failure. Stress, and consequently strain, induced on the TTBC due to progressive TGO growth, seems to be primarily responsible for the crack initiation and propagation leading to the coating failure. Increment of elastic energy stored within the top coat due to the increasing of TGO thickness, finally causes thick thermal barrier coating failure in high temperature isothermal oxidation.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Catalytic Processes in Materials Science · Flame retardant materials and properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (36)
Show source-provided references
1. On the performance and failure mechanism of thermal barrier coating systems used in gas turbine blade applications: influence of bond coat/superalloy combination10.1016/j.engfailanal.2015.07.023 ↗
2. Damage and performance assessment of protective coatings on turbine blades
3. TGO growth and crack propagation in a thermal barrier coating10.1007/s11666-008-9251-8 ↗
4. Effect of TGO thickness on the thermal barrier coatings life under thermal shock and thermal cycle loading10.1016/j.ceramint.2018.02.140 ↗
5. Lifetime evaluation of a thick thermal barrier coated superalloy used in turbine blade10.1016/j.msea.2010.06.005 ↗
6. Superior thermal barrier coatings using solution precursor plasma spray10.1007/s11666-004-0050-6 ↗
7. Failure modes in plasma-sprayed thermal barrier coatings10.1016/S0921-5093(02)00251-4 ↗
8. Mechanical properties of thermal barrier coatings after isothermal oxidation. Depth sensing indentation analysis10.1016/j.surfcoat.2009.02.035 ↗
9. Samadi · 2009
10. Atmospheric plasma sprayed thick thermal barrier coatings with high segmentation crack density10.1016/j.surfcoat.2004.01.002 ↗
11. Thermophysical properties and thermal cycling behavior of plasma sprayed thick thermal barrier coatings10.1016/j.surfcoat.2004.02.004 ↗
12. Atmospheric plasma sprayed thermal barrier coatings with high segmentation crack densities: spraying process, microstructure and thermal cycling behavior10.1016/j.surfcoat.2011.06.032 ↗
13. Failure mechanisms of dense vertically-cracked thermal barrier coatings10.1016/j.msea.2004.05.061 ↗
14. A numerical study on generation mechanism of vertical cracks in top coat of TBCs during APS deposition10.1007/s11666-015-0232-4 ↗
15. Evaluation of generation mechanism of vertical cracks in top coat of TBCs during APS deposition by laser AE method10.1007/s11666-015-0247-x ↗
16. Propagation feature of cracks in plasma-sprayed YSZ coatings under gradient thermal cycling10.1016/j.ceramint.2014.10.174 ↗
17. High temperature oxidation resistance of plasma sprayed and surface treated YSZ coating on Hastelloy X10.1016/j.surfcoat.2017.05.002 ↗
18. Cooling rate effect on phase transformation of plasma sprayed partially stabilized zirconia10.1023/A:1017937524472 ↗
19. An investigation on the microstructure and oxidation behavior of laser remelted air plasma sprayed thermal barrier coatings10.1016/j.surfcoat.2012.03.026 ↗
20. The influence of laser treatment on thermal shock resistance of plasma-sprayed nanostructured yttria stabilized zirconia thermal barrier coatings10.1016/j.ceramint.2013.06.008 ↗
21. The growth and influence of thermally grown oxide in a thermal barrier coating10.1016/j.surfcoat.2006.01.023 ↗
22. Determination of parabolic rate constants from a local analysis of mass-gain curves
23. Kinetics and mechanism of isothermal oxidation of compositionally graded yttria stabilized zirconia (YSZ) based thermal barrier coating10.1016/j.corsci.2014.06.050 ↗
24. TGO growth and crack propagation in a thermal barrier coating10.1007/s11666-008-9251-8 ↗
25. Degradation mechanism characterization and remaining life prediction for NiCoCrAlY coatings
26. Oxidation of conventional and nanostructured 8 wt.% yttria-stabilized zirconia coating surface coatings on γ-TiAl10.1016/j.apsusc.2015.01.192 ↗
27. Bose · 2007
28. Board · 1996
29. Diffusion cells and chemical failure of MCrAlY bond coats in thermal-barrier coating systems10.1023/A:1010369024142 ↗
30. Microstructure-based life prediction of thermal barrier coatings10.4028/www.scientific.net/KEM.592-593.413 ↗
31. Fox · 2004 · vol. 184 · 311
32. Microstructural evolution and growth kinetics of thermally grown oxides in plasma sprayed thermal barrier coatings10.1016/j.pnsc.2016.01.004 ↗
33. Microtexture of the thermally grown alumina in commercial thermal barrier coatings10.1016/j.scriptamat.2005.10.043 ↗
34. Thermal stability and mechanical properties of thick thermal barrier coatings with vertical type cracks10.1016/S1003-6326(14)63284-2 ↗
35. Uneven growth of thermally grown oxide and stress distribution in plasma-sprayed thermal barrier coatings10.1016/j.surfcoat.2009.03.031 ↗
36. Thermal cycling behavior of plasma sprayed segmented thermal barrier coatings10.2320/matertrans.47.306 ↗