Thermomechanical analysis of quartz porcelain in temperature cycles
Source abstract
Abstract
Abstract Samples made from a mixture of 50% kaolin and clay, 25% quartz and 25% feldspar were tested by non-destructive sonic resonant method, which is sensitive to the structure defects. Sound velocity and Young's modulus of the green samples were measured during a cooling stage of the firing from temperature 1250 °C. Fired samples were also measured in temperature cycles 20–800–20 °C to reveal a role of the quartz grains in porcelain structure. A microcracking was begun in the cooling stage at the glass phase transformation point (∼760 °C) and continued to room temperature as a consequence of different thermal expansions of phases. A sharp drop of the mechanical strength (∼25%) measured during cooling between 600 and 500 °C confirms an important function of the β → α transformation of quartz. Unsolved quartz grains decrease their volume and generate tensile stress in their close surroundings, which causes the microcracks. Sound velocity and Young's modulus of the fired samples evidenced hysteresis on heating and cooling, attributed to microcracking during cooling and healing the microcracks during heating in the region of the α–β transformation of quartz. Given those conditions, there follows a rapid change of the sound velocity (∼21%) and Young's modulus (∼46%).
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Building materials and conservation · Recycling and utilization of industrial and municipal waste in materials production · Glass properties and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. About the important correlation between microstructure properties and product quality of strength-stressed high-voltage insulators
2. Avoiding quartz in alumina porcelain for high-voltage insulators
3. Liebermann, J., Reliability of materials for high-voltage insulators. www.ceramicbulletin.org, Am. Ceram. Soc. Bull., (May) 2000.
4. Creep viscosity of vitreous china10.1111/j.1551-2916.2004.00923.x ↗
5. Effect of filler size on the strength of porcelain bodies
6. Porcelain microstructure and technical properties
7. Influence of SiO2 on mechanical properties of electroporcelain III: influence of the α–β transformation of quartz and cristobalite on mechanical strength
8. Influence of SiO2 on mechanical properties of electroporcelain II: influence of the α–β transformation of quartz and cristobalite on sound velocity
9. Interphasen-Effekte Teil I: In porösen keramischen Gefügen
10. Vazquez, S.B., Velasquez, J.C., Alumina additions affect elastic properties of electrical porcelains. www.ceramicbulletin.org, Am. Ceram. Soc. Bull., (April) 1998.
11. Effect of cristobalite formation on bending strength of alumina-strengthened porcelain bodies10.2109/jcersj.111.122 ↗
12. Ceramic properties of hard porcelain in relation to their mineralogical compositions and microstructures: I. Mechanical strength and Young's modulus of elasticity
13. Structure-property relationship in high-tension ceramic insulator fired at high temperature10.1016/j.mseb.2003.09.005 ↗
14. Bending strength of porcelains10.1016/S0272-8842(01)00068-2 ↗
15. Acoustic emission from a porcelain body during cooling10.1111/j.1551-2916.1999.tb20083.x ↗
16. ASTM C 1198-01 · 2001
17. Apparatus for thermomechanical analysis of ceramics
18. Schreiber · 1973
19. Thermal expansion of textured electroceramics
20. Thermal expansion anisotropy, microcracking and acoustic emission of Nb2O5 ceramics10.1016/0272-8842(92)90103-K ↗