Mechanical properties and rapid consolidation of binderless nanostructured tantalum carbide

Abstract The rapid sintering of nanostructured TaC hard material was investigated with a focus on the manufacturing potential of high-frequency induction heated sintering process. The advantage of this process is that it allows very quick densification to near theoretical density and prohibition of grain growth in nanostructured materials. A dense pure TaC hard material with a relative density of up to 96% was produced with simultaneous application of 80 MPa pressure and induced current within 3 min. The finer the initial TaC powder size, the higher the density and the better mechanical properties. The fracture toughness and hardness values obtained from 10 h milled powder were 5.1 ± 0.3 MPa m1/2 and 22 GPa, respectively, under 80 MPa pressure and 80% output of total power capacity (15 kW).