Production and characterization of self-colored dental zirconia blocks
Source abstract
Abstract
Abstract The objective of this study is to produce and characterize self-colored dental zirconia blocks by using zirconia raw material having Fe 2 O 3 content. Five different compositions with different amounts of Fe 2 O 3 were prepared by using two different raw materials. The shaped samples were sintered at 1500 °C for 2 h. Color differences, phase formations, microhardness, fracture toughness, and microstructures of the specimens were investigated. Self-colored zirconia blocks and frameworks of desired physical and mechanical properties for dental restorations can be produced by using zirconia raw material having Fe 2 O 3 content.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Dental materials and restorations · Bone Tissue Engineering Materials · Dental Implant Techniques and Outcomes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (22)
Show source-provided references
1. Fracture behaviour of Y-TZP ceramics: new outcomes10.1016/j.ceramint.2009.09.001 ↗
2. State of the art of zirconia for dental applications10.1016/j.dental.2007.05.007 ↗
3. From porcelain-fused-to-metal to zirconia: clinical and experimental considerations10.1016/j.dental.2010.10.024 ↗
4. What future for zirconia as a biomaterial?10.1016/j.biomaterials.2005.07.034 ↗
5. The firing procedure influences properties of a zirconia core ceramic10.1016/j.dental.2007.04.008 ↗
6. Reliability and properties of core materials for all-ceramic dental restorations10.1016/j.jdsr.2008.04.001 ↗
7. High-strength CAD/CAM-fabricated veneering material sintered to zirconia copings—a new fabrication mode for all-ceramic restorations10.1016/j.dental.2008.04.019 ↗
8. Color related to ceramic and zirconia restorations: a review10.1016/j.dental.2010.10.018 ↗
9. The color of Fe2O3 and Bi2O3 pigmented dental zirconia ceramic
10. Fracture toughness of nanocrystalline tetragonal zirconia with low yttria content10.1016/S1359-6454(02)00283-5 ↗
11. Characterization of glasses and ceramics by continuous indentation tests10.4028/www.scientific.net/KEM.103.217 ↗
12. ISE and fracture toughness evaluation by Vickers hardness testing of an Al3Nb–Nb2Al–AlNbNi in situ composite10.1016/j.jallcom.2008.04.016 ↗
13. L. Ćurković, V. Rede, K. Grilec, A. Mulabdić, Hardness and fracture toughness of alumina ceramics, in: Proceedings of the Conference on Materials, Processes, Friction and Wear MATRIB’07, vol. 12, Vela Luka, 2007, pp. 21–23.
14. Effect of ion-exchange temperature on mechanical properties of a dental porcelain10.1016/j.ceramint.2010.05.007 ↗
15. Fracture toughness (KIC), hardness, sintering and grain growth behavior of 8YSCZ/Al2O3 composites produced by colloidal processing10.1016/j.jallcom.2004.08.084 ↗
16. Fracture toughness of alumina–zirconia composites10.1016/j.ceramint.2005.02.012 ↗
17. Y-TZP ceramics with optimized toughness: new results10.1016/j.jallcom.2004.02.014 ↗
18. Comparison of three fracture toughness testing techniques using a dental glass and a dental ceramic10.1016/S0109-5641(98)00032-3 ↗
19. Fracture toughness evaluation of Wc–Co alloys by indentation testing
20. Enhancement of the martensitic transformation of tetragonal zirconia powder in the presence of iron oxide10.1016/S0921-5093(99)00374-3 ↗
21. XPS characterisation of ceria-stabilised zirconia doped with iron oxide10.1016/S0169-4332(98)00802-2 ↗
22. Effect of oxide additives on grain growth during sintering of nanocrystalline zirconia alloys10.1016/S0167-577X(97)00254-1 ↗