High-strength TiB 2 –TaC ceramic composites prepared using reactive spark plasma consolidation

Abstract This study demonstrates that reactive consolidation achieved via spark plasma sintering (SPS) is an effective strategy to enhance the high-temperature flexural strength of TiB 2 -based ceramics. Monolithic ceramics of TaC and TiB 2 were consolidated by non-reactive SPS and were used as reference samples. The microstructural development during room- and high-temperature strength tests was analyzed. The room-temperature strength of TiB 2 ceramics was analyzed as a function of the grain size. The high-temperature strength and associated microstructural development of monolithic TaC ceramics are reported for the first time. The TiB 2 –TaC ceramic system was then consolidated by reactive SPS at 2000 °C. The flexural strength of the 10 wt% TaC–TiB 2 ceramic composites reached 533 MPa at room temperature and 480 MPa at 1600 °С. The development of the (Ti,Ta)(C,B) phase was considered the main reason for the preservation of the high strength up to 1600 °С. Both bulk TaC and TiB 2 exhibited drastic decreases in their bending strengths at 1600 °С because of the activation of plastic deformation associated with high-temperature creep, and their strength did not exceed 210 MPa.