Brazing ZrO2 ceramic and TC4 alloy by novel WB reinforced Ag-Cu composite filler: Microstructure and properties

Abstract Residual stresses in ceramic-metal joints is the important factor for their reliable implementation in cutting-edge industries. Composite fillers is reported to be a promising approach to reduce the residual stresses. Until now, few experimental researches on the brazing of ZrO 2 ceramic and TC4 alloy using composite fillers have been reported. In this study, to release the residual stresses and improve the joints strength, novel WB reinforced Ag-Cu composite filler was fabricated to braze ZrO 2 ceramic and TC4 alloy. Scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and transmission electron microscopy (TEM) were applied for the analysis of microstructure and phases structure in the joints. The TiB whiskers and W particles were in situ synthesized via the reaction between active Ti and WB particles, and randomly distributed in the brazing seam. The effect of brazing temperature and WB content on interfacial microstructure and mechanical strength in the brazed joints were investigated. When brazed at 870 ??C for 10 min, favorable microstructure reinforced by TiB whiskers and W particles in the brazing seam was achieved with 7.5 wt% WB addition in composite filler. The maximum average shear strength of the joints was 83.2 MPa, which about 59.4% increase over the joints without WB addition.