Mechanical property evaluation of carbon nanotubes reinforced plasma sprayed YSZ-alumina composite coating
Source abstract
Abstract
Abstract Yttria (8%) stabilized zirconia (8YSZ)-alumina-carbon nanotube (CNT) composite coatings were deposited using air plasma spray (APS) technique. Three zirconia alumina (ZA) composite coatings, without CNT reinforcement, and with 1%CNT, 3%CNT reinforcement were deposited using identical process parameters (500 A and 66 V). Indentation method was used to characterize mechanical behavior of coatings. The CNT reinforced composite coating showed superior mechanical properties as compared to the conventional 8YSZ coating. The addition of alumina and 1%CNTs increased the Young's modulus by around 25% and 40%, respectively. However, the increase in CNT content decreased the Young's modulus as a result of CNT agglomeration. The hardness, fracture toughness increased with addition of alumina and CNT. The fracture toughness increased from 0.55 ± 0.26 MPa m 1/2 for 8YSZ to 1.76 ± 0.65 MPa m 1/2 for 17%alumina-3%CNT reinforcement due to various toughening mechanisms like crack deflection, bridging etc. The maximum displacement of indenter was found to decrease from ~ 176 nm for conventional YSZ coating to ~ 120 nm for 3% CNT reinforced coating. The surface roughness (Ra) was found to be decrease with alumina addition and CNT reinforced coating. The CNT reinforced coating showed surface roughness of around 6 µm. Scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) was used to characterize the coating microstructure and elemental composition respectively.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · High-Temperature Coating Behaviors · Diamond and Carbon-based Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (64)
Show source-provided references
1. Microstructure, composition and property relationships of plasma- sprayed thermal barrier coatings10.1016/0257-8972(92)90055-F ↗
2. R.A. Miller, History of thermal barrier coatings for gas turbine engines emphasizing NASA's role from 1942 to 1990, Nasa Tm—2009-215459, 215459, 2009, p. 29. 〈http://www.sti.nasa.gov〉.
3. Current status of thermal barrier coatings – an overview10.1016/0257-8972(87)90003-X ↗
4. 2 – Ceramic thermal barrier coating materials10.1533/9780857090829.1.25 ↗
5. Thermal cycle properties of plasma sprayed YSZ/Al2O3 thermal barrier coatings10.1179/026708408X343591 ↗
6. Hot corrosion of YSZ/Al2O3 dispersed NiCrAlY plasma-sprayed coatings in Na2SO4–10wt% NaCl melt10.1016/j.corsci.2010.04.007 ↗
7. Hot corrosion behavior of YSZ, Gd2Zr2O7 and YSZ/Gd2Zr2O7 thermal barrier coatings exposed to molten sulfate and vanadate salt
8. Porosity analysis and oxidation behavior of plasma sprayed YSZ and YSZ/LaPO4 abradable thermal barrier coatings10.1016/j.ceramint.2016.07.057 ↗
9. Failure analysis on abnormal corrosion of economizer tubes in a waste heat boiler10.1016/j.engfailanal.2016.12.011 ↗
10. Failure analysis of the wall tubes of a water-tube boiler10.1016/j.engfailanal.2017.05.032 ↗
11. Development and environmental durability of mullite and mullite/YSZ dual layer coatings for SiC and Si3N4 ceramics10.1016/S0257-8972(96)03074-5 ↗
12. Current status of environmental barrier coatings for Si-based ceramics
13. R.A. Miller, History of Thermal Barrier Coatings for Gas Turbine Engines, 2009.
14. Thermal cycle properties of plasma sprayed YSZ/Al 2 O 3 thermal barrier coatings10.1179/026708408X343591 ↗
15. A comparative study on hot corrosion resistance of three types of thermal barrier coatings: YSZ, YSZ + Al2O3 and YSZ/Al2O310.1016/j.msea.2007.06.001 ↗
16. Thermal shock resistance of Y-TZP with Palmqvist cracks10.1016/S0955-2219(02)00065-1 ↗
17. Thermal fracture of thermal barrier coatings in a high heat flux environment10.1016/S0257-8972(98)00485-X ↗
18. Characterization of microstructural defects in plasma-sprayed thermal barrier coatings10.1007/BF02646967 ↗
19. Studies on the behaviour of stellite-6 as plasma sprayed and laser remelted coatings in molten salt environment at 900°C under cyclic conditions10.1016/j.jmatprotec.2005.08.018 ↗
20. Bond coat oxidation and hot corrosion behavior of plasma sprayed YSZ coating on Ni superalloy †
21. Advanced ceramic materials for high temperature applications10.1002/adem.200500269 ↗
22. Phase stability and thermal conductivity of nanostructured tetragonal yttria–stabilized zirconia thermal barrier coatings deposited by air–plasma spraying10.1016/j.ceramint.2017.06.142 ↗
23. Engineered thermal barrier coatings deposited by suspension plasma spray10.1016/j.matlet.2017.08.096 ↗
24. Plasma spray deposition of tri-layer environmental barrier coatings10.1016/j.jeurceramsoc.2014.04.027 ↗
25. High-temperature erosion resistance of ZrB 2 -based ceramic coating for lightweight carbon / carbon composites under simulated atmospheric re-entry conditions by high frequency plasma wind tunnel test Outer-layered coating SiC whisker CBCFs (d)10.1016/j.ceramint.2016.03.029 ↗
26. Structure and thermal properties of heat treated plasma sprayed ceria-yttria co-stabilized zirconia coatings10.1016/j.ceramint.2009.10.020 ↗
27. Hot corrosion behaviour of plasma sprayed YSZ/LaMgAl11O19 composite coatings in molten sulfate-vanadate salt10.1016/j.corsci.2011.03.019 ↗
28. Hot corrosion of lanthanum zirconate and partially stabilized zirconia thermal barrier coatings10.1115/1.1924534 ↗
29. An investigation on oxidation, hot corrosion and mechanical properties of plasma-sprayed conventional and nanostructured YSZ coatings10.1016/j.surfcoat.2011.06.036 ↗
30. Nanostructured zirconia-30 vol% alumina composite coatings deposited by atmospheric plasma spraying10.1016/j.tsf.2005.02.040 ↗
31. Comparison of thermal shock resistances of plasma-sprayed nanostructured and conventional yttria stabilized zirconia thermal barrier coatings10.1016/j.ceramint.2012.05.060 ↗
32. Microstructural feature, thermal shock resistance and isothermal oxidation resistance of nanostructured zirconia coating10.1016/j.msea.2005.10.025 ↗
33. Influence of MoO3on boron aluminosilicate glass-ceramic coating for enhancing titanium high-temperature oxidation resistance10.1016/j.jallcom.2017.09.189 ↗
34. Hot corrosion resistance and mechanical behavior of atmospheric plasma sprayed conventional and nanostructured zirconia coatings10.1142/S201019451200267X ↗
35. Microstructural analysis of YSZ and YSZ/Al2O3 plasma sprayed thermal barrier coatings after high temperature oxidation10.1016/j.surfcoat.2007.11.029 ↗
36. Microstructural stability of zirconia-alumina composite coatings during hot corrosion test at 1050°C10.1016/j.jallcom.2010.06.110 ↗
37. Effect of strain rate and notch geometry on tensile properties and fracture mechanism of creep strength enhanced ferritic P91 steel10.1016/j.jnucmat.2017.10.037 ↗
38. An improved technique for detremining hardness and elastic modulas using load and displacement sensing indentation experiments10.1557/JMR.1992.1564 ↗
39. On the fundamental relation used in nanoindentation with piecewisely defined indenters10.1016/j.msea.2009.01.079 ↗
40. Relationships between the mode II fracture toughness and microstructure of thermal spray coatings10.1016/S0257-8972(99)00018-3 ↗
41. A critical evaluation of indentation techniques for measuring fracture toughness: I, direct crack measurement10.1111/j.1151-2916.1981.tb10320.x ↗
42. Role of powder treatment and carbon nanotube dispersion in the fracture toughening of plasma-sprayed aluminum oxide—carbon nanotube nanocomposite10.1166/jnn.2007.851 ↗
43. Carbon nanotubes stabilize high temperature phase and toughen Al 2 O 3 -based thermal barrier coatings10.1016/j.compositesb.2017.05.032 ↗
44. Effect of carbon nanotubes and aluminum oxide on the properties of a plasma sprayed thermal barrier coating10.1016/j.ceramint.2017.09.196 ↗
45. Effect of feedstock size and its distribution on the properties of detonation sprayed coatings10.1007/s11666-007-9032-9 ↗
46. Influences of atmospheric plasma spraying parameters on the porosity level of alumina coating on AZ31B magnesium alloy using response surface methodology10.1016/j.pnsc.2012.09.004 ↗
47. Effect of some parameters on microstructure and hardness of alumina coatings prepared by the air plasma spraying process10.1016/j.surfcoat.2004.02.007 ↗
48. Aluminum composite reinforced with multiwalled carbon nanotubes from plasma spraying of spray dried powders10.1016/j.surfcoat.2008.12.004 ↗
49. The effect of nanotube waviness and agglomeration on the elastic property of carbon nanotube-reinforced composites10.1115/1.1751182 ↗
50. Mechanical properties and fracture behaviour of ZrO2-Y203 ceramics10.1007/BF00554988 ↗
51. Chromium carbide–CNT nanocomposites with enhanced mechanical properties10.1016/j.actamat.2008.09.023 ↗
52. Nanoscratch behavior of carbon nanotube reinforced aluminum coatings10.1016/j.tsf.2009.11.079 ↗
53. Experimental and numerical investigation into the effect of carbon nanotube buckling on the reinforcement of CNT/Cu composites10.1016/j.compscitech.2013.02.003 ↗
54. R.F. Stapelberg, Handbook of Relaibilty, Availability, Maintainability and Safety in Engineering Design, n.d., https://doi.org/10.1007/978-1-84800-175-6.10.1007/978-1-84800-175-6 ↗
55. A statistical distribution function of wide applicability10.1115/1.4010337 ↗
56. High weibull modulus HVOF titania coatings10.1361/105996303770348357 ↗
57. Microstructure and indentation mechanical properties of plasma sprayed nano-bimodal and conventional ZrO 2 e8wt%Y 2 O 3 thermal barrier coatings10.1016/j.vacuum.2011.10.029 ↗
58. Effect of thermal exposure on hardness and Young's modulus of EB-PVD yttria-partially-stabilized zirconia thermal barrier coatings10.1016/j.ceramint.2005.01.018 ↗
59. Porosity, mechanical properties, residual stresses of supersonic plasma-sprayed Ni-based alloy coatings prepared at different powder feed rates10.1016/j.apsusc.2007.12.023 ↗
60. Effect of carbon nanotube (CNT) content on the mechanical properties of CNT-reinforced aluminium composites10.1016/j.compscitech.2010.05.004 ↗
61. The role of surfactants in dispersion of carbon nanotubes10.1016/j.cis.2006.11.007 ↗
62. Effect of CNT waviness on the effective mechanical properties of long and short CNT reinforced composites10.1016/j.commatsci.2014.06.034 ↗
63. Enhanced fracture toughness in carbon-nanotube-reinforced amorphous silicon nitride nanocomposite coatings10.1016/j.actamat.2012.02.046 ↗
64. Effect of far-field stresses and residual stresses incorporation in predicting fracture toughness of carbon nanotube reinforced yttria stabilized zirconia10.1063/1.4990731 ↗