Glass–ceramics as oxidation resistant bond coat in thermal barrier coating system
Source abstract
Abstract
Abstract Thermal barrier coating (TBC) system consisting of yttria stabilized zirconia (YSZ) top coat, glass–ceramic bond coat and nickel base superalloy substrate was subjected to static oxidation test at 1200 °C for 500 h in air. Oxidation resistance of this TBC system was compared with the conventional TBC system under identical heat treatment condition. Both the TBC systems were characterized by SEM as well as EDX analysis. No TGO layer was found between the bond coat and the top coat in the case of glass–ceramic bonded TBC system while the conventional TBC system exhibited a TGO layer of about 16 μm thickness at the bond coat-top coat interface region.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Nuclear Materials and Properties · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (10)
Show source-provided references
1. An experimental investigation on thermo-mechanical buckling delamination failure characteristic of air plasma sprayed thermal barrier coatings10.1016/j.surfcoat.2006.11.025 ↗
2. The effect of thermal barrier coatings on diesel engine performance10.1016/j.surfcoat.2006.07.123 ↗
3. Modelling of TBC system failure: Stress distribution as a function of TGO thickness and thermal expansion mismatch10.1016/j.engfailanal.2004.12.027 ↗
4. Oxidation and crack nucleation/growth in an air-plasma-sprayed thermal barrier coating with NiCrAlY bond coat10.1016/j.surfcoat.2004.06.027 ↗
5. Modification of oxide layer in plasma-sprayed thermal barrier coatings10.1016/j.surfcoat.2005.08.141 ↗
6. Effect of thermally grown oxide (TGO) microstructure on the durability of TBCs with PtNiAl diffusion bond coats10.1016/j.msea.2005.11.014 ↗
7. Improved oxidation resistance of thermal barrier coatings10.1016/S0257-8972(99)00345-X ↗
8. Substrate and bond coat compositions: factors affecting alumina scale adhesion10.1016/S0921-5093(97)00851-4 ↗
9. Thermal barrier coatings with improved oxidation resistance10.1016/0257-8972(94)90147-3 ↗
10. Mechanical properties and oxidation resistance of plasma-sprayed multilayered Al2O3/ZrO2 thermal barrier coatings10.1016/j.surfcoat.2005.02.087 ↗