Transparency of K0.5N0.5NbO3–Sr(Mg1/3Nb2/3)O3 lead-free ceramics modulated by relaxor behavior and grain size

Abstract High transparency was obtained in (1− x )(K 0.5 Na 0.5 )NbO 3 – x Sr(Mg 1/3 Nb 2/3 )O 3 ( x =0.02, 0.03, 0.04, 0.05, 0.06, 0.07, 0.08) lead-free ceramics by pressure-less sintering procedure. The effects of Sr(Mg 1/3 Nb 2/3 )O 3 content on the microstructure, phase transition, optical properties and electrical properties were studied in detail. The X-ray diffraction results showed that the crystal structure of ceramics gradually transformed from orthorhombic phase into pseudo-cubic phase with doping of Sr(Mg 1/3 Nb 2/3 )O 3 . The fine grain microstructure with clear grain boundary was observed in all compositions, while the grain size exhibited significant composition dependence. It was found that a more uniform distribution with smaller grain size was favorable to high optical transmittance, owing to the decreased scattering by grains and grain boundaries. In addition, a strong diffuse phase transformation in KNN-based ceramics induced by Sr(Mg 1/3 Nb 2/3 )O 3 doping, causing the ceramics become more relaxor-like and transparent. The transmittance and electric properties results indicated that the 0.95(K 0.5 Na 0.5 )NbO 3 –0.05 Sr(Mg 1/3 Nb 2/3 )O 3 ceramics exhibited higher transmittance (60% in the near-IR region) accompanied with better electrical properties ( e m =2104, P r =5.0 μC/cm 2 , d 33 =92 pC/N).