Wetting of AgCu-Ti filler on porous Si3N4 ceramic and brazing of the ceramic to TiAl alloy
Source abstract
Abstract
Abstract The effect of Ti content on the wettability of AgCu-Ti filler on porous Si3N4 ceramic was studied by the sessile drop method. AgCu-2 wt% Ti filler alloy showed a minimum contact angle of 14.6° on porous Si3N4 ceramic during the isothermal wetting process. The mechanism of AgCu-Ti filler wetting on porous Si3N4 ceramic is clarified in this paper. Porous Si3N4 ceramic was brazed to TiAl alloy using AgCu-xTi (x = 0, 2 wt%, 4 wt%, 6 wt%, 8 wt%) filler alloy at 880 °C for 10 min. The effect of Ti content on the interfacial microstructure and mechanical properties of porous-Si3N4/AgCu-xTi/TiAl joints are studied. The typical interfacial microstructure of p-Si3N4/AgCu-Ti/TiAl joint is p-Si3N4/penetration layer (Ag(s,s)+Si3N4+TiN+Ti5Si3)/Ag(s,s)+Cu(s,s)+TiCu/AlCu2Ti/TiAl. The maximum shearing strength of the brazed joint was 14.17 MPa and fracture that occurred during the shearing test propagated in the porous Si3N4 ceramic substrate for the formation of the penetration layer.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. Progress in joining ceramics to metals10.1016/S1006-706X(06)60032-0 ↗
2. Joining of dissimilar materials10.1016/j.cirp.2015.05.006 ↗
3. The role of wettability in metal–ceramic joining10.1016/j.scriptamat.2010.03.007 ↗
4. Liquid metal wettability and advanced ceramic brazing10.1016/j.jeurceramsoc.2007.07.021 ↗
5. Wettability of silicon nitride ceramic composites by silver, copper and silver copper titanium alloys10.1016/j.jeurceramsoc.2004.12.005 ↗
6. Silicon nitride and related materials10.1111/j.1151-2916.2000.tb01182.x ↗
7. Strength and microstructure of brazed cemented carbide and silicon nitride joints10.1016/0924-0136(95)02103-5 ↗
8. Interfacial behavior in the brazing of silicon nitride joint using a Nb-foil interlayer10.1016/j.jmatprotec.2012.09.019 ↗
9. Brazing of Si3N4 ceramic to copper10.1016/S0924-0136(97)00427-5 ↗
10. Interfacial microstructure and joining properties of TiAl/Si3N4 brazed joints10.1016/j.msea.2011.05.079 ↗
11. Formation of interfacial microstructure in brazing of Si3N4 with Ti-actived Ag-Cu filler alloys10.1016/0956-716X(95)00127-H ↗
12. Characterization of the Si3N4/Si3N4 joints fabricated using particles modified braze10.1016/j.msea.2014.08.023 ↗
13. Brazing TC4 alloy to Si3N4 ceramic using nano-Si3N4 reinforced AgCu composite filler10.1016/j.matdes.2015.03.046 ↗
14. Microstructure evolution of Si3N4/Si3N4 joint brazed with Ag–Cu–Ti+SiCp composite filler10.1016/j.ceramint.2010.02.010 ↗
15. Titanium metallization of Si3N4 ceramics by molten salt reaction: coating microstructure and brazing property10.1016/S0040-6090(02)00950-1 ↗
16. Nanostructure of wetting triple line in a Ag–Cu–Ti/Si3N4 reactive system10.1016/S1359-6454(98)00375-9 ↗
17. Dielectric and mechanical properties of porous Si3N4 ceramics prepared via low temperature sintering10.1016/j.ceramint.2008.09.010 ↗
18. Development and evaluation of TiAl sheet structures for hypersonic applications10.1016/j.msea.2007.02.020 ↗
19. Effect of porosity and microstructure on the strength of Si3N4 designed microstructure for high strength, high thermal shock resistance, and facile machining10.1111/j.1151-2916.1997.tb03179.x ↗
20. Microstructure and mechanical properties of silicon nitride ceramics with controlled porosity10.1111/j.1151-2916.2002.tb00305.x ↗
21. Microstructure and mechanical properties of three porous Si3N4 ceramics fabricated by different techniques10.1016/j.msea.2012.03.114 ↗
22. Effects of roughness on the wettability of high temperature wetting system10.1016/j.surfcoat.2015.12.092 ↗
23. Wettability of aluminium nitride based ceramics of different porosity by two active silver based brazing alloys10.1016/j.msea.2004.02.021 ↗
24. Interfacial microstructure and mechanical properties of porous-Si3N4 ceramic and TiAl alloy joints vacuum brazed with AgCu filler10.1016/j.ceramint.2017.04.149 ↗
25. Microstructure and mechanical properties of porous Si3N4 /Invar joints brazed with Ag-Cu-Ti+Mo/Cu/Ag-Cu multi-layered composite filler10.1016/j.ceramint.2017.05.354 ↗
26. Brazing continuous carbon fiber reinforced Li2O–Al2O3–SiO2 ceramic matrix composites to Ti–6Al–4V alloy using Ag–Cu–Ti active filler metal10.1016/j.matdes.2015.08.005 ↗
27. Thermal expansion of metal–ceramic composites: a three-dimensional analysis10.1016/S0921-5093(98)00698-4 ↗
28. Wettability and pressureless infiltration mechanism in SiC-Cu systems10.1016/S1674-4799(09)60059-5 ↗
29. Joining of silicon nitride with a Cu76.5Pd8.5Ti15 filler alloy10.1016/j.ceramint.2005.10.016 ↗
30. Brazing of Si3N4 with amorphous Ti40Zr25Ni15Cu20 filler10.1016/j.msea.2008.11.056 ↗
31. Effect of Ti content on microstructure and strength of Si3N4/Si3N4 joints brazed with Cu–Pd–Ti filler metals10.1016/j.msea.2008.02.027 ↗
32. Villars · 1995
33. Interfacial microstructure of induction brazed joints of TiAl-based intermetallics to steel 35CrMo with AgCuNiLi filler10.1016/j.msea.2005.08.009 ↗