Ablation behavior of C/C-ZrC-SiC composites prepared by reactive melt infiltration under oxyacetylene torch at two heat fluxes

Zhigang Zhao, Kezhi Li, Wei Li, Qing Liu, Gang Kou, Yulei Zhang

Ceramics International· Volume 44· Issue 14
Publisher page

Abstract

Abstract C/C-ZrC-SiC composites were prepared by reactive melt infiltration and tested using an oxyacetylene torch with the heat fluxes of 4.18 and 2.38 MW/m 2 . The results showed that compared to C/C and C/C-SiC at the heat flux of 4.18 MW/m 2 , the mass ablation rates of C/C-ZrC-SiC were decreased by 60.8% and 44.8%, respectively. Its linear ablation rate was 7.3% higher than that of C/C, but was 13.5% lower than that of C/C-SiC. The C-SiC matrix and fibers of C/C-SiC in the center region were severely depleted by the high ablation temperature. C/C-ZrC-SiC composites experienced the temperature exceeding 2400 °C associated with intense mechanical scouring of gas flow. The severe depletion of SiC and carbon fibers on the surface led to the formation of the porous ZrO 2 layer. The spallation of ZrO 2 occurred in the center of the ablated surface as a result of mechanical denudation of high temperature gas flow. At the heat flux of 2.38 MW/m 2 , the mass and linear ablation rates of C/C-ZrC-SiC were decreased by 76.8% and 88.4% (C/C), 66.9% and 58.3% (C/C-SiC), respectively. The oxide was slightly peeled off in the center region of C/C-SiC. The surface temperatures of C/C-SiC and C/C-ZrC-SiC were lower than that of C/C composites. The island-like ZrO 2 and SiO 2 layer were formed on the ablated surface of C/C-ZrC-SiC and acted as effective barriers to shield the ablation heat and slow inward transport of oxygen to the underlying material.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · Diamond and Carbon-based Materials Research

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (43)

Show source-provided references
1. Fitzer · 1998 · 250
2. Multiphysics coupled fluid/thermal/ablation simulation of carbon/carbon composites10.2514/1.A33612 ↗
3. Oxidation behavior and protection of carbon/carbon composites10.1016/0008-6223(87)90197-7 ↗
4. Advanced structural ceramics in aerospace propulsion10.1038/nmat4687 ↗
5. Refractory diborides of zirconium and hafnium10.1111/j.1551-2916.2007.01583.x ↗
6. Ultra-high temperature ceramics: materials for extreme environments10.1016/j.scriptamat.2016.10.018 ↗
7. Ablation behavior and mechanism of C/C–ZrC–SiC composites under an oxyacetylene torch at 3000 °C10.1016/j.ceramint.2012.10.273 ↗
8. Cyclic ablation behavior of C/C-ZrC-SiC composites under oxyacetylene torch10.1016/j.ceramint.2013.10.069 ↗
9. Effects of porous C/C density on the densification behaviour and ablation property of C/C–ZrC–SiC composites10.1016/j.carbon.2013.01.059 ↗
10. Ablation behaviour of C/C and C/C–ZrC–SiC composites with cone-shaped holes under an oxyacetylene flame10.1016/j.corsci.2015.09.022 ↗
11. Microstructure and ablation behaviors of a novel gradient C/C-ZrC-SiC composite fabricated by an improved reactive melt infiltration10.1016/j.ceramint.2016.07.190 ↗
12. Microstructure and mechanical properties of C/C–ZrC–SiC composites fabricated by reactive melt infiltration with Zr, Si mixed powders10.1016/j.jmst.2013.05.005 ↗
13. Microstructures and ablation properties of C/C-SiC-ZrC composites prepared using C/C skeletons with various densities10.1016/j.ceramint.2013.03.093 ↗
14. C/C–SiC–ZrC composites fabricated by reactive melt infiltration with Si0.87Zr0.13 alloy10.1016/j.ceramint.2012.02.016 ↗
15. Qualitative analysis of hafnium diboride based ultra high temperature ceramics under oxyacetylene torch testing at temperatures above 2100 °C10.1016/j.jeurceramsoc.2013.11.018 ↗
16. Heat flux mapping of oxyacetylene flames and their use to characterise Cf-HfB2 composites10.1080/17436753.2015.1104050 ↗
17. Microstructure and ablation properties of zirconium carbide doped carbon/carbon composites10.1016/j.carbon.2009.09.035 ↗
18. Oxidation behavior of aerospace materials in high enthalpy flows using an oxyacetylene torch facility10.1111/jace.13462 ↗
19. Flash method of determining thermal diffusivity, heat capacity, and thermal conductivity10.1063/1.1728417 ↗
20. National Standard Committee of China, GJB323A-96: measurement standard of ablation properties of materials, Beijing, 1996.
21. Effect of heat flux on ablation behaviour and mechanism of C/C–ZrB2–SiC composite under oxyacetylene torch flame10.1016/j.corsci.2013.04.052 ↗
22. Chase · 1998
23. 3D Cf/SiC-ZrC-ZrB2 composites fabricated via sol-gel process combined with reactive melt infiltration10.1016/j.jeurceramsoc.2016.04.011 ↗
24. Kinetics model for the growth of silicon carbide by the reaction of liquid silicon with carbon10.1111/j.1151-2916.1995.tb08685.x ↗
25. Effect of oxidation on elastic modulus of C/C–SiC composites10.1016/j.msea.2007.09.078 ↗
26. UHTC-carbon fiber composites: preparation, oxyacetylene torch testing and characterization10.1016/j.jeurceramsoc.2012.08.018 ↗
27. Modelling of carbon–carbon composite ablation in rocket nozzles10.1016/j.compscitech.2010.04.002 ↗
28. Improved ablation resistance of carbon–phenolic composites by introducing zirconium silicide particles10.1016/j.compositesb.2015.08.023 ↗
29. Growth mechanism of silica nanowires without a metal catalyst via oxyacetylene torch ablation10.1016/j.matlet.2012.01.056 ↗
30. Oxidation-resistant ZrB2–SiC composites at 2200 °C10.1016/j.compscitech.2007.08.017 ↗
31. Aerothermal behaviour of a SiC fibre-reinforced ZrB2 sharp component in supersonic regime10.1016/j.jeurceramsoc.2012.01.019 ↗
32. Ablative property of HfC based multilayer coating for C/C composites under oxy-acetylene torch10.1016/j.apsusc.2010.11.020 ↗
33. Microstructure and ablation mechanism of C/C–SiC composites10.1016/j.jeurceramsoc.2013.08.026 ↗
34. Pierson · 1996 · 145
35. Effects of ZrB2 and SiC dual addition on the oxidation resistance of graphite at 1600–2000 °C10.1016/j.corsci.2013.06.041 ↗
36. Mechanical and ablation properties of 2D-carbon/carbon composites pre-infiltrated with a SiC filler10.1016/j.carbon.2006.06.003 ↗
37. Ablation behaviors of ultra-high temperature ceramic composites10.1016/j.msea.2007.02.040 ↗
38. Ablation behavior of ZrB2–SiC ultra high temperature ceramics under simulated atmospheric re-entry conditions10.1016/j.compscitech.2008.02.009 ↗
39. Corrosion of silicon-based ceramics in combustion environments10.1111/j.1151-2916.1993.tb03684.x ↗
40. Oxidation of ultrahigh temperature ceramics in water vapor10.1149/1.1786929 ↗
41. The ZrB2 volatility diagram10.1111/j.1551-2916.2005.00599.x ↗
42. Thermodynamic analysis of ZrB2–SiC oxidation: formation of a SiC-depleted region10.1111/j.1551-2916.2006.01329.x ↗
43. Thermoablative resistance of ZrB2-SiC-WC ceramics at 2400 °C10.1016/j.actamat.2017.05.033 ↗