Fabrication of micro-scale textured grooves on green ZrO 2 ceramics by pulsed laser ablation

Abstract The green ZrO 2 ceramics were fabricated by cold isostatic pressing. Pulsed laser ablation with a wavelength of 1064 nm was performed to fabricate micro-scale textured grooves on the surface of green ZrO 2 ceramics. The influence of laser parameters on surface quality was studied. The heat-affected zone around the machined grooves and micromorphology of laser-irradiated surface were investigated. Results showed that micro-scale textured grooves with a width of 30–50 µm and a depth of 15–50 µm on the green ZrO 2 ceramic surfaces were successfully fabricated by pulsed laser ablation. The laser parameters had a profound influence on the surface quality of micro-scale textured grooves. Better surface quality could be obtained with frequency below 40 Hz, power below 6 W, and scanning velocity above 200 mm/s. A sintering layer was found on the laser-irradiated surfaces when frequency was above 60 Hz, power was above 10 W, and scanning velocity was below 150 mm/s. Analysis of this sintering layer revealed clear melting and resolidification of ZrO 2 particles.