Effect of BN content on microstructures, mechanical and dielectric properties of porous BN/Si3N4 composite ceramics prepared by gel casting

Abstract Porous BN/Si 3 N 4 composite ceramics with different BN contents have been fabricated by gel casting. The rheological behaviors of the suspensions, microstructure, mechanical properties, dielectric properties and critical temperature difference of thermal shock (Δ T C ) of porous BN/Si 3 N 4 composite ceramics with different BN contents were investigated. With BN contents increasing, the mechanical properties of the porous BN/Si 3 N 4 composite ceramics were partially declined, but the dielectric properties and thermal shock resistances were enhanced at the same time. For the porous Si 3 N 4 ceramic without BN addition, the porosity, flexural strength, dielectric constant and critical temperature difference were 48.1%, 128 MPa, 4.1 and 395 °C, while for the 10 vol% BN/Si 3 N 4 porous composite ceramics, they were 49.4%, 106.6 MPa, 3.8, and 445 °C, respectively. The overall performance of the obtained porous BN/Si 3 N 4 composite ceramics indicated that it could be one of the ideal candidates for high-temperature wave-transparent applications.