Strengthening mechanism of graphene oxide nanosheets for Al2O3–C refractories
Source abstract
Abstract
Abstract Al 2 O 3 –C refractories containing graphene oxide nanosheets (GONs) and additives of Al, Si and SiO 2 were prepared. The GONs/ α -Al 2 O 3 composite powders were prepared by ball milling expanded graphite (EG) with micron sized α -Al 2 O 3 , and then used to make the Al 2 O 3 –C refractory specimens. The results showed that GONs were distributed well in α -Al 2 O 3 powder by ball milling, and the size and thickness of GONs depended on the amount of expanded graphite added. The GONs enhanced the formation of ceramic whiskers in the specimens at lower temperature owing to their higher reactivity than graphite flake. The mechanical properties such as cold modulus of rupture (CMOR), flexural modulus ( E ), force and displacement curves of Al 2 O 3 –C refractories with GONs were improved compared with those without GONs. This improvement was attributed to the strengthening effects of GONs at 800 °C and the synergetic strengthening effects with graphite flake and the in-situ formed whiskers at 1000–1400 °C.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Aluminum Alloys Composites Properties · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Carbon based refractories
2. Effects of resin and graphite content on density and oxidation behavior of MgO–C refractory bricks10.1016/j.ceramint.2005.03.008 ↗
3. Atmosphere and carbon effects on microstructure and phase analysis of in situ spinel formation in MgO–C refractories matrix10.1016/j.ceramint.2008.03.001 ↗
4. Influence of additives on corrosion resistance and corroded microstructures of MgO-C refractories10.1016/S0955-2219(01)00208-4 ↗
5. High temperature mechanical behavior of Al2O3–MgO–C refractories for steelmaking use10.1016/j.ceramint.2010.12.019 ↗
6. Effects of nanometer carbon black on performance of low-carbon MgO–C composites10.1016/S1006-706X(10)60187-2 ↗
7. Influences of black carbon addition on mechanical performance of low-carbon MgO–C composite10.1016/S1006-706X(10)60201-4 ↗
8. Effect of multi-walled carbon nanotubes on the thermal conductivity and pore characteristic of blast furnace carbon refractories10.1007/s11661-010-0300-9 ↗
9. Study on low carbon containing MgO–C refractory: use of nano carbon10.1016/j.ceramint.2011.10.086 ↗
10. Characteristics and application of nano-tech magnesia carbon bricks
11. Nano-tech refractories-1: the development of the nano structural matrix
12. Mechanical properties of SiC composites incorporating SiC-coated multi-walled carbon nanotubes10.1016/j.ijrmhm.2006.08.005 ↗
13. Reinforcement of mullite matrix with multi-walled carbon nanotubes10.1016/j.ceramint.2005.12.009 ↗
14. Microstructures and mechanical properties of Al2O3–C refractories with addition of multi-walled carbon nanotubes10.1016/j.msea.2012.04.001 ↗
15. Improved thermal shock performance of Al2O3–C refractories due to nanoscaled additives10.1016/j.ceramint.2011.08.011 ↗
16. Nano- and micrometre additions of SiO2, ZrO2 and TiO2 in fine grained alumina refractory ceramics for improved thermal shock performance
17. Microstructure evaluation of MgO-C refractories with TiO2- and Al-additions10.1016/j.jeurceramsoc.2006.03.001 ↗
18. The effect of antioxidants on the oxidation behaviour of magnesia-carbon refractory bricks10.1016/j.ceramint.2006.10.004 ↗
19. Formation of dumbbell-shaped β-SiC whiskers in advanced refractories for Al2O3–ZrO2–C slide gate
20. Determination of structural and mechanical properties of multilayer graphene added silicon nitride-based composites10.1016/j.ceramint.2011.06.051 ↗
21. Reinforcing effects of adding alkylated graphene oxide to polypropylene10.1016/j.carbon.2011.04.055 ↗
22. Functionalized graphene sheets for polymer nanocomposites10.1038/nnano.2008.96 ↗
23. Preparation of graphene nanosheet/alumina composites by spark plasma sintering10.1016/j.materresbull.2010.11.005 ↗
24. Microstructures and mechanical properties of Al2O3–C refractories with silicon additive using different carbon sources10.1016/j.msea.2010.12.066 ↗
25. Preparation of expanded graphite with 160μm mesh of fine flake graphite10.1016/j.matlet.2005.10.004 ↗
26. Study on preparation of activated mesocarbon microbeads/expanded graphite composites for electrical double layer capacitors10.1016/j.compscitech.2006.11.011 ↗
27. Preparation and electrical properties of graphene nanosheet/Al2O3 composites10.1016/j.carbon.2010.01.017 ↗
28. Carbothermic reduction synthesis of Ti(C, N) powder in the presence of molten salt10.1016/j.ceramint.2007.03.016 ↗
29. Effect of temperature on the properties and microstructures of carbon refractories for blast furnace (BF)10.1007/s11661-009-9850-0 ↗
30. Hu · 2008
31. A new method for the derivation of activation energies from experiments performed at constant heating rate10.1016/S0040-6031(96)03053-5 ↗