Size-controlled high magnetization CoFe2O4 nanospheres and nanocubes using rapid one-pot sonochemical technique

Abstract Highly crystalline single phase spherical and monodisperse cobalt ferrite (CoFe 2 O 4 ) nanoparticles (NPs) with uniform shape and size distribution have been synthesized by one pot-rapid sonochemical method. The effect of different solvents, such as aqueous, alcoholic, and a mix of water/ethanol in 1:1 volume ratio on the shape, size, and crystalline structure of CoFe 2 O 4 NPs were studied using X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy and Fourier transform infrared spectroscopy. The size of CoFe 2 O 4 nanoparticle was controlled in the range from 20 to 110 nm based on the solvent medium used in the synthesis process. Furthermore, the evolution from spherical to cubic morphology of cobalt ferrite NPs is achieved by simply changing the solvent medium from aqueous to alcoholic medium. The magnetic properties of all the synthesized CoFe 2 O 4 NPs were studied by vibrating sample magnetometer (VSM) at room temperature. The magnetization value was found to be particle size dependent, and high magnetization (Ms) of 92.5 emu/g was obtained for the CoFe 2 O 4 NPs sample synthesized in a mixed solution of water and ethanol. A possible reaction mechanism for the formation of cobalt ferrite NPs by the sonochemical technique was discussed. The facile method adopted in our study appears to be a promising route for synthesis of highly crystalline nanoparticles within short times and without the need for using any calcination process.