Thermoelectric properties of copper-deficient Cu2-Se (0.05 ≤ x ≤ 0.25) binary compounds
Source abstract
Abstract
Abstract Recently, many novel superionic thermoelectric materials have been discovered along the concept of “phonon-liquid electron-crystal” (PLEC). Among them, Cu 2- x Se-based liquid-like materials are typical examples. In this study, a series of copper-deficient Cu 2- x Se (0.05 ≤ x ≤ 0.25) materials were synthesized and used to study the role of Cu vacancies on the electrical and thermal transport properties. The X-ray photoelectron spectroscopy (XPS) measurements suggest that the valence states of Cu and Se are independent on the Cu/Se atomic ratio. With increasing the content of Cu vacancies, the hole concentration is monotonously increased, leading to the improved electrical conductivity and reduced Seebeck coefficient. Based on the single parabolic band model analysis, it is found that changing the content of Cu vacancies does not obviously modify the material's electronic band structure and effective mass. Due to the presence of highly mobile Cu ions inside the crystal structure, the lattice thermal conductivities of all Cu 2- x Se (0.05 ≤ x ≤ 0.25) materials are very low with values around 0.39 W m −1 K −1 at 500 K. Because of the significantly reduced Seebeck coefficient and increased electronic thermal conductivity, the thermoelectric figure of merit zTs are decreased when increasing x from 0.05 to 0.25. At 750 K, a maximum zT of 0.46 is obtained in Cu 1.95 Se among all Cu 2- x Se (0.05 ≤ x ≤ 0.25) materials.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced Thermoelectric Materials and Devices · Chalcogenide Semiconductor Thin Films · Phase-change materials and chalcogenides
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. Copper ion liquid-like thermoelectrics10.1038/nmat3273 ↗
2. Rationally designing high-performance bulk thermoelectric materials10.1021/acs.chemrev.6b00255 ↗
3. Phase transition and high temperature thermoelectric properties of copper selenide Cu2-xSe (0 ≤ x ≤ 0.25)10.1088/1674-1056/20/8/087201 ↗
4. Thermoelectric properties of copper selenide with ordered selenium layer and disordered copper layer10.1016/j.nanoen.2012.02.010 ↗
5. Ultrahigh thermoelectric performance by electron and phonon critical scattering in Cu2Se1-xIx10.1002/adma.201302660 ↗
6. Thermoelectric properties of Ag-doped Cu2Se and Cu2Te10.1039/c3ta12508d ↗
7. Self-propagating high-temperature synthesis for compound thermoelectrics and new criterion for combustion processing10.1038/ncomms5908 ↗
8. Superior intrinsic thermoelectric performance with zT of 1.8 in single-crystal and melt-quenched highly dense Cu2-xSe bulks10.1038/srep07671 ↗
9. Influence of compensating defect formation on the doping efficiency and thermoelectric properties of Cu2-ySe1-xBrx10.1021/acs.chemmater.5b02405 ↗
10. Impacts of Cu deficiency on the thermoelectric properties of Cu2-xSe nanoplates10.1016/j.actamat.2016.04.050 ↗
11. Synthesis and transport property of Cu1.8S as a promising thermoelectric compound10.1039/c1cc16368j ↗
12. High Thermoelectric performance in non-toxic earth-abundant copper sulfide10.1002/adma.201400515 ↗
13. Ultrahigh thermoelectric performance in mosaic crystals10.1002/adma.201501030 ↗
14. High thermoelectric performance in copper telluride10.1038/am.2015.91 ↗
15. Compound defects and thermoelectric properties in ternary CuAgSe-based materials10.1039/C5TA02721G ↗
16. Thermoelectric transport of Se-rich Ag2Se in normal phases and phase transitions10.1063/1.4870509 ↗
17. Sulfide bornite thermoelectric material: a natural mineral with ultralow thermal conductivity10.1039/C4EE02428A ↗
18. CuCrSe2: a high performance phonon glass and electron crystal thermoelectric material10.1039/c3ta11903c ↗
19. Revisiting some chalcogenides for thermoelectricity10.1088/1468-6996/13/5/053003 ↗
20. Thermoelectric properties of n-type Nb-doped Ag8SnSe610.1063/1.4945033 ↗
21. High thermoelectric performance of superionic argyrodite compound Ag8SnSe610.1039/C6TC00810K ↗
22. Low sound velocity contributing to the high thermoelectric performance of Ag8SnSe610.1002/advs.201600196 ↗
23. Thermoelectric transport in Cu7PSe6 with high copper ionic mobility10.1021/ja5056092 ↗
24. The crystal structures of Cu1.8Se, Cu3Se2, α-CuSe and γ-CuSe, CuSe2, and CuSe2II10.1139/v76-122 ↗
25. X-ray study of the average structures of Cu2Se and Cu1.8S in the room temperature and the high temperature phases10.1016/0022-4596(91)90289-T ↗
26. Crystal structure and lattice dynamics of superionic copper selenide Cu2-δSe10.1016/S0925-8388(03)00439-0 ↗
27. Structural behaviour of β-Cu2-δSe (δ = 0, 0.15, 0.25) in dependence on temperature studied by synchrotron powder diffraction10.1016/j.jallcom.2005.10.079 ↗
28. Crystal structure of Cu2Se10.30970/cma4.0184 ↗
29. Superstructural ordering in low-temperature phase of superionic Cu2Se10.1016/0167-2738(87)90079-8 ↗
30. New layered structures of cuprous chalcogenides as thin film solar cell materials: Cu2Te and Cu2Se10.1103/PhysRevLett.111.165502 ↗
31. Low-temperature structural and transport anomalies in Cu2Se10.1103/PhysRevB.89.195209 ↗
32. Structure family and polymorphous phase transition in the compounds with soft sublattice: Cu2Se as an example10.1063/1.4948609 ↗
33. X-ray diffraction study of Cu1.8Zn0.2Se10.1007/BF02758043 ↗
34. Massalski · 1990
35. Electrical and thermal transports of binary copper sulfides CuxS with x from 1.8 to 1.9610.1063/1.4953439 ↗
36. Highly efficient and robust Au/MgCuCr2O4 catalyst for gas-phase oxidation of ethanol to acetaldehyde10.1021/ja406820f ↗
37. Nature of copper active sites in the carbon monoxide oxidation on CuAl2O4 and CuCr2O4 spinel type catalysts10.1006/jcat.1998.2094 ↗
38. The valence of copper in sulfides and selenides: an X-ray photoelectron spectroscopy study10.1016/0022-5088(80)90019-3 ↗
39. Photoconductivity of Cu2S, Cu2Se and Cu2Te