Thermal and mechanical properties of cordierite, mullite and steatite produced by plasma spraying
Source abstract
Abstract
Abstract Cordierite, mullite and steatite are silicate materials widely used in the ceramics industry. There is, however, only sparse information on their application in plasma spraying and properties of sprayed materials. Plasma sprayed deposits of cordierite, mullite and steatite contain amorphous phases as the result of rapid cooling of molten particles. The amorphous phase has a significant influence on physical properties, especially in connection with heat treatment. This article deals with phase changes of cordierite, mullite and steatite, resulting from plasma deposition. Special attention is paid to amorphous phase crystallization in subsequent heat treatment. Plasma sprayed deposits were produced using a water stabilized plasma torch WSP ® . The processes taking place in the deposits were examined primarily by differential thermal analysis (DTA), thermal dilatometry (TMA) and X-ray diffraction (XRD). These measurements were complemented by the determination of physical properties (namely, density, Young’s modulus and strength) and morphological observations. Important thermal characteristics like crystallization temperature and the coefficient of thermal expansion (CTE) of all materials were determined.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (17)
Show source-provided references
1. Thermal-expansion behavior of plasma sprayed cordierite10.1016/0167-577X(88)90126-7 ↗
2. Thermal shock characteristics of plasma sprayed mullite coatings10.1361/105996398770350710 ↗
3. Thermal expansion of mullite10.1111/j.1151-2916.1990.tb05270.x ↗
4. J. Hlaváč, Základy technologie silikátů SNTL ALFA, Praha, Czech Republic, 1988, (in Czech, Elements of Silicate Technology).
5. H. Herman, R.W. Iseli, Europatent 0 072 643, February 23, 1983.
6. Structure of plasma-sprayed oxides in the MgO–Al2O3–SiO2 system10.1007/BF00544522 ↗
7. Plasma-sprayed cordierite—structure and transformations10.1007/BF01148761 ↗
8. K.N. Lee, R.A. Miller, N.S. Jacobson, U.S. Patent No. 5 391 404, February 21, 1995.
9. Surface thermal cracking of thermal barrier coatings owing to stress relaxation: zirconia versus mullite10.1016/0257-8972(95)02647-9 ↗
10. Thermomechanical fatigue characterization of zirconia (8%Y2O3–ZrO2) and mullite thermal barrier coatings on diesel engine components: effect of coatings on engine performance10.1243/0954406001523731 ↗
11. Development of refractory silicate-yttria-stabilized zirconia dual-layer thermal barrier coatings10.1361/105996300770350069 ↗
12. K. Neufuss, J. Ilavský, J. Dubský, B. Kolman, P. Chráska, Plasma spraying of silicates II, in: Proceedings of the United Thermal Spray Conference, Dusseldorf, 1999, pp. 636–640.10.31399/asm.cp.itsc1999p0636 ↗
13. K. Neufuss, P. Chráska, Patents (Czech Republic) 283 203, November 25, 1997 and 286 735, April 4, 2000.10.1007/s11666-997-0056-y ↗
14. Properties of plasma-sprayed freestanding ceramic parts10.1007/s11666-997-0027-3 ↗
15. ASTM C1161: Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature, American Society for Testing and Materials, Philadelphia, PA, 1987.
16. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments10.1557/JMR.1992.1564 ↗
17. Residual and applied stresses in plasma sprayed Cr2O3 coatings10.4028/www.scientific.net/MSF.404-407.419 ↗