Crystallization behavior of CMAS and NaVO3+CMAS mixture and its potential effect to thermal barrier coatings corrosion

Xinmu Zhang, Yang Yu, Jingyong Sun, Hui Xin, Fuxing Ye, Lei Guo

Ceramics International· Volume 47· Issue 22
Publisher page

Abstract

Abstract Calcium-magnesium-alumina-silicate (CMAS) and molten salt corrosion pose great threats to thermal barrier coatings (TBCs), and recently, a coupling effect of CMAS and molten salt has been found to cause even severer corrosion to TBCs. In this study, the crystallization behavior of CMAS and CMAS+NaVO3 is investigated for potentially clarifying their corrosion mechanisms to TBCs. Results indicated that at 1000 °C and 1100 °C, CMAS was crystallized to form CaMgSi2O6, while at 1200 °C, the crystallization products were CaMgSi2O6, CaSiO3 and CaAl2Si2O8. The introduction of NaVO3 in CMAS reduced the crystallization ability, and as the NaVO3 content increased, glass crystallization occurred at a lower temperature, with crystallization products mainly consisting of CaAl2Si2O8 and CaMgSi2O6. At 1200 °C, CMAS+10 wt% NaVO3 was in a molten state without any crystallization, which suggested that NaVO3 addition in CMAS could reduce its melting point, indicating enhanced penetration ability in TBCs and thus increased corrosiveness.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: High-Temperature Coating Behaviors · Advanced ceramic materials synthesis · Magnesium Oxide Properties and Applications

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (46)

Show source-provided references
1. Thermal-barrier coatings for more efficient gas-turbine engines10.1557/mrs.2012.232 ↗
2. Recent developments in the field of thermal barrier coatings10.1007/s11666-009-9312-7 ↗
3. Overview on advanced thermal barrier coatings10.1016/j.surfcoat.2010.08.151 ↗
4. Hot corrosion behavior of NdYbZr2O7 exposed to V2O5 and Na2SO4+V2O5 molten salts10.1016/j.ceramint.2019.12.083 ↗
5. Effect of environmental pressure on the microstructure of YSZ thermal barrier coating via suspension plasma spraying10.1016/j.jeurceramsoc.2020.08.022 ↗
6. Microstructural characterization and room-temperature erosion behavior of as-deposited SPS, EB-PVD and APS YSZ-based TBCs10.1007/s11666-018-0763-6 ↗
7. Tailoring the EB-PVD columnar microstructure to mitigate the infiltration of CMAS in 7YSZ thermal barrier coatings10.1016/j.jeurceramsoc.2016.07.027 ↗
8. Review: microstructure-development mechanism during sintering in polycrystalline zirconia10.1080/09506608.2017.1402424 ↗
9. Degradation of zirconia in moisture10.1016/j.corsci.2020.109038 ↗
10. Epitaxial growth and cracking of highly tough 7YSZ splats by thermal spray technology10.1007/s40145-017-0252-2 ↗
11. Thermal barrier coatings for gas-turbine engine applications10.1126/science.1068609 ↗
12. Thermal barrier coatings technology: critical review, progress update, remaining challenges and prospects10.1179/1743280413Y.0000000019 ↗
13. Advanced structural ceramics in aerospace propulsion10.1038/nmat4687 ↗
14. Processing science of advanced thermal-barrier systems10.1557/mrs.2012.233 ↗
15. A delamination mechanism for thermal barrier coatings subject to calcium-magnesium-alumino-silicate (CMAS) infiltration10.1016/j.actamat.2004.11.028 ↗
16. Environmental degradation of high-temperature protective coatings for ceramic-matrix composites in gas-turbine engines10.1038/s41529-019-0075-4 ↗
17. Environmental degradation of thermal-barrier coatings by molten deposits10.1557/mrs.2012.230 ↗
18. CMAS resistance characteristics of LaPO4/YSZ thermal barrier coatings at 1250°C–1350°C10.1016/j.corsci.2019.04.014 ↗
19. Progress update on failure mechanisms of advanced thermal barrier coatings: a review10.1016/j.porgcoat.2015.09.019 ↗
20. Corrosion products evolution and hot corrosion mechanisms of REPO4 (RE= Gd, Nd, La) in the presence of V2O5 + Na2SO4 molten salt10.1016/j.jeurceramsoc.2018.10.031 ↗
21. A comparative investigation on the corrosion degradation of plasma sprayed YSZ and LnMgAl11O19 (Ln = Nd, Sm, Gd) coatings exposed to the molten V2O5 + Na2SO4 salt mixture at 1100 °C10.1016/j.jeurceramsoc.2019.04.055 ↗
22. Effects of surface roughness on CMAS corrosion behavior for thermal barrier coating applications10.1007/s40145-020-0449-7 ↗
23. Hot corrosion behaviour of nanostructured zirconia in molten NaVO3 salt10.1016/j.ceramint.2017.05.077 ↗
24. Comparison of hot corrosion behaviors of plasma-sprayed nanostructured and conventional YSZ thermal barrier coatings exposure to molten vanadium pentoxide and sodium sulfate10.1016/j.jeurceramsoc.2013.08.006 ↗
25. Corrosion behavior of Sc2O3–Y2O3 co-stabilized ZrO2 thermal barrier coatings with CMAS attack10.1016/j.ceramint.2019.05.063 ↗
26. Hot corrosion behavior and wettability of calcium–magnesium–alumina–silicate (CMAS) on LaTi2Al9O19 ceramic10.1016/j.corsci.2019.108199 ↗
27. Molten silicate interactions with plasma sprayed thermal barrier coatings: role of materials and microstructure10.1016/j.jeurceramsoc.2019.01.023 ↗
28. Zirconium silicate growth induced by the thermochemical interaction of yttria-stablized zirconia coatings with molten CMAS deposits10.1016/j.corsci.2019.01.011 ↗
29. CMAS (CaO–MgO–Al2O3–SiO2) resistance of Y2O3-stabilized ZrO2 thermal barrier coatings with Pt layers10.1016/j.ceramint.2017.09.197 ↗
30. Novel thermal barrier coatings that are resistant to high-temperature attack by glassy deposits10.1016/j.actamat.2007.08.028 ↗
31. Microstructural characterization of the interaction between 8YPSZ (EB-PVD) thermal barrier coatings and a synthetic CAS10.1016/j.surfcoat.2013.11.014 ↗
32. Calcia-magnesia-alumino-silicate (CMAS)-induced degradation and failure of air plasma sprayed yttria-stabilized zirconia thermal barrier coatings10.1016/j.actamat.2015.12.044 ↗
33. Comparison of NaVO3+CMAS mixture and CMAS corrosion to thermal barrier coatings10.1016/j.corsci.2020.108968 ↗
34. Hot corrosion resistance of air plasma sprayed ceramic Sm2SrAl2O7 (SSA) thermal barrier coatings in simulated gas turbine environments10.1016/j.ceramint.2018.06.234 ↗
35. Impermeable CeO2 overlay for the protection of plasma sprayed YSZ thermal barrier coating from molten sulfate-vanadate salts10.1016/j.surfcoat.2018.11.048 ↗
36. Evaluation of laser-glazed plasma-sprayed thermal barrier coatings under high temperature exposure to molten salts10.1016/j.surfcoat.2005.10.011 ↗
37. Hot corrosion behavior of YSZ, Gd2Zr2O7 and YSZ/Gd2Zr2O7 thermal barrier coatings exposed to molten sulfate and vanadate salt10.1016/j.apsusc.2017.09.047 ↗
38. Hot corrosion evaluation of Gd2O3-Yb2O3 co-doped Y2O3 stabilized ZrO2 thermal barrier oxides exposed to Na2SO4+V2O5 molten salt10.1016/j.ceramint.2016.11.109 ↗
39. CMAS effects on ship gas-turbine components/materials
40. Effects of laser glazing on CMAS corrosion behavior of Y2O3 stabilized ZrO2 thermal barrier coatings10.1016/j.corsci.2019.06.025 ↗
41. Role of environmental deposits and operating surface temperature in spallation of air plasma sprayed thermal barrier coatings10.1016/S0257-8972(96)02994-5 ↗
42. Thermochemical interaction of thermal barrier coatings with molten CaO-MgO-Al2O3-SiO2 (CMAS) deposits10.1111/j.1551-2916.2006.01209.x ↗
43. Adsorbability and spreadability of calcium-magnesium-alumino-silicate (CMAS) on Al-modified 7YSZ thermal barrier coating10.1016/j.ceramint.2016.09.106 ↗
44. Deposition and CMAS corrosion mechanism of 7YSZ thermal barrier coatings prepared by plasma spray-physical vapor deposition10.15541/jim20140397 ↗
45. Mechanisms of cracking and delamination within thick thermal barrier systems in aero-engines subject to calcium-magnesium-alumino-silicate (CMAS) penetration10.1016/j.msea.2008.01.006 ↗
46. Self-crystallization characteristics of calcium-magnesium-alumina-silicate (CMAS) glass under simulated conditions for thermal barrier coating applications10.1016/j.jeurceramsoc.2020.07.025 ↗