Effect of PyC interphase thickness on mechanical and ablation properties of 3D Cf/ZrC–SiC composite

Chunlei Yan, Rongjun Liu, Changrui Zhang, Yingbin Cao

Ceramics International· Volume 42· Issue 11
Publisher page

Abstract

Abstract Three-dimensional (3D) C f /ZrC–SiC composites were successfully prepared by the polymer infiltration and pyrolysis (PIP) process using polycarbosilane (PCS) and a novel ZrC precursor. The effects of PyC interphase of different thicknesses on the mechanical and ablation properties were evaluated. The results indicate that the C f /ZrC–SiC composites without and with a thin PyC interlayer of 0.15 µm possess much poor flexural strength and fracture toughness. The flexural strength grows with the increase of PyC layer thickness from 0.3 to 1.2 µm. However, the strength starts to decrease with the further increase of the PyC coating thickness to 2.2 µm. The highest flexural strength of 272.3±29.0 MPa and fracture toughness of 10.4±0.7 MPa m 1/2 were achieved for the composites with a 1.2 µm thick PyC coating. Moreover, the use of thicker PyC layer deteriorates the ablation properties of the C f /ZrC–SiC composites slightly and the ZrO 2 scale acts as an anti-ablation component during the testing.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · Aluminum Alloys Composites Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (20)

Show source-provided references
1. High speed propulsion: performance advantage of advanced materials10.1023/B:JMSC.0000041687.37448.06 ↗
2. Promising ultra-high-temperature ceramic materials for aerospace applications10.1134/S0036023613140039 ↗
3. Experimental approaches to the thermodynamics of ceramics above 1500°C10.1111/j.1551-2916.2012.05102.x ↗
4. Fabrication and properties of ZrB2–SiC–BN machinable ceramics10.1016/j.jeurceramsoc.2009.09.022 ↗
5. Densification and mechanical behavior of HfC and HfB2 fabricated by spark plasma sintering10.1111/j.1551-2916.2007.02248.x ↗
6. Preparation of 3D Cf/ZrC-SiC composites by joint processes of PIP and RMI, fabrication and properties of PIP 3D Cf/ZrC–SiC composites10.1016/j.msea.2014.03.071 ↗
7. Fabrication and properties of PIP 3D Cf/ZrC–SiC composites10.1016/j.msea.2013.10.102 ↗
8. The influence of the interphase and associated interfaces on the deflection of matrix cracks in ceramic matrix composites10.1016/S1359-835X(00)00095-6 ↗
9. The influence of an interphase on the deflection of a matrix crack in a ceramic–matrix composite10.1016/S0266-3538(01)00143-9 ↗
10. The properties of Cf/SiC composites prepared from different precursors10.1016/j.ceramint.2014.12.111 ↗
11. Influence of pyrolytic carbon interface thickness on microstructure and mechanical properties of SiC/SiC composites by NITE process10.1016/j.compscitech.2007.05.037 ↗
12. Experimental design in the deposition of BN interface coatings on SiC fibers by chemical vapor deposition10.1016/j.surfcoat.2006.05.026 ↗
13. Fabrication and properties of Cf/SiC–ZrC composites10.1111/j.1551-2916.2008.02632.x ↗
14. Microstructures and mechanical properties of 3D 4-directional, Cf/ZrC–SiC composites using ZrC precursor and polycarbosilane10.1016/j.mseb.2013.07.001 ↗
15. Zirconium carbide, hafnium carbide and their ternary carbide nanoparticles by an in situ polymerization route10.1039/C4RA14996C ↗
16. Mechanical properties of 3D KD-I SiCf/SiC composites with engineered fiber–matrix interfaces10.1016/j.compscitech.2011.01.014 ↗
17. Ablation behavior and mechanism of C/ZrC, C/ZrC–SiC and C/SiC composites fabricated by polymer infiltration and pyrolysis process10.1016/j.corsci.2014.05.005 ↗
18. UHTC composites for hypersonic applications
19. Melting temperatures of refractory oxides: (Part I)10.1351/pac198254030681 ↗
20. Oxidation-resistant ZrB2–SiC composites at 2200°C10.1016/j.compscitech.2007.08.017 ↗