Thermal shock resistance and bonding strength of tri-layer Yb2SiO5/mullite/Si coating on SiCf/SiC composites
Source abstract
Abstract
Abstract A Yb2SiO5/mullite/Si tri-layer environmental-barrier-coating (EBC) were coated on SiCf/SiC substrates via Air Plasma Spraying (APS). The thermal cycle tests (TCT) were conducted under thermal corrosive condition of vapor-oxygen (50 vol% H2O and 50 vol% O2) with thermal shock from 1200 °C to 200 °C. Microstructures, weight loss and bonding strength of the samples were systemically investigated after 101, 396, 606 and 700 TCT cycles respectively. The results show that the corner of the tri-layer coating peel off from the sample with weight loss of 1.3% after 700 TCT cycles. The bonding strength between substrate and tri-layer coatings gradually decreases to 6.79 MPa (approximately 55.2% of virgin specimens) after 700 cycles due to thermal shock induced cracks distributed horizontally within Si layers and between Si layer and outer layers.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · High-Temperature Coating Behaviors · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (26)
Show source-provided references
1. Thermal barrier coatings technology: critical review, progress update, remaining challenges and prospects10.1179/1743280413Y.0000000019 ↗
2. Corrosion of selected ceramic materials in hot gas environment10.1016/j.jeurceramsoc.2006.01.015 ↗
3. BN/SiC Coating on SiC Tows Prepared by Chemical Vapor Infiltration10.1088/1757-899X/678/1/012062 ↗
4. The microstructure and mechanical properties of silicon carbide fibers with boron nitride interphase
5. Rare earth silicate environmental barrier coatings for SiC/SiC composites and Si3N4 ceramics10.1016/j.jeurceramsoc.2004.12.013 ↗
6. Upper temperature limit of environmental barrier coatings based on mullite and BSAS10.1111/j.1151-2916.2003.tb03466.x ↗
7. Oxidation and volatilization of silica formers in water vapor10.1111/j.1151-2916.2003.tb03459.x ↗
8. Rare earth silicate environmental barrier coatings: present status and prospective10.1016/j.ceramint.2017.01.153 ↗
9. Thermal properties of rare-earth monosilicates for EBC on Si-based ceramic composites10.1111/jace.13982 ↗
10. Corrosion of RE2Si2O7 (RE=Y, Yb, and Lu) environmental barrier coating materials by molten calcium-magnesium-alumino-silicate glass at high temperatures10.1016/j.jeurceramsoc.2019.05.036 ↗
11. Mechanical and thermal properties of Yb2SiO5: a promising material for T/EBCs applications10.1111/jace.14085 ↗
12. Thermal shock behavior of 8YSZ and double-ceramic-layer La2Zr2O7/8YSZ thermal barrier coatings fabricated by atmospheric plasma spraying10.1016/j.ceramint.2011.12.076 ↗
13. Microstructure evolution and thermomechanical properties of plasma-sprayed Yb2SiO5 coating during thermal aging10.1111/jace.14690 ↗
14. Thermal shock resistance of tri-layer Yb2SiO5/Yb2Si2O7/Si coating for SiC and SiC-matrix composites10.1111/jace.15713 ↗
15. Effect of pre-oxidation treatment on the bonding strength and thermal shock resistance of SiC coating for C/C-ZrC-SiC composites10.1016/j.ceramint.2015.01.151 ↗
16. Diffusion study of rare-earth oxides into silica layer for environmental barrier coating applications10.1016/j.jeurceramsoc.2019.05.026 ↗
17. Failure mechanism associated with the thermally grown silica scale in environmental barrier coated C/SiC composites10.1111/jace.14273 ↗
18. Stability and CMAS resistance of ytterbium-silicate/hafnate EBCs/TBC for SiC composites10.1111/jace.13262 ↗
19. Resistance of 2ZrO2·Y2O3top coat in thermal/environmental barrier coatings to calcia‐magnesia‐aluminosilicate attack at 1500°C10.1111/jace.14854 ↗
20. Preparation of Si/mullite/Yb2SiO5 environment barrier coating (EBC) by plasma spray-physical vapor deposition (PS-PVD)10.15541/jim20170194 ↗
21. Mechanisms of ytterbium monosilicate/mullite/silicon coating failure during thermal cycling in water vapor10.1111/jace.13792 ↗
22. Fracture mechanisms of ytterbium monosilicate environmental barrier coatings during cyclic thermal exposure10.1016/j.actamat.2015.10.019 ↗
23. Plasma spray deposition of tri-layer environmental barrier coatings10.1016/j.jeurceramsoc.2014.04.027 ↗
24. Response of ytterbium disilicate-silicon environmental barrier coatings to thermal cycling in water vapor10.1016/j.actamat.2015.12.053 ↗
25. Microstructure and damage evolution of SiCf/PyC/SiC and SiCf/BN/SiC mini-composites: a synchrotron X-ray computed microtomography study10.1016/j.ceramint.2019.03.004 ↗
26. Structure, composition, and defect control during plasma spray deposition of ytterbium silicate coatings10.1007/s10853-015-9358-5 ↗