Isothermal oxidation and TGO growth behaviors of YAG/YSZ double-ceramic-layer thermal barrier coatings
Source abstract
Abstract
Abstract In this study, yttrium aluminum garnet/yttria-stabilized zirconia (YAG/YSZ) double-ceramic-layer thermal barrier coatings (DCL TBC) and yttria-stabilized zirconia (YSZ) single-ceramic-layer thermal barrier coatings (SCL TBC) were deposited by atmosphere plasma spray (APS) on the Inconel 738 alloy substrate, and isothermal oxidation tests were performed to investigate the formation and growth behavior of thermally grown oxide (TGO). Results showed that the Al2O3 TGO thickness of both TBC groups increased by increasing the isothermal oxidation time，and then slowly decreased with the appearance and growth of the adverse multilayer structure comprising CoCr2O4, (Ni,Co)Al2O4, NiCr2O4, and NiO mixed oxides. However, since the significant inhibition effect of the YAG coating to oxygen ionic diffusion, the mixed oxides appearance time and TGO growth behaviors were delayed in the DCL TBC. As a result, the TGO thickness of the DCL TBC was always smaller than that of the SCL TBC in the entire oxidation process. And the Al2O3 layer thickness proportion in the total TGO of the DCL TBC was greater than or equal to that of the SCL TBC after oxidation for the same period. The results of weight gain showed that compared with the SCL TBC, the parabolic oxidation rate of the DCL TBC was decreased approximately 35%. Consequently, the DCL TBC has better high-temperature oxidation resistance than the SCL TBC.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Nuclear Materials and Properties · Catalytic Processes in Materials Science
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (45)
Show source-provided references
1. Oxidation control in plasma spraying NiCrCoAlY coating10.1016/j.apsusc.2012.01.134 ↗
2. Evolution of hot corrosion resistance of YSZ, Gd2Zr2O7, and Gd2Zr2O7 + YSZ composite thermal barrier coatings in Na2SO4 + V2O5 at 1050 °C10.1016/j.jeurceramsoc.2012.01.006 ↗
3. Evaluation of normal and nanolayer composite thermal barrier coatings in fused vanadate-sulfate salts at 1000 °C
4. Mechanism controlling the durability of thermal barrier coatings10.1016/S0079-6425(00)00020-7 ↗
5. Microstructure evolution of Al-modified 7YSZ PS-PVD TBCs in thermal cycle10.1016/j.ceramint.2021.01.064 ↗
6. Effect of segmented cracks on TGO growth and life of thick thermal barrier coating under isothermal oxidation conditions10.1016/j.ceramint.2019.11.245 ↗
7. Gas turbine coatings-An overview10.1016/j.engfailanal.2012.07.007 ↗
8. Oxygen transport by gas permeation through the zirconia layer in plasma sprayed thermal barrier coatings10.1016/j.surfcoat.2003.10.018 ↗
9. Effect of oxide growth on the stress development in double-ceramic-layer thermal barrier coatings10.1016/j.ceramint.2017.07.218 ↗
10. Thermal barrier coatings for gas-turbine engine applications10.1126/science.1068609 ↗
11. Production and characterization of GZ/CYSZ alternative thermal barrier coatings with multilayered and functionally graded designs10.1016/j.jeurceramsoc.2016.01.036 ↗
12. Particle in-flight behavior and its influence on the microstructure and mechanical property of plasma sprayed La2Ce2O7 thermal barrier coatings10.1016/j.msea.2014.11.098 ↗
13. Evolution of microstructural and mechanical properties of lanthanum zirconate thermal barrier coatings at high temperature10.1016/j.surfcoat.2014.07.067 ↗
14. Thermal cycling behavior of La2Ce2O7/8YSZ double-ceramic-layer thermal barrier coatings prepared by atmospheric plasmas praying10.1016/j.surfcoat.2010.03.053 ↗
15. New thermal barrier coatings based on pyrochlore/YSZ double-layer systems10.1111/j.1744-7402.2004.tb00186.x ↗
16. Ceramic materials for thermal barrier coatings10.1016/S0955-2219(03)00129-8 ↗
17. Microstructural analysis of YSZ and YSZ/Al2O3 plasma sprayed thermal barrier coatings after high temperature oxidation10.1016/j.surfcoat.2007.11.029 ↗
18. Effects of incorporation of micro and nano Al2O3 layers on thermal shock behaviour of YSZ thermal barrier coatings10.1080/00084433.2016.1196845 ↗
19. Low thermal conductivity in garnets10.1111/j.1151-2916.1997.tb02937.x ↗
20. Theoretical investigation on mechanical and thermal properties of a promising thermal barrier material: Yb3Al5O1210.1016/j.jmst.2014.06.007 ↗
21. Thermal conductivity, phase stability, and oxidation resistance of Y3Al5O12(YAG)/Y2O3–ZrO2(YSZ) thermal-barrier coatings10.1023/B:OXID.0000025334.02788.d3 ↗
22. Phase stability of plasma sprayed YAG-YSZ composite beads/coatings at high temperature10.1016/j.jeurceramsoc.2013.04.031 ↗
23. Cyclic oxidation behavior and thermal barrier effect of YSZ-(Al2O3/YAG) double-layer TBCs prepared by the composite sol-gel method10.1016/j.surfcoat.2011.09.025 ↗
24. Detonation spraying of copper: theoretical analysis and experimental studies
25. Isothermal oxidation properties of YAG/8YSZ double ceramic thermal barrier coatings
26. Inhibition behavior of LZO on the oxidation of bond-coat in thermal barrier coatings
27. Thermal durability of YSZ/Nanostructured Gd2Zr2O7 TBC undergoing thermal cycling10.1007/s11085-019-09937-7 ↗
28. A high performance NiCoCrAlY bond coat manufactured using laser powder deposition10.1016/j.corsci.2017.07.018 ↗
29. YSZ/NiCrAlY interface oxidation of APS thermal barrier coatings10.1016/j.corsci.2018.06.035 ↗
30. High temperature oxidation resistance and thermal growth oxides formation and growth mechanism of double-layer thermal barrier coatings10.1016/j.jallcom.2019.05.052 ↗
31. Effects of Al2O3 diffusion barrier layer (including Y-containing small oxide precipitates) and nanostructured YSZ top coat on the oxidation behavior of HVOF NiCoCrAlTaY/APS YSZ coatings at 1100 °C10.1016/j.corsci.2018.07.013 ↗
32. High speed laser cladded Ti-Cu-NiCoCrAlTaY burn resistant coating and its oxidation behavior
33. Isothermal oxidation and TGO growth behavior of NiCoCrAlY-YSZ thermal barrier coatings on a Ni-based superalloy10.1016/j.jallcom.2020.156093 ↗
34. Microstructural evolution at interfaces of thermal barrier coatings during isothermal oxidation10.1016/j.jeurceramsoc.2016.02.011 ↗
35. Segregation and microstructural evolution at interfaces of atmospheric plasma sprayed thermal barrier coatings during thermal cycling10.1016/j.jallcom.2019.153026 ↗
36. Yttrium influence of the alumina growth mechanism on an FeCr23Al510.1016/0169-4332(87)90136-X ↗
37. Effect of residual stress on the spallation of the thermally-grown oxide formed on NiCoCrAlY coating10.1016/j.surfcoat.2019.125112 ↗
38. Oxidation behavior of thermal barrier coatings with HVOF and detonation-sprayed NiCrAlY bond coats10.1016/j.corsci.2008.02.002 ↗
39. Kinetics and mechanism of isothermal oxidation of compositionally graded yttria stabilized zirconia (YSZ) based thermal barrier coating10.1016/j.corsci.2014.06.050 ↗
40. Corrosion mechanism of a NiCoCrAlTaY coated Mar-M247 superalloy in molten salt vapour10.1016/j.corsci.2011.10.021 ↗
41. Isothermal oxidation behavior and kinetics of thermal barrier coatings produced by cold gas dynamic spray technique10.1016/j.surfcoat.2016.12.021 ↗
42. Impermeability of Y3Al5O12 ceramic against molten glassy calcium-magnesium-alumina-silicate10.1016/j.cja.2018.02.007 ↗
43. High-temperature oxidation behavior in YSZ coated Cr2AlC and CoNiCrAlY substrates10.1016/j.surfcoat.2020.126239 ↗
44. Effect of microstructure on early oxidation of MCrAlY coatings10.1016/j.actamat.2018.08.018 ↗
45. Preparation and oxidation behaviour of NiCrAlYSc coatings on a Ni-based single crystal superalloy10.1016/j.corsci.2020.108703 ↗