Densification and Properties of Fe2O3 Nanoparticles added CaO Refractories

Abstract Up to 8 wt. % of Nano-iron oxide was added to CaO refractory matrix. The crystalline phases and microstructure characteristics of specimens sintered at 1650 °C for 5 h in an electric furnace were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The physical properties are reported in terms of bulk density, apparent porosity and hydration resistance. The mechanical behavior was studied by a cold crushing strength (CCS) and flexural strength at 1200 °C test. As a result, it was found that the presence of Nano-iron oxide in the CaO refractory matrix induced 2CaO.Fe 2 O 3 (C 2 F), CaO.Fe 2 O 3 (CF) and 3CaO.Al 2 O 3 (C 3 A) phase’s formation, which improved the sintering process. Nano-iron oxide also influenced the bonding structure through a direct bonding enhancement. On the Other hand, the presence of Nano-iron oxide resulting in improvement properties of CaO refractory matrix refractories such as bulk density, hydration resistance and cold crushing strength. The maximum flexural strength at 1200 °C is achieved by the samples containing 4 wt. % nano-Fe 2 O 3 .