Effect of Al on the formation and structure of alkali-silica reaction products
Source abstract
Abstract
The use of Al-rich supplementary cementitious materials can effectively reduce the expansion of concrete caused by alkali-silica reaction (ASR). However, the role of Al in mitigating the formation and structure of ASR products is only poorly understood, since direct investigation of the reaction in the micro-scale veins of aggregates is difficult. Recent successful synthesis of ASR products provides a unique opportunity to directly assess the role of Al in ASR. In this study, the effect of Al on the formation and structure of ASR products synthesized at 40 and 80 °C is investigated. It is found that the presence of Al in concentration lower than 0.1 mM neither prevents ASR nor alters the structure of the crystalline ASR products formed at 40 °C. However, formation of the crystalline ASR product at 80 °C is lowered at higher Al content due to the formation of a zeolitic precursor.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Magnesium Oxide Properties and Applications · Recycling and utilization of industrial and municipal waste in materials production
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (69)
Show source-provided references
1. Swamy · 1991
2. How does fly ash mitigate alkali–silica reaction (ASR) in accelerated mortar bar test (ASTM C1567)?10.1016/j.cemconcomp.2012.11.004 ↗
3. The influence of metakaolin and silica fume on the chemistry of alkali–silica reaction products10.1016/S0958-9465(00)00096-2 ↗
4. Long-term effectiveness of supplementary cementing materials against alkali–silica reaction10.1016/S0008-8846(01)00538-5 ↗
5. The effect of fly ash composition on the expansion of concrete due to alkali–silica reaction10.1016/S0008-8846(00)00283-0 ↗
6. Pozzolanic reaction of glass powder and its role in controlling alkali–silica reaction10.1016/j.cemconcomp.2015.12.008 ↗
7. The effect of supplementary cementing materials on alkali-silica reaction: a review10.1016/j.cemconres.2010.11.003 ↗
8. The capacity of ternary blends containing slag and high-calcium fly ash to mitigate alkali silica reaction10.1016/j.cemconcomp.2013.12.008 ↗
9. The effect of metakaolin on alkali–silica reaction in concrete10.1016/S0008-8846(99)00261-6 ↗
10. Assessment of binary and ternary blends of metakaolin and Class C fly ash for alkali-silica reaction mitigation in concrete10.1016/j.cemconres.2010.08.006 ↗
11. Mitigation of alkali-silica reaction by limestone calcined clay cement (LC3)10.1016/j.cemconres.2020.106176 ↗
12. The effect of pozzolans and slag on the expansion of mortars cured at elevated temperature: part II: microstructural and microchemical investigations10.1016/j.cemconres.2003.12.026 ↗
13. S.-Y. Hong, F.P. Glasser, Alkali sorption by CSH and CASH gels: part II. Role of alumina, Cem. Concr. Res. 32 (2002) 1101–1111.10.1016/S0008-8846(02)00753-6 ↗
14. Aspects of the pore solution chemistry of blended cements related to the control of alkali silica reaction10.1016/0008-8846(87)90046-9 ↗
15. Increasing concrete durability with high-reactivity metakaolin10.1016/S0958-9465(00)00097-4 ↗
16. Use of ternary cementitious systems containing silica fume and fly ash in concrete10.1016/S0008-8846(99)00096-4 ↗
17. S.-Y. Hong, F.P. Glasser, Alkali binding in cement pastes: part I. The CSH phase, Cem. Concr. Res. 29 (1999) 1893–1903.10.1016/S0008-8846(99)00187-8 ↗
18. Alkali uptake in calcium alumina silicate hydrate (CASH)10.1016/j.cemconres.2016.03.009 ↗
19. Alkali fixation of C–S–H in blended cement pastes and its relation to alkali silica reaction10.1016/j.cemconres.2012.03.010 ↗
20. The influence of aluminium on the dissolution of amorphous silica and its relation to alkali silica reaction10.1016/j.cemconres.2012.09.009 ↗
21. The effect of aluminum in solution on the dissolution of amorphous silica and its relation to cementitious systems10.1111/jace.12098 ↗
22. Assessing the potential of ToF-SIMS as a complementary approach to investigate cement-based materials—applications related to alkali–silica reaction10.1016/j.cemconres.2014.11.008 ↗
23. ASR prevention—effect of aluminum and lithium ions on the reaction products10.1016/j.cemconres.2015.06.002 ↗
24. The contribution of quartz and the role of aluminum for understanding the AAR with greywacke10.1016/j.cemconres.2007.05.009 ↗
25. Alkali-silica reaction in waterglass-activated slag mortars incorporating fly ash and metakaolin10.1016/j.cemconres.2018.03.002 ↗
26. Hagelia · 2012
27. Alkali-silica reaction products: comparison between samples from concrete structures and laboratory test specimens10.1016/j.matchar.2010.09.010 ↗
28. Composition of alkali–silica reaction products at different locations within concrete structures10.1016/j.matchar.2009.01.011 ↗
29. Reduced alkali-silica reaction damage in recycled glass mortar samples with supplementary cementitious materials10.1016/j.jclepro.2017.11.119 ↗
30. Examination of the concrete from an old Portuguese dam: texture and composition of alkali–silica gel10.1016/j.matchar.2007.04.007 ↗
31. E-modulus of the alkali–silica-reaction product determined by micro-indentation10.1016/j.conbuildmat.2013.03.018 ↗
32. T. Katayama, Late-expansive ASR in a 30-year old PC structure in eastern Japan, in: Proc. 14th Int. Conf. Alkali-Aggregate React. (ICAAR), Austin, Texas, USA, Pap., 2012.
33. T. Katayama, ASR gels and their crystalline phases in concrete—universal products in alkali–silica, alkali–silicate and alkali–carbonate reactions, in: Proc. 14th Int. Conf. Alkali Aggreg. React. (ICAAR), Austin, Texas, 2012: pp. 20–25.
34. The influence of potassium–sodium ratio in cement on concrete expansion due to alkali-aggregate reaction10.1016/j.cemconres.2008.05.004 ↗
35. Raman microscopy of alkali-silica reaction (ASR) products formed in concrete10.1016/j.cemconres.2017.08.014 ↗
36. Synthesis, characterization, and water uptake property of alkali-silica reaction products10.1016/j.cemconres.2019.04.009 ↗
37. Synthesis of alkali-silica reaction product structurally identical to that formed in field concrete10.1016/j.matdes.2020.108562 ↗
38. I. V Pekov, N. V Zubkova, Y.E. Filinchuk, N. V Chukanov, A.E. Zadov, D.Y. Pushcharovsky, E.R. Gobechiya, Shlykovite KCa [Si4O9(OH)]·3H2O and cryptophyllite K2Ca[Si4O10]·5H2O, new mineral species from the Khibiny alkaline pluton, Kola peninsula, Russia, Geol. Ore Depos. 52 (2010) 767–777.10.1134/S1075701510080088 ↗
39. Formation of shlykovite and ASR-P1 in concrete under accelerated alkali-silica reaction at 60 and 80 °C10.1016/j.cemconres.2020.106213 ↗
40. Characterization of amorphous and crystalline ASR products formed in concrete aggregates10.1016/j.cemconres.2020.106190 ↗
41. The role of calcium on the formation of alkali-silica reaction products10.1016/j.cemconres.2019.105898 ↗
42. The combined effect of potassium, sodium and calcium on the formation of alkali-silica reaction products10.1016/j.cemconres.2019.105914 ↗
43. B. Lothenbach, P. Durdzinski, K. De Weerdt, Thermogravimetric analysis. K. Scrivener, R. Snellings, B. Lothenbach (Eds.), A Practical Guide to Microstructural Analysis of Cementitious Materials, in: CRC Press Oxford, UK, 2016: pp. 177–212.
44. D.A. Kulik, T. Wagner, S. V Dmytrieva, G. Kosakowski, F.F. Hingerl, K. V Chudnenko, U.R. Berner, GEM-Selektor geochemical modeling package: revised algorithm and GEMS3K numerical kernel for coupled simulation codes, Comput. Geosci. 17 (2013) 1–24.10.1007/s10596-012-9310-6 ↗
45. T. Wagner, D.A. Kulik, F.F. Hingerl, S. V Dmytrieva, GEM-Selektor geochemical modeling package: TSolMod library and data interface for multicomponent phase models, Can. Mineral. 50 (2012) 1173–1195.10.3749/canmin.50.5.1173 ↗
46. Thoenen · 2014
47. Cemdata18: a chemical thermodynamic database for hydrated Portland cements and alkali-activated materials10.1016/j.cemconres.2018.04.018 ↗
48. B.J. Merkel, B. Planer-Friedrich, D.K. Nordstrom, Groundwater geochemistry, A Pract. Guid. to Model. Nat. Contam. Aquat. Syst. 2 (2005).
49. R.J. Myers, S.A. Bernal, J.L. Provis, A thermodynamic model for C-(N-) ASH gel: CNASH_ss. Derivation and validation, Cem. Concr. Res. 66 (2014) 27–47.10.1016/j.cemconres.2014.07.005 ↗
50. B.Y. Zhen-Wu, D.P. Prentice, J. V Ryan, K. Ellison, M. Bauchy, G. Sant, zeo19: a thermodynamic database for assessing zeolite stability during the corrosion of nuclear waste immobilization glasses, Npj Mater. Degrad. 4 (2020) 1–12.10.1038/s41529-019-0106-1 ↗
51. Characterization of calcium aluminate phases in cements by aluminum-27 MAS NMR spectroscopy10.1021/ic00058a043 ↗
52. Triple-quantum two-dimensional 27Al magic angle nuclear magnetic resonance study of the aluminum incorporation in calcium silicate hydrates10.1021/ja9806940 ↗
53. Structural characterization of C–S–H and C–A–S–H samples—part II: local environment investigated by spectroscopic analyses10.1016/j.jssc.2009.09.024 ↗
54. Thermodynamic properties of CSH, CASH and MSH phases: results from direct measurements and predictive modelling10.1016/j.apgeochem.2018.03.004 ↗
55. Synthesis of ZSM-5 zeolites with defined distribution of Al atoms in the framework and multinuclear MAS NMR analysis of the control of Al distribution10.1021/cm301629a ↗
56. 29Si and 27Al MAS NMR study of zeolite β with different Si/Al ratios10.1016/0021-9517(90)90116-2 ↗
57. 29Si MAS NMR spectroscopic investigation of alkali silica reaction product gels10.1016/0008-8846(93)90035-8 ↗
58. Impact of a 70° C temperature on an ordinary Portland cement paste/claystone interface: an in situ experiment10.1016/j.cemconres.2016.02.001 ↗
59. ThermoChimie database developments in the framework of cement/clay interactions10.1016/j.apgeochem.2014.12.006 ↗
60. Geological constraints on the thermodynamic properties of the stilbite—stellerite solid solution in low-grade metabasalts10.1016/S0016-7037(01)00629-9 ↗
61. Cement/clay interactions–a review: experiments, natural analogues, and modeling10.1016/j.wasman.2006.01.027 ↗
62. Alkali–silica reaction: current understanding of the reaction mechanisms and the knowledge gaps10.1016/j.cemconres.2015.05.024 ↗
63. Incorporation of aluminum in the calcium silicate hydrate (C–S–H) of hydrated Portland cements: a high-field 27Al and 29Si MAS NMR investigation10.1021/ic020607b ↗
64. The role of Al in C–S–H: NMR, XRD, and compositional results for precipitated samples10.1016/j.cemconres.2005.03.002 ↗
65. 27Al and 29Si solid-state NMR characterization of calcium-aluminosilicate-hydrate10.1021/ic202124x ↗
66. The effect of sodium hydroxide on Al uptake by calcium silicate hydrates (CSH)10.1016/j.jcis.2020.03.057 ↗
67. Zeolite formation in class F fly ash blended cement pastes10.1111/j.1151-2916.1992.tb04228.x ↗
68. The pore solution of blended cements: a review10.1617/s11527-015-0724-1 ↗
69. H.C. Helgeson, H. HC, D. JM, N. HW, B. DK, Summary and critique of the thermodynamic properties of rock-forming minerals, Am. J. Sci. (1978) 278-A.