Effect of pumice and fly ash incorporation on high temperature resistance of cement based mortars

Abstract The effects of high temperature on the mechanical properties of cement based mortars containing pumice and fly ash were investigated in this research. Four different mortar mixtures with varying amounts of fly ash were exposed to high temperatures of 300, 600, and 900 °C for 3 h. The residual strength of these specimens was determined after cooling by water soaking or by air cooling. Also, microstructure formations were investigated by X-ray and SEM analyses. Test results showed that the pumice mortar incorporating 60% fly ash revealed the best performance particularly at 900 °C. This mixture did not show any loss in compressive strength at all test temperatures when cooled in air. The superior performance of 60% FA mortar may be attributed to the strong aggregate–cement paste interfacial transition zone (ITZ) and ceramic bond formation at 900 °C. However, all mortar specimens showed severe losses in terms of flexural strength. Furthermore, specimens cooled in water showed greater strength loss than the air cooled specimens. Nevertheless, the developed pumice, fly ash and cement based mortars seemed to be a promising material in preventing high temperature hazards.