Micro foaming performance of scCO 2 -aid glutaraldehyde/hexametaphosphate/thermoplastic starch foams modified by alkali treatment and montmorillonite nano-platelets
Source abstract
Abstract
The micro foaming performance, moisture resistance and dynamic viscosity of scCO 2 -aid glutaraldehyde/hexametaphosphate/thermoplastic tapioca starch (GA/SHMP/TOS) foams were considerably improved by proper NaOH treatment. The expansion ratio, resilience rate, dynamic viscosity values of these NaOH modified foams improved to a maximum, as the time for NaOH treatment approached a proper value. The dynamic viscosity, expansion ratio and resilience rate of the scCO 2 -aid GA/SHMP/TOS foams modified using 110 atm scCO 2 -pressure, the proper alkali treatment time, SHMP loading and varying montmorillonite (MMT) loadings improved further, as their MMT loadings approached a proper value of 2.5 part per hundred parts of tapioca starch (PHTOS). Relatively large dynamic viscosity (7.1x10 4 Pa·s), extremely large expansion ratio (∼75), cell density (1.1x10 9 cells/cm 3 ) and/or resilience rate (∼80%) were acquired for the scCO 2 -aid GA/SHMP/TOS/MMT foam modified using the proper alkali treatment time and MMT loading. Thermal analyses results showed that crystallization onset temperatures and crystallization rates of scCO 2 -aid GA/SHMP/TOS/MMT foams modified using the proper alkali treatment time and varying MMT loadings improved to a highest value by adding 2.5 PHTOS of MMT nano-platelets. Possible reasons accounting for the considerably improved micro foaming performance of scCO 2 -aid GA/SHMP/TOS/MMT foams modified using the proper alkali treatment time and MMT loading are proposed in this study.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: biodegradable polymer synthesis and properties · Polymer Foaming and Composites · Polymer composites and self-healing
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Hubei Collaborative Innovation Center for Advanced Organic Chemical Materials, Ministry of Education, Key Laboratory for the Green Preparation and Application of Functional Materials, Hubei Key Laboratory of Polymer Materials, Faculty of Materials Science and Engineering, Hubei University, Wuhan, China
References (96)
Show source-provided references
1. Martien VDO · New Biotechnol · 2016 · 37 · 48
2. 10.5334/aogh.283110.5334/aogh.2831 ↗
3. 10.1016/j.biortech.2020.12347310.1016/j.biortech.2020.123473 ↗
4. 10.1016/j.marpolbul.2010.09.02710.1016/j.marpolbul.2010.09.027 ↗
5. 10.1089/ees.2017.038010.1089/ees.2017.0380 ↗
6. 10.1016/j.envpol.2015.02.03410.1016/j.envpol.2015.02.034 ↗
7. 10.1038/544297a10.1038/544297a ↗
8. 10.1002/(SICI)1097-0126(1998100)47:2<89::AID-PI86>3.0.CO;2-F10.1002/(SICI)1097-0126(1998100)47:2<89::AID-PI86>3.0.CO;2-F ↗
9. 10.1016/j.progpolymsci.2014.04.00110.1016/j.progpolymsci.2014.04.001 ↗
10. 10.1002/(SICI)1097-4636(199604)30:4<475::AID-JBM5>3.0.CO;2-M10.1002/(SICI)1097-4636(199604)30:4<475::AID-JBM5>3.0.CO;2-M ↗
11. 10.1021/ie403041h10.1021/ie403041h ↗
12. 10.1016/j.ces.2012.02.05110.1016/j.ces.2012.02.051 ↗
13. 10.1016/j.polymer.2014.06.05910.1016/j.polymer.2014.06.059 ↗
14. 10.1590/S1516-1439201300500013310.1590/S1516-14392013005000133 ↗
15. 10.1016/j.mtphys.2021.10051210.1016/j.mtphys.2021.100512 ↗
16. 10.1016/j.carbpol.2019.11523410.1016/j.carbpol.2019.115234 ↗
17. 10.1016/j.progpolymsci.2012.07.00510.1016/j.progpolymsci.2012.07.005 ↗
18. 10.1007/s10570-010-9419-510.1007/s10570-010-9419-5 ↗
19. 10.1016/j.clay.2011.04.02310.1016/j.clay.2011.04.023 ↗
20. 10.1080/0360255090282439010.1080/03602550902824390 ↗
21. 10.1016/j.carbpol.2015.01.01210.1016/j.carbpol.2015.01.012 ↗
22. 10.1007/s13726-011-0009-710.1007/s13726-011-0009-7 ↗
23. Sungsanit K · Korea-aust Rheol J · 2010 · 22 · 187
24. 10.1016/j.ijbiomac.2019.09.05810.1016/j.ijbiomac.2019.09.058 ↗
25. 10.1021/acs.iecr.5b0347310.1021/acs.iecr.5b03473 ↗
26. 10.1177/02624893120310010110.1177/026248931203100101 ↗
27. 10.1002/mame.20100037110.1002/mame.201000371 ↗
28. 10.3390/polym1205110810.3390/polym12051108 ↗
29. 10.1007/s13233-015-3018-010.1007/s13233-015-3018-0 ↗
30. 10.1016/j.eurpolymj.2012.03.01510.1016/j.eurpolymj.2012.03.015 ↗
31. 10.1016/j.eurpolymj.2017.04.01010.1016/j.eurpolymj.2017.04.010 ↗
32. 10.1002/app.4506710.1002/app.45067 ↗
33. Chauvet M · J Appl Polym Sci · 2020 · 138 · 1
34. 10.1002/app.2671510.1002/app.26715 ↗
35. 10.1016/j.biortech.2006.10.03010.1016/j.biortech.2006.10.030 ↗
36. 10.1016/j.foodres.2015.07.01910.1016/j.foodres.2015.07.019 ↗
37. 10.1016/j.indcrop.2014.12.02510.1016/j.indcrop.2014.12.025 ↗
38. 10.1016/j.polymdegradstab.2005.07.00110.1016/j.polymdegradstab.2005.07.001 ↗
39. 10.1016/j.jfoodeng.2007.08.00510.1016/j.jfoodeng.2007.08.005 ↗
40. 10.1002/app.4556510.1002/app.45565 ↗
41. 10.1016/j.carbpol.2011.10.00810.1016/j.carbpol.2011.10.008 ↗
42. 10.1016/j.carbpol.2015.09.01910.1016/j.carbpol.2015.09.019 ↗
43. 10.1016/j.carbpol.2011.09.01610.1016/j.carbpol.2011.09.016 ↗
44. İLknur G · Starch-Starke · 2018 · 71 · 1800046
45. 10.1016/j.carbpol.2007.11.01310.1016/j.carbpol.2007.11.013 ↗
46. 10.1002/app.2927010.1002/app.29270 ↗
47. 10.1039/C3GC41895B10.1039/C3GC41895B ↗
48. 10.1016/j.carbpol.2011.01.04010.1016/j.carbpol.2011.01.040 ↗
49. 10.1016/j.jcou.2017.01.02810.1016/j.jcou.2017.01.028 ↗
50. 10.1021/bm100023510.1021/bm1000235 ↗
51. 10.1002/star.20150019410.1002/star.201500194 ↗
52. 10.1016/j.eurpolymj.2013.11.01510.1016/j.eurpolymj.2013.11.015 ↗
53. 10.1002/app.3952310.1002/app.39523 ↗
54. 10.1016/j.supflu.2011.03.00610.1016/j.supflu.2011.03.006 ↗
55. 10.1016/j.materresbull.2015.03.02610.1016/j.materresbull.2015.03.026 ↗
56. 10.1016/j.foodres.2007.09.00210.1016/j.foodres.2007.09.002 ↗
57. 10.1002/app.3342910.1002/app.33429 ↗
58. 10.1081/JFP-20004813910.1081/JFP-200048139 ↗
59. 10.1021/jf303480410.1021/jf3034804 ↗
60. 10.1016/j.carbpol.2010.03.04210.1016/j.carbpol.2010.03.042 ↗
61. 10.1016/j.ifset.2011.07.00610.1016/j.ifset.2011.07.006 ↗
62. 10.1002/pat.437810.1002/pat.4378 ↗
63. 10.1021/acs.iecr.7b0117110.1021/acs.iecr.7b01171 ↗
64. 10.1021/acsami.7b0132910.1021/acsami.7b01329 ↗
65. 10.1021/ie102438p10.1021/ie102438p ↗
66. 10.1007/s10965-021-02664-110.1007/s10965-021-02664-1 ↗
67. 10.1016/j.foodchem.2013.08.05910.1016/j.foodchem.2013.08.059 ↗
68. 10.1016/j.foodhyd.2009.09.00210.1016/j.foodhyd.2009.09.002 ↗
69. 10.1016/j.indcrop.2021.11352510.1016/j.indcrop.2021.113525 ↗
70. 10.1016/j.ijbiomac.2019.05.00910.1016/j.ijbiomac.2019.05.009 ↗
71. 10.1016/j.foodchem.2012.06.00310.1016/j.foodchem.2012.06.003 ↗
72. 10.1016/j.carbpol.2014.01.05410.1016/j.carbpol.2014.01.054 ↗
73. 10.1016/j.ijbiomac.2020.12.16610.1016/j.ijbiomac.2020.12.166 ↗
74. 10.1016/j.foodchem.2010.01.04810.1016/j.foodchem.2010.01.048 ↗
75. Masina N · Carbohyd Polym · 2016 · 57 · 281
76. Qin Y · Materials (Basel, Switzerland) · 2019 · 12 · 560
77. 10.1016/j.foodres.2009.03.01910.1016/j.foodres.2009.03.019 ↗
78. 10.1002/pen.2022910.1002/pen.20229 ↗
79. 10.1002/polb.2036610.1002/polb.20366 ↗
80. 10.1557/mrs.2011.20510.1557/mrs.2011.205 ↗
81. 10.1016/j.clay.2013.07.01110.1016/j.clay.2013.07.011 ↗
82. 10.1016/j.polymer.2006.08.03410.1016/j.polymer.2006.08.034 ↗
83. 10.1016/j.polymer.2010.03.04210.1016/j.polymer.2010.03.042 ↗
84. 10.1016/j.polymer.2009.12.03210.1016/j.polymer.2009.12.032 ↗
85. 10.1021/ie101375f10.1021/ie101375f ↗
86. 10.1016/j.polymer.2007.03.05610.1016/j.polymer.2007.03.056 ↗
87. 10.1016/j.polymer.2004.11.02810.1016/j.polymer.2004.11.028 ↗
88. 10.1002/pen.1010710.1002/pen.10107 ↗
89. 10.1002/pi.510410.1002/pi.5104 ↗
90. 10.1007/s10924-012-0455-010.1007/s10924-012-0455-0 ↗
91. 10.1002/mame.20030015610.1002/mame.200300156 ↗
92. 10.1021/ie201532h10.1021/ie201532h ↗
93. 10.1016/j.indcrop.2012.08.03210.1016/j.indcrop.2012.08.032 ↗
94. 10.1016/j.carbpol.2016.07.00910.1016/j.carbpol.2016.07.009 ↗
95. 10.1002/app.2204610.1002/app.22046 ↗
96. 10.1002/pen.76030201010.1002/pen.760302010 ↗