Functional ultra-high performance concrete with sisal fibre for nuclear containment: Mechanical, impact, and high-temperature performance
Source abstract
Abstract
Severe nuclear accidents entail the peril of falling molten corium onto the sacrificial concrete basemat, jeopardizing containment vessel integrity through structural compromise and potential radioactive release. Traditional sacrificial concrete poses challenges due to its limited strength and susceptibility to explosive spalling under extreme thermal stress. To reduce such risks, this research produced a functional ultra-high performance concrete (FUHPC) based on sisal fibre, which combines blast resistance, impact resistance and sacrificial properties. Using a Modified Andreasen and Andersen (MAA) model for mix design, a systematic study was conducted on the effects of different sisal fibre content on the mechanical properties, impact resistance, and high-temperature performance of FUHPC. The results indicate that when the fibre volume fraction is 0.6 vol%, the material properties are synergistically enhanced: (1) Flexural strength, compressive strength, elastic modulus and impact resistance were 25.72 MPa, 153.13 MPa, 48.30 GPa and 243.26 MPa respectively, representing increases of 19.74%, 16.03%, 15.77% and 16.96% compared to the control group. (2) Chloride ion migration coefficient decreased by 19.47%, and dry shrinkage rate decreased by 10.14%; (3) Microstructural analysis revealed that sisal fibres effectively refined the pores and formed a crack-blocking network, significantly enhancing the matrix density; (4) After exposure to 1000°C high temperatures, sisal fibres shrink to form interfacial gaps. Their natural tubular structure, combined with micro-cracks caused by thermal shrinkage, constructs a multi-scale steam channel network. This unique pore structure effectively dissipates internal steam pressure, preventing high-temperature explosions. Additionally, the free water content of FUHPC is below 5%, meeting the requirements for sacrificial concrete. Comprehensive performance evaluation determined that the optimal admixture ratio of sisal fibre is 0.6 vol%. This study provides a new approach for the development of explosion-resistant, impact resistance nuclear safety protection infrastructure. • Mixture of FUHPC was designed via MAA particle packing model. • Mechanical and impact resistance properties of FUHPC were improved via sisal fibre. • Pore structure of FUHPC were improved by sisal fibre. • High-temperature properties of FUHPC were improved via sisal fibre. • Optimal amount of sisal fibre in FUHPC was determined to be 0.6 vol%.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Fire effects on concrete materials · Innovative concrete reinforcement materials · Concrete and Cement Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (72)
Show source-provided references
1. The simulation of the fine crushing process of basalt-manufactured sand and its morphology's effect on the early age evolution of concrete ITZ
2. Preparation and properties of sisal fiber reinforced magnesium phosphate cement
3. Experimental study on mechanical properties of raw bamboo fibre-reinforced concrete
4. Tailored continuous flax Fiber-Reinforced shape memory polymer biocomposites: enhanced thermomechanical and shape memory performance for sustainable structural applications10.1016/j.compositesb.2025.112840 ↗
5. Studies on the durability of natural fibres and the effect of corroded fibres on the strength of mortar10.1016/j.cemconcomp.2004.09.008 ↗
6. Optimizing high-performance lightweight concrete with hybrid fiber: enhancing mechanical and thermal properties10.1016/j.conbuildmat.2024.139598 ↗
7. Effects of graphene sulfonate nanosheets on mechanical and thermal properties of sacrificial concrete during high temperature exposure10.1016/j.cemconcomp.2017.06.007 ↗
8. Thermal behavior of siliceous and ferro-siliceous sacrificial concrete subjected to elevated temperatures10.1016/j.matdes.2016.01.127 ↗
9. Effect of various polymer fibers on spalling mitigation of ultra-high performance concrete at high temperature10.1016/j.cemconcomp.2020.103815 ↗
10. Spalling behavior in ultra-high performance concrete: multi-technique insights and multi-scale fiber-rubber mitigation strategies
11. Influence of multi-scale fiber on residual compressive properties of a novel rubberized concrete subjected to elevated temperatures
12. Effect of spatial distribution of polymer fibers on preventing spalling of UHPC at high temperatures10.1016/j.cemconres.2020.106281 ↗
13. Effect of aggregate size and inclusion of polypropylene and steel fibers on explosive spalling and pore pressure in ultra high-performance concrete (UHPC) at elevated temperature10.1016/j.cemconcomp.2019.02.016 ↗
14. Influence of hybrid fibres on strength and stress-strain behaviour of concrete under uni-axial stresses10.1016/j.conbuildmat.2019.02.113 ↗
15. Preventive effects of polypropylene and jute fibers on spalling of UHPC at high temperatures in combination with waste porous ceramic fine aggregate as an internal curing material10.1016/j.conbuildmat.2019.02.056 ↗
16. Combined effect of flax fibers and steel fibers on spalling resistance of ultra-high performance concrete at high temperature10.1016/j.cemconcomp.2021.104067 ↗
17. Study on the dynamic impact mechanical properties of high-temperature resistant ultra-high performance concrete (HTRUHPC) after high temperatures
18. Characterization and properties of natural fiber polymer composites: a comprehensive review10.1016/j.jclepro.2017.10.101 ↗
19. Effects of various fibres on high-temperature spalling in high-performance concrete10.1016/j.conbuildmat.2014.07.068 ↗
20. Effect of natural fibers on thermal spalling resistance of ultra-high performance concrete10.1016/j.cemconcomp.2020.103512 ↗
21. Utilization of hybrid sisal and steel fibers to improve elevated temperature resistance of ultra-high performance concrete10.1016/j.cemconcomp.2022.104555 ↗
22. Axial compression performance of circular UHPC-filled stainless-steel tubular columns10.1016/j.engstruct.2023.117430 ↗
23. T.R. Allen, R.E. Stoller, S. Yamanaka. Comprehensive nuclear materials, Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States), 2012.
24. Investigation on response of HPR1000 under different mitigation strategies after SGTR accident10.1016/j.anucene.2017.10.024 ↗
25. Optimal formulation and performance evaluation of functional ultra-high performance concrete with barium ferrite
26. The “Chunnel” fire. I: chemoplastic softening in rapidly heated concrete
27. T. Sevón, Molten core-concrete interactions in nuclear accidents: theory and design of an experimental facility, VTT Technical Research Centre of Finland, 2005.
28. M. Nie, Temporary melt retention in the reactor pit of the European pressurized water reactor (EPR). 2005.
29. A new design approach of steel fibre reinforced ultra-high performance concrete composites: experiments and modeling10.1016/j.cemconcomp.2020.103597 ↗
30. Feasibility analysis of treating recycled rock dust as an environmentally friendly alternative material in Ultra-High performance concrete (UHPC)10.1016/j.jclepro.2020.120673 ↗
31. Mix design and properties assessment of ultra-high performance fibre reinforced concrete (UHPFRC)10.1016/j.cemconres.2013.11.002 ↗
32. Effects of graphene oxide on mechanical properties and microstructure of ultra-high-performance lightweight concrete
33. GB/T 2419-2005, The method for fluidity of cement mortar; Standards Press of China: Beijing, China, 2005. (In Chinese).
34. GB/T 17671-2021, Method of Testing Cements-Determination of Strength; Chin Architecture and Building Press: Beijing, China, 2021. (In Chinese).
35. GB/T50081-2019, Standard for Test Methods of Concrete Physical and Mechanical Properties, General Administration of Quality Supervision. Inspection and Quarantine, People’s Republic of China, (2019).
36. T/CECS 02:2020, Technical specification for detecting strength of concrete by ultrasonic-rebound combined method; China Planning Press: Beijing, China, 2020. (In Chinese).
37. JC/T 603-2004, Standard test method for drying shinkage of mortar; China Building Materials Industry Press: Beijing, China, 2004. (In Chinese).
38. GB/T 50082-2009, Standard for test methods of Long-term performance and durability of ordinary concrete; China Architecture and Building Press: Beijing, China, 2009. (In Chinese).
39. NT Build 492, Concrete, mortar and cement-based repair materials: Chloride migration coefficient from non-steady-state migration experiments, 1999.
40. Influence of sisal fibers on the mechanical performance of ultra-high performance concretes10.1016/j.conbuildmat.2021.122958 ↗
41. Static and dynamic compressive properties of ultra-high performance concrete (UHPC) with hybrid steel fiber reinforcements10.1016/j.cemconcomp.2017.02.010 ↗
42. Improvement effect of steel fiber orientation control on mechanical performance of UHPC10.1016/j.conbuildmat.2018.08.146 ↗
43. Effect of fiber content on mechanical and fracture properties of ultra high performance fiber reinforced cementitious composites10.1016/j.compstruct.2013.07.033 ↗
44. Mechanical properties of ambient cured high strength hybrid steel and synthetic fibers reinforced geopolymer composites10.1016/j.cemconcomp.2017.10.011 ↗
45. Fresh and hardened properties of Self-Compacting concrete reinforced with hybrid recycled Steel–Polypropylene fiber10.1061/(ASCE)MT.1943-5533.0001851 ↗
46. Experimental study on mechanical properties and durability of basalt fiber reinforced coral aggregate concrete10.1016/j.conbuildmat.2019.117628 ↗
47. Studies on mechanical properties characterization of hybrid sisal and stinging nettle fiber reinforced epoxy composite material10.1016/j.jmrt.2025.07.159 ↗
48. Prediction of the elastic modulus and the splitting tensile strength of concrete incorporating both fine and coarse recycled aggregate10.1016/j.conbuildmat.2019.04.212 ↗
49. Mechanical properties and microstructure of ultra-high-performance concrete with high elastic modulus10.1016/j.conbuildmat.2022.127385 ↗
50. Stray current induced chloride ion transport and corrosion characteristics of cracked ultra-high performance concrete10.1016/j.conbuildmat.2023.132536 ↗
51. Static and dynamic tensile properties of ultra-high performance concrete (UHPC) reinforced with hybrid sisal fibers
52. Static and dynamic compressive properties of ultra-high performance concrete (UHPC) with hybrid steel fiber reinforcements10.1016/j.cemconcomp.2017.02.010 ↗
53. Toughening in cement based composites. Part II: fiber reinforced cementitious composites10.1016/0958-9465(95)00029-1 ↗
54. Implication of pore size distribution parameters on compressive strength, permeability and hydraulic diffusivity of concrete10.1016/j.conbuildmat.2011.08.055 ↗
55. Effect of graphite nanoplatelets and carbon nanofibers on rheology, hydration, shrinkage, mechanical properties, and microstructure of UHPC10.1016/j.cemconres.2018.01.001 ↗
56. Mechanical properties of ambient cured high strength hybrid steel and synthetic fibers reinforced geopolymer composites10.1016/j.cemconcomp.2017.10.011 ↗
57. Sustainable seawater-sea sand cement mortar with municipal solid waste incineration ash: mechanical performance, microstructure, and environmental benefits10.1016/j.rineng.2025.106839 ↗
58. Concrete at high temperatures: material properties and mathematical models
59. Mechanical properties and hydration of ultra-high-performance seawater sea-sand concrete (UHPSSC) with limestone calcined clay cement (LC3)10.1016/j.conbuildmat.2023.130950 ↗
60. Synergistic effects of hybrid polypropylene and steel fibers on explosive spalling prevention of ultra-high performance concrete at elevated temperature10.1016/j.cemconcomp.2018.11.009 ↗
61. Splitting strength of GGBFS concrete incorporating with steel fiber and polypropylene fiber after exposure to elevated temperatures10.1016/j.firesaf.2012.07.009 ↗
62. Explosive spalling and residual mechanical properties of fiber-toughened high-performance concrete subjected to high temperatures10.1016/j.cemconres.2005.12.014 ↗
63. Compressive behavior of fiber reinforced high-performance concrete subjected to elevated temperatures10.1016/j.cemconres.2004.02.011 ↗
64. Compressive stress–strain relationship of steel fiber-reinforced reactive powder concrete after exposure to elevated temperatures10.1016/j.conbuildmat.2012.05.031 ↗
65. Permeability and pore structure evolution of silicocalcareous and hematite high-strength concretes submitted to high temperatures
66. Mechanical and thermal properties of graphene sulfonate nanosheet reinforced sacrificial concrete at elevated temperatures10.1016/j.conbuildmat.2017.07.157 ↗
67. Microstructure of fire-damaged concrete. A case study10.1016/j.cemconcomp.2004.02.022 ↗
68. Mechanical properties and ablation behaviour of nuclear sacrificial materials containing graphene sulfonate nanosheets10.1016/j.conbuildmat.2018.10.016 ↗
69. Spalling, thermal, and hydrous behavior of ordinary and high-strength concrete subjected to elevated temperature10.1061/(ASCE)MT.1943-5533.0000272 ↗
70. Review of concrete performance at elevated temperature and hot sodium exposure applications in nuclear industry10.1016/j.nucengdes.2013.01.018 ↗
71. H.J. Allelein, K. Neu, J.P.Van Dorsselaere, European Validation of the Integral Code ASTEC (EVITA): First experience in validation and plant sequence calculations, Nucl. Eng. Des. 235 (2-4) (2005) 285-308. https://doi.org/10.1016/j.nucengdes.2004.08.051.10.1016/j.nucengdes.2004.08.051 ↗
72. H. Alsmeyer, W. Tromm, The COMET concept for cooling core melts: Evaluation of the experimental studies and use in the EPR, Forschungszentrum Karlsruhe, 1999.