Insights into the corrosion resistance of Cr-Mo alloy reinforcing steel in simulated pore solution and real seawater sea-sand concrete: A preliminary study
Source abstract
Abstract
Corrosion of steel bars embedded in reinforced concrete structures considerably reduces the service life and even causes early failure of the structure. The purpose of this study is to investigate the corrosion resistance mechanism of Cr-Mo alloy reinforcing steel (CR) in seawater sea-sand concrete (SWSSC) and the possibility of its application in SWSSC. Three types of steel were carried out in real SWSSC and seawater sea-sand concrete pore solution (SWSSCPS). Compared with low-carbon steel (LC) and stain-less steel (SS), electrochemical measurements, AFM, XPS and SEM-EDS were applied to study the composition, structure and morphology characterizations of passive film. Electrochemical analysis revealed that in the initial stage of immersion, the corrosion resistance of CR demonstrated a rapid increase in open-circuit potential and electrochemical impedance spectroscopy (EIS), suggesting an active-passive transition process. The passive film on CR was found to have a distinct elemental distribution, with chromium and iron playing crucial roles in enhancing its stability. Based on the interactions of steel corrosion products and passive film at the steel-concrete and steel-solution interface, the possible formation of passive film and the resistance mechanism of CR were proposed. This study substantially augments the comprehension of the corrosion resistance characteristics of CR within SWSSC. Moreover, it proffers invaluable perspectives for the optimization of its utilization, which is conducive to fostering the advancement of reinforced concrete structures in marine and coastal zones.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete Corrosion and Durability · Corrosion Behavior and Inhibition · Concrete and Cement Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (41)
Show source-provided references
1. Deterioration of marine concrete exposed to wetting-drying action10.1016/j.jclepro.2020.123383 ↗
2. Evaluation of modulus of elasticity of concrete containing both natural and recycled concrete aggregates
3. Developing green and economical low-alkalinity seawater sea sand concrete via innovative processing underground sediment
4. Use of supplementary cementitious materials in seawater–sea sand concrete: state-of-the-art review10.1016/j.conbuildmat.2024.136009 ↗
5. Sand mining in BRICS economies: tragedy of the commons or fortune in the making?10.1016/j.jclepro.2023.140122 ↗
6. Development of admixtures on seawater sea sand concrete: a critical review on concrete hardening, chloride ion penetration and steel corrosion10.1016/j.conbuildmat.2023.134219 ↗
7. Seawater-mixed concretes containing natural and sea sand aggregates–a review10.1016/j.rineng.2023.101457 ↗
8. A review on seawater sea-sand concrete: mixture proportion, hydration, microstructure and properties10.1016/j.conbuildmat.2021.123602 ↗
9. Some considerations for applicability of seawater as mixing water in concrete10.1061/(ASCE)MT.1943-5533.0001006 ↗
10. Combined effect of metakaolin and sea water on performance and microstructures of concrete10.1016/j.conbuildmat.2014.10.023 ↗
11. Corrosion of carbon steel and corrosion-resistant rebars in concrete structures under chloride ion attack10.1007/s11665-012-0314-0 ↗
12. Influence of impressed current on the initiation of damage in reinforced mortar due to corrosion of embedded steel10.1016/j.cemconres.2007.08.022 ↗
13. Non-uniform rust expansion for chloride-induced pitting corrosion in RC structures10.1016/j.conbuildmat.2013.10.042 ↗
14. Microscopic investigation of mill scale and its proposed effect on the variability of chloride-induced depassivation of carbon steel rebar10.1016/j.corsci.2010.11.025 ↗
15. Effects of chloride ion binding on microstructure of cement pastes10.1061/(ASCE)MT.1943-5533.0001707 ↗
16. Durability of fiber reinforced polymer (FRP) in simulated seawater sea sand concrete (SWSSC) environment10.1016/j.corsci.2018.06.022 ↗
17. A review on mechanical properties of FRP bars subjected to seawater sea sand concrete environmental effects
18. Structural performance of stainless steel reinforced concrete members: a review10.1016/j.conbuildmat.2022.126673 ↗
19. Chloride-induced corrosion resistance of high-strength stainless steels in simulated alkaline and carbonated concrete pore solutions10.1016/j.corsci.2011.12.012 ↗
20. Experimental and numerical studies of reinforced concrete stair beams strengthened with steel bars and plates10.1016/j.engstruct.2023.117037 ↗
21. Mechanical behavior and durability of coral aggregate concrete and bonding performance with fiber-reinforced polymer (FRP) bars: A critical review10.1016/j.jclepro.2020.125652 ↗
22. Bond performance between FRP bars and geopolymer concrete after elevated temperature exposure10.1016/j.conbuildmat.2023.131476 ↗
23. Testing and numerical modelling of circular stainless steel reinforced concrete columns10.1016/j.engstruct.2024.117607 ↗
24. Wang · 2022 · 1247
25. Surface modification of fibres with silane for enhancing the durability of FRP composites as reinforcement for seawater sea sand concrete (SWSSC): a review10.1016/j.conbuildmat.2024.138678 ↗
26. Durability test on the flexural performance of seawater sea-sand concrete beams completely reinforced with FRP bars10.1016/j.conbuildmat.2018.10.166 ↗
27. Durability of FRP-to-concrete bonded joints subjected to 110 months accelerated laboratory and field exposure10.1016/j.engstruct.2024.117681 ↗
28. Evaluation of the long-term performance and durability of basalt fiber reinforced polymer bars in concrete structures10.1016/j.conbuildmat.2024.138226 ↗
29. Durability of seawater and sea sand concrete filled filament wound FRP tubes under seawater environments10.1016/j.compositesb.2020.108409 ↗
30. Effect of mill scale on the long-term corrosion resistance of a low-alloy reinforcing steel in concrete subjected to chloride solution10.1016/j.conbuildmat.2017.12.125 ↗
31. Initial-corrosion condition behavior of the Cr and Al alloy steel bars in coral concrete for marine construction10.1016/j.cemconcomp.2021.104051 ↗
32. Passive behaviour of alloy corrosion-resistant steel Cr10Mo1 in simulating concrete pore solutions with different pH10.1016/j.apsusc.2016.07.142 ↗
33. Corrosion resistance of low-alloy steel in concrete subjected to long-term chloride attack: characterization of surface conditions and rust layers10.1016/j.corsci.2022.110370 ↗
34. Function of Cu-Sb or Al microalloying on the corrosion resistance of 9Cr steel exposed to simulated concrete pore solution10.1016/j.corsci.2024.111983 ↗
35. Corrosion behavior and mechanism of Cr10Mo1 steel subjected to different corrosive ions in simulated concrete pore solution10.1016/j.jmrt.2024.09.148 ↗
36. Synergistic inhibition of molybdate and phytate on chloride-induced corrosion of carbon steel in simulated concrete pore solutions10.1016/j.cemconcomp.2023.105366 ↗
37. Corrosion resistance of Cr10Mo1 alloy corrosion-resistant steel in seawater–sea sand concrete pore solution10.1061/JMCEE7.MTENG-16693 ↗
38. On the penetration of corrosion products from reinforcing steel into concrete due to chloride-induced corrosion10.1016/j.corsci.2010.03.025 ↗
39. Oxide formation and conversion on carbon steel in mildly basic solutions10.1016/j.electacta.2009.05.020 ↗
40. Sato · 1998
41. Characterisation of passive films formed on low carbon steel in borate buffer solution (pH 9.2) by electrochemical impedance spectroscopy10.1016/j.apsusc.2005.02.135 ↗