Sulfate attack on portland-dolomite cement exposed to sodium sulfate solution at 5 ℃ and 20 ℃

The purpose of the study is to investigate the sulfate resistance of portland-dolomite cement (PDC) with varying dolomite contents, when exposed to sodium sulfate solution at 5 ℃ and 20 ℃. Visual appearance, expansion, mass change, and compressive strength of PDC mortars were tested, and XRD , FTIR , and SEM analyses were conducted to examine deterioration products and microstructure. Results indicate that at 20 ℃, the incorporation of 10 % dolomite in PDC had a negligible impact on sulfate resistance, whereas higher dolomite replacements of 20 % and 30 % notably diminished it. In contrast, exposure at 5 °C led to more severe deterioration in all PDC samples, regardless of dolomite content, and the higher dolomite content, the poorer resistance to sulfate attack . The increased formation of ettringite and gypsum resulted in reduced sulfate resistance of PDC at 20 ℃. However, at 5 ℃, the presence of dolomite significantly promoted the formation of thaumasite at later stages, which caused initial ettringite and subsequent late-stage thaumasite sulfate attack, ultimately leading to the failure of PDC. The findings suggest that PDC should be carefully considered when used in sulfate-rich environments, particularly at low temperatures.