Enhancing bending performance of cemented lithium feldspar tailings backfill with 3D printing polymer lattices: Effects of unit shapes and materials
Source abstract
Abstract
To comprehensively test and analyze the effects of three-dimensional printed polymer lattice (3DPPL) on the bending performance of cemented lithium feldspar tailings backfill (CLFTB) specimens, this study conducted three-point bending test on 3DPPL-reinforced CLFTB (3DPPL-RCLFTB) specimens prepared with different unit shapes: cube (CU), hexagonal prism (HE), octagon (OC) and materials: white resin (WR), black nylon (BN), transparent resin (TR). The results indicated that WR performed best in enhancing the strength of CLFTB, while TR was most effective in improving toughness, with OC was the optimal unit shape. The maximum strength and maximum deflection of 3DPPL-RCLFTB reached 5.961 MPa and 28.84 mm, respectively, representing increases of 2.75-3.74 times and 24.06-27.78 times compared to the control group (N-3DPPL-RCLFTB). All 3DPPL-RCLFTB specimens exhibited superior bending performance and ductility, with 3DPPL effectively prolonging the destruction process and significantly improving stability. The incorporation of 3DPPL transformed the destruction mode of CLFTB from a single crack destruction mode to a multiple crack destruction mode, shifting from brittle to ductile destruction. The maximum strain value on the surface of the 3DPPL-RCLFTB specimens was 36.343%, with the TR-OC-3DPPL-RCLFTB showing the best multiple crack destruction mode. • Using different 3DPPL enhanced the bending performance of CLFTB. • 3DPPL significantly improved the stability and toughness of CLFTB. • 3DPPL optimized the CLFTB destruction mechanism. • The surface strain of CLFTB was obtained by DIC.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Tailings Management and Properties · Rock Mechanics and Modeling · Grouting, Rheology, and Soil Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (73)
Show source-provided references
1. A multidisciplinary evaluation of mixtures of municipal solid waste incineration bottom ash and mine tailings for sustainable geotechnical solutions[J]10.1016/j.conbuildmat.2024.139139 ↗
2. The exploration of effect for nano-Al2O3 on solid waste based superfine tailings cemented paste backfill: pyrolysis property, hydration mechanism and environmental risk[J]10.1016/j.conbuildmat.2024.139035 ↗
3. Experimental study on iron ore tailings sand and municipal solid waste incineration fly ash used in semi-rigid base of asphalt pavement[J]10.1016/j.conbuildmat.2023.131981 ↗
4. Using soil tuff-modified polymetallic lead–zinc tailings sand to facilitate sustainable development of subgrade engineering[J]10.1016/j.conbuildmat.2024.136128 ↗
5. A multidisciplinary evaluation of mixtures of municipal solid waste incineration bottom ash and mine tailings for sustainable geotechnical solutions[J]10.1016/j.conbuildmat.2024.139139 ↗
6. Considering the development levels of countries, contributions of mineral recovery from mining tailings and urban mining wastes to sustainability criteria–a review[J]10.1016/j.resourpol.2024.105399 ↗
7. Exploring the economic potential of an electrochemical alternative to managing acid mine tailings[J]10.1016/j.mineng.2022.107968 ↗
8. Sediment source fingerprints of natural processes and anthropogenic pressures: a contribution to manage the Paraopeba River basin impacted by the B1 tailings dam collapse[J]10.1016/j.jenvman.2024.120590 ↗
9. Mechanical activation for sulfidic tailings treatment by tailings: environmental aspects and cement consumption reduction[J]
10. Improvement of tailings gradation on workability and strength of cemented tailings backfill[J]10.1016/j.conbuildmat.2023.131633 ↗
11. Multi-solid waste collaborative production of clinker-free cemented iron tailings backfill material with ultra-low binder-tailing ratio[J]10.1016/j.conbuildmat.2022.130271 ↗
12. A comparative study on the workability, mechanical properties and microstructure of cemented fine tailings backfill with different binder[J]10.1016/j.conbuildmat.2024.139189 ↗
13. Influence of fiber type and content on the flexural strength of cemented lithium feldspar tailings backfill composites[J]10.1016/j.jcou.2024.102990 ↗
14. Enhancing dynamic mechanical properties of cemented lithium mica tailings backfill with alkaline rice straw fibers: experimental investigation and microscopic analysis[J]
15. Study on mechanical behavior of inclined cemented tailings composite backfill (CTCB) under uniaxial compression[J]10.1016/j.conbuildmat.2024.137410 ↗
16. Compressive strength characteristics of cemented tailings backfill with alkali-activated slag[J]10.3390/app8091537 ↗
17. Strength efficiency evaluation of cemented tailings backfill with different stratified structures[J]10.1016/j.engstruct.2018.11.030 ↗
18. Conversion of recovered phosphorus tailings into high-value lightweight ceramic materials and evaluation of environmental safety[J]10.1016/j.psep.2024.11.005 ↗
19. Effect of prefabricated flaw angle on the mechanical properties and failure characteristics of stratified cemented tailings backfill[J]
20. Effect of microwave on coupled rheological and mechanical properties of cemented tailings backfill[J]10.1016/j.conbuildmat.2024.137558 ↗
21. Study on the performance of highly doped copper tailings sand for concrete pavements using specific grading techniques[J]10.1016/j.mineng.2024.108836 ↗
22. Investigation of flocculation behavior of tailings during settling-concentration: Influence of true density, particle size, and mud layer height[J]10.1016/j.jmrt.2023.09.032 ↗
23. Effect of calcination temperature on the activity of basalt tailings for the lightweight geopolymer from microwave curing[J]10.1016/j.matchemphys.2024.129991 ↗
24. Preliminary investigation of the effects of high-temperature thermal activation on the activity of graphite tailings and the mechanical properties of graphite tailings mortar[J]10.1016/j.conbuildmat.2024.138732 ↗
25. Multi-solid waste collaborative production of clinker-free cemented iron tailings backfill material with ultra-low binder-tailing ratio[J]10.1016/j.conbuildmat.2022.130271 ↗
26. Mechanical properties of uniaxial compression of total tailings paste under lateral restraint effect[J]10.1016/j.conbuildmat.2023.134702 ↗
27. Developing a robust indicator to evaluate circular economy through reuse strategy: A case study of using water treatment sludge as a coagulant for dewatering of iron ore tailings slurry[J]
28. A review of circular economy strategies for mine tailings[J]
29. Effects of modified multi-walled carbon nanotubes and PVA fibers on mechanical properties and microstructure of lithium slag base geopolymer[J]10.1016/j.conbuildmat.2024.137237 ↗
30. Engineering properties of natural fibre-reinforced one-part geopolymer concrete[J]10.1016/j.conbuildmat.2024.139161 ↗
31. Comparative mechanical performances of cement-treated sand reinforced with fiber for road and pavement applications[J]10.1016/j.trgeo.2021.100626 ↗
32. Development of a novel DNA-shaped steel fiber and its performance on fresh and hardened concrete[J]10.1016/j.conbuildmat.2024.138689 ↗
33. Compressive fatigue behavior and failure evolution of additive fiber-reinforced cemented tailings composites[J]10.1007/s12613-021-2351-x ↗
34. Exploring the effect of polyoxymethylene fiber on concrete toughness and self-sensing capability of concrete cracking under bending[J]10.1016/j.conbuildmat.2024.138933 ↗
35. Carbon nanotube reinforced cementitious tailings composites: Links to mechanical and microstructural characteristics[J]10.1016/j.conbuildmat.2022.130123 ↗
36. Effect of different fibers and fiber contents on the mechanical properties and failure behavior of early age cemented lithium feldspar tailings backfill[J]
37. Mechanical behavior and microscopic mechanism of synergistically enhanced cemented ultra-fine tailings backfill with polypropylene fiber and silica fume[J]10.1016/j.conbuildmat.2024.137668 ↗
38. Effect of alkaline rice straw fibers content and curing ages on static mechanical properties of cemented lithium mica tailings backfill[J]
39. Flexural performance and microstructural characterization of cement-treated sand reinforced with palm fiber[J]10.1016/j.jmrt.2023.06.036 ↗
40. Experimental study on mechanical properties, microstructure and ratio parameter optimization of mixed fiber-reinforced rubber cemented coarse aggregate backfill[J]10.1016/j.conbuildmat.2023.134105 ↗
41. Enhancing the physical properties of cemented ultrafine tailings backfill (CUTB) with fiber and rice husk ash: Performance, mechanisms, and optimization[J]10.1016/j.jmrt.2024.02.068 ↗
42. Recycling waste tyre polymer for production of fibre reinforced cemented tailings backfill in green mining[J]10.1016/j.scitotenv.2023.168320 ↗
43. Influence of basalt fiber on pore structure, mechanical performance and damage evolution of cemented tailings backfill[J]10.1016/j.jmrt.2023.10.240 ↗
44. Investigation of the dynamic mechanical properties and damage mechanisms of fiber-reinforced cemented tailing backfill under triaxial split-Hopkinson pressure bar testing[J]10.1016/j.jmrt.2023.09.236 ↗
45. The significance of mixing time in the development of the engineering properties of cemented fiber-reinforced tailings materials[J]
46. Experimental study on fiber-reinforced cement tailings sand-based grouting material preparation and factors influencing the grouting effect[J]10.1016/j.conbuildmat.2024.137104 ↗
47. Mechanical properties and interface microscopic characterisation of fibre-reinforced slag-fly ash geopolymer agglutinated iron tailings filling materials[J]
48. Study on flexural properties of 3D printing functionally graded lattice structure cement composites[J]10.1016/j.matlet.2024.137231 ↗
49. Compressive and flexural responses of auxetic sandwich panels with modified re-entrant honeycomb cores[J]10.1177/10996362241275532 ↗
50. The preparation and axial compressive properties of 3D-printed polymer lattice-reinforced cementitious composite columns[J]
51. Energy absorption and low-velocity impact responses of the sandwich panels with lattice truss core[J]10.1177/10996362241238272 ↗
52. Elevating mechanical performance of cementitious composites with surface-modified 3D-Printed polymeric reinforcements[J]
53. Influence of types and shapes of 3D printed polymeric lattice on ductility performance of cementitious backfill composites[J]10.1016/j.conbuildmat.2021.124973 ↗
54. Employing U-shaped 3D printed polymer to improve flexural properties of cementitious tailings backfills[J]10.1016/j.conbuildmat.2021.126296 ↗
55. The preparation and axial compressive properties of 3D-printed polymer lattice-reinforced cementitious composite columns[J]
56. Enhancing flexural property and mesoscopic mechanism of cementitious tailings backfill fabricated with 3D-printed polymers[J]10.1016/j.conbuildmat.2024.135009 ↗
57. Polymer shape effect on damage evolution, internal defects and crack propagation of 3D-printed polymer-based cementitious backfill[J]10.1016/j.conbuildmat.2023.133386 ↗
58. Influence of 3D-printed polymer structures on dynamic splitting and crack propagation behavior of cementitious tailings backfill[J]10.1016/j.conbuildmat.2022.128137 ↗
59. 3D-printed polymeric lattice-enhanced sustainable municipal solid waste incineration fly ash alkali-activated cementitious composites[J]
60. The preparation and axial compressive properties of 3D-printed polymer lattice-reinforced cementitious composite columns[J]
61. Study on flexural properties of 3D printed lattice-reinforced concrete structures using acoustic emission and digital image correlation[J]10.1016/j.conbuildmat.2022.127418 ↗
62. Damage and fracture investigation of self-compacting concrete in the filling layer of CRTS-III using three-point bending tests[J]
63. Interfacial bonding performance of 3D-printed Ultra-High Performance Strain-Hardening Cementitious Composites (UHP-SHCC) and cast normal concrete[J]
64. Methodological approach for mineralogical characterization of tailings from a Cu (Au, Ag) skarn type deposit using QEMSCAN (Quantitative Evaluation of Minerals by Scanning Electron Microscopy)[J]10.1016/j.gexplo.2019.106439 ↗
65. Flexural behavior of cementitious backfill composites reinforced by various 3D printed polymeric lattices[J]10.1016/j.compstruct.2023.117489 ↗
66. Study on flexural properties of 3D printed lattice-reinforced concrete structures using acoustic emission and digital image correlation[J]10.1016/j.conbuildmat.2022.127418 ↗
67. Cementitious composites reinforced with 3D printed functionally graded polymeric lattice structures: experiments and modelling[J]
68. Development of green binder systems based on flue gas desulfurization gypsum and fly ash incorporating slag or steel slag powders[J]10.1016/j.conbuildmat.2020.120275 ↗
69. Co-disposal of magnesium slag and high-calcium fly ash as cementitious materials in backfill[J]10.1016/j.jclepro.2020.123684 ↗
70. Effect of specimen composition on the strength development in cemented paste backfill[J]10.1139/t06-005 ↗
71. Preparation and application research of hybrid alkali-resistant glass fiber reinforced cement grout[J]
72. Mix design and flexural toughness of PVA fiber reinforced fly ash-geopolymer composites[J]10.1016/j.conbuildmat.2017.05.172 ↗
73. Influence of different fibers on compressive toughness and damage of early age cemented tailings backfill[J]10.1007/s11356-022-24830-8 ↗