Comparative study of nanomaterials activated recycled powders from demolition and decoration wastes as supplementary cementitious material
Source abstract
Abstract
Powdered particles can significantly affect the technical performance of recycled aggregates and recycled concrete. Therefore, there has been a considerable focus on the disposal and utilization of recycled powder (RP) with high value. This study applied nano-CaCO3 (NC), nano–graphene oxide (GO) and nano–SiO2 (NS) to activate RP from demolition and decoration waste (RP1 and RP2, respectively). The results indicated that the nanomaterials had an activation effect on RP, but the effect was more pronounced for RP2. In addition, NC had the best activation effect on the RP among the three nanomaterials. Comparing to cement pastes with 30% RP2, compressive strength of cement paste activated by NC, GO, and NS were increased by 43.4%, 33.3% and 23.7% at 28d, respectively. Thermogravimetric analysis (TGA), X-ray diffraction (XRD), Scanning electronic microscopy (SEM), and mercury intrusion porosity (MIP) were utilized to further explore the activation mechanism. Results presented that nanomaterial activated RP could promote hydration degree to produce more Ca(OH)2 (CH), meanwhile, the nanomaterials activated RP refine and modified the orientation index of CH. This paper implies a useful activation method for RP, which is expected to fully stimulate the potential of RP to form new kinds of supplementary cementitious material.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Recycled Aggregate Concrete Performance · Concrete and Cement Materials Research · Innovative concrete reinforcement materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (57)
Show source-provided references
1. Water transport and shrinkage in concrete made with ground recycled concrete-additioned cement and mixed recycled aggregate10.1016/j.cemconcomp.2021.103957 ↗
2. Performance of silica fume slurry treated recycled aggregate concrete reinforced with carbon fibers
3. Investigation on dynamic mechanical properties of fly ash/slag-based geopolymeric recycled aggregate concrete10.1016/j.compositesb.2020.107776 ↗
4. Synergic effect of recycled aggregate, fly ash, and hydrated lime in concrete production
5. Circular economy research on building construction and demolition waste: A review of current trends and future research directions10.1016/j.jclepro.2022.131927 ↗
6. Utilization of construction spoil and recycled powder in fired bricks
7. Changing the soaking method of microbially induced calcium carbonate precipitation technology to improve the reinforcement effect of recycled concrete aggregates
8. Effect of brick aggregate on failure process of mixed recycled aggregate concrete via X-CT10.1016/j.conbuildmat.2022.126934 ↗
9. Transfer properties in recycled aggregates concrete: experimental and numerical approaches10.1016/j.conbuildmat.2022.126778 ↗
10. Assessing the relaxation of recycled aggregates concrete from free and restrained shrinkage tests
11. The effect of mechanical-thermal synergistic activation on the mechanical properties and microstructure of recycled powder geopolymer10.1016/j.jclepro.2021.129477 ↗
12. The utilization of active recycled powder from various construction wastes in preparing ductile fiber-reinforced cementitious composites: a case study
13. The utilization of eco-friendly recycled powder from concrete and brick waste in new concrete: A critical review10.1016/j.cemconcomp.2020.103807 ↗
14. Performance of asphalt mortar with recycled concrete powder under different filler-to-asphalt weight ratios
15. Low-carbon stabilization/solidification of municipal solid waste incineration fly ash10.1007/s42768-022-00102-6 ↗
16. Valorisation of alum sludge to produce green and durable mortar10.1007/s42768-022-00113-3 ↗
17. Incorporation of natural waste from agricultural and aquacultural farming as supplementary materials with green concrete: A review10.1016/j.compositesb.2019.107076 ↗
18. Mechanical properties of concrete mixed with recycled powder produced from construction and demolition waste10.1016/j.jclepro.2018.03.277 ↗
19. Properties of self-consolidating concrete with recycled clay-brick-powder replacing cementitious material
20. Effect of recycled concrete powder on strength, electrical resistivity, and water absorption of self-compacting mortars
21. Chloride permeability of concrete mixed with activity recycled powder obtained from C&D waste10.1016/j.conbuildmat.2018.12.065 ↗
22. Combined use of recycled powder and recycled coarse aggregate derived from construction and demolition waste in self-compacting concrete10.1016/j.conbuildmat.2020.119323 ↗
23. Quality properties of self-consolidating concrete mixed with waste concrete powder10.1016/j.conbuildmat.2016.12.174 ↗
24. Utilization potential of aerated concrete block powder and clay brick powder from C&D waste10.1016/j.conbuildmat.2019.117721 ↗
25. The particle-size effect of waste clay brick powder on its pozzolanic activity and properties of blended cement10.1016/j.jclepro.2019.118521 ↗
26. Effect of particle size and CO2 treatment of waste cement powder on properties of cement paste
27. Comparison of technical properties of cement pastes with different activated recycled powder from construction and demolition waste10.1016/j.cemconcomp.2021.104065 ↗
28. Effects of carbonated hardened cement paste powder on hydration and microstructure of Portland cement10.1016/j.conbuildmat.2018.07.159 ↗
29. Utilizing thermal activation treatment to improve the properties of waste cementitious powder and its newmade cementitious materials10.1016/j.jclepro.2021.129074 ↗
30. Orthogonal experimental and theoretical study on mechanical properties of fiber-reinforced recycled powder concrete
31. Utilizing heat-mechanical synergistic treatment for separating concrete waste into high-quality recycled aggregate, active recycled powder and new concrete
32. Environmental assessment and geomechanical properties of controlled low-strength materials with recycled and alternative components for cements and aggregates10.1016/j.cemconcomp.2017.03.013 ↗
33. Surface characterization of carbonated recycled concrete fines and its effect on the rheology, hydration and strength development of cement paste10.1016/j.cemconcomp.2020.103809 ↗
34. Characteristics of decoration waste dusting powder and its effect on mechanical properties of cement paste
35. Management system for engineering and decoration waste: an exploratory study in Shenzhen10.1016/j.jenvman.2022.115085 ↗
36. China National Standards GB 175, Common Portland Cement, Beijing, China, 2007 (in Chinese).
37. An approach to effectively improve the interfacial bonding of paste-limestone by incorporating different nanomaterials10.1016/j.compositesb.2022.110046 ↗
38. Comparative study on mechanisms for improving mechanical properties and microstructure of cement paste modified by different types of nanomaterials10.1515/ntrev-2021-0027 ↗
39. Influence of silane on hydration characteristics and mechanical properties of cement paste10.1016/j.cemconcomp.2020.103743 ↗
40. Properties of cement pastes and mortars containing recycled green glass powder10.1016/j.conbuildmat.2020.120875 ↗
41. China National Standards GB/T50081, Standard for Test Method of Mechanical Properties on Ordinary Concrete, 2002. Beijing, China (in Chinese).
42. The hydration of cement paste using the semi-isothermal method of derivative thermogravimetry10.1016/0008-8846(80)90111-8 ↗
43. Effects of chemical composition of fly ash on compressive strength of fly ash cement mortar10.1016/j.conbuildmat.2019.01.208 ↗
44. Deterioration mechanism of plain and blended cement mortars partially exposed to sulfate attack10.1016/j.conbuildmat.2017.08.017 ↗
45. Investigation of recycled powder as supplementary cementitious material10.1680/jmacr.18.00513 ↗
46. Recycled gypsum powder from waste drywalls combined with fly ash for partial cement replacement in concrete10.1016/j.jclepro.2020.122785 ↗
47. Study on the essential properties of recycled powders from construction and demolition waste10.1016/j.jclepro.2019.119865 ↗
48. EN 450–1:2012 Fly Ash for Concrete. Definition, Specifications and Conformity Criteria; European Committee for Standardization: Brussels, Belgium, 2012.
49. China National Standards GB/T 1596–2017, Fly ash for cement and concrete, 2017. Beijing, China (in Chinese).
50. Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete.
51. An investigation into the hydration and microstructure of cement pastes modified with glass powders10.1016/j.conbuildmat.2016.02.085 ↗
52. The effect of zeolite on the properties and hydration of blended cements10.1016/j.cemconcomp.2009.10.004 ↗
53. Effect of graphene oxide on the hydration and microstructure of fly ash-cement system10.1016/j.conbuildmat.2018.11.199 ↗
54. Effect of nano-TiO2 on the mechanical properties of cement mortar10.1016/j.conbuildmat.2011.10.047 ↗
55. J. Grandet, J. Ollivier. 7th International Congress on the Chemistry of Cement, Paris, vol. 3, VII-85, 1980.
56. Z. Wu, H.Lian. High Performance Concrete, [M] China railway publishing house, 1999.
57. Mindess · 2003