Study on the effect of nano-silica on the early-age strength and microstructure of cement paste mixed with calcium nitrite under negative temperature conditions
Source abstract
Abstract
During construction at low temperatures, fresh concrete is susceptible to early freeze damage, which can permanently damage the concrete structure. Therefore, this study aimed to enhance the early-age strength and durability properties of the cement paste at −5 ℃ by incorporating calcium nitrite (CN) antifreeze and nano-silica (NS). First, the effects of CN and NS on the fresh properties of the cement paste were measured by setting time and bleeding rate tests. Subsequently, the mechanical properties and chloride content after salt solution erosion were tested for each group of specimens, and the change in slurry densification was further observed by ultrasonic pulse velocity and resistivity tests. Finally, the hydration products and microstructure of the specimens were analyzed using XRD and SEM tests. The results showed that the addition of CN and NS could reduce the setting time of cement paste and avoid the bleeding phenomenon of cement paste under negative temperature environment. The decrease in curing temperature and the use of NS both inhibited the promotion of C3A hydration by nitrite ions, which led to a decrease in nitrite-AFm content. However, NS can compensate for the reduced nitrite-AFm content by promoting the production of hydrated C-S-H through nucleation and pozzolanic effects. Ultimately, the strength and resistance of the slurry to chloride erosion are improved.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Innovative concrete reinforcement materials · Magnesium Oxide Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (61)
Show source-provided references
1. Effects of nano-silica modification on early age hydration process in winter construction of tunnel engineering10.1016/j.conbuildmat.2023.133804 ↗
2. Effect of w/c ratio and antifreeze admixture on the frost damage of sulfoaluminate cement concrete at − 20 °C10.1016/j.conbuildmat.2022.128457 ↗
3. Analysis of damage development in cement paste due to ice nucleation at different temperatures10.1016/j.cemconcomp.2014.06.007 ↗
4. Damage study on service performance of early-age frozen concrete10.1016/j.conbuildmat.2019.03.199 ↗
5. Gradient power modified ohmic heating curing to prepare hybrid carbon fibers/high performance concrete under deep-freeze low temperature10.1016/j.conbuildmat.2022.127279 ↗
6. Experimental research on development of heated form incorporating exothermic reaction powder to protect concrete in cold weather10.1016/j.conbuildmat.2016.12.136 ↗
7. Potential application of Portland cement-calcium sulfoaluminate cement blends to avoid early age frost damage10.1016/j.conbuildmat.2018.09.136 ↗
8. Hydration mechanism and early frost resistance of calcium sulfoaluminate cement concrete10.1016/j.conbuildmat.2019.117862 ↗
9. Early-age mechanical properties and hydration degrees of magnesium phosphate cement paste in freezing winter of cold regions10.1016/j.conbuildmat.2022.128337 ↗
10. Mechanical properties of high-ductility magnesium phosphate cement composite cured at low temperatures
11. Hydration investigation of negative temperature concrete at early age based on low-field nuclear magnetic resonance10.1016/j.coldregions.2021.103449 ↗
12. The effects of urea on strength gaining of fresh concrete under the cold weather conditions10.1016/j.conbuildmat.2014.04.008 ↗
13. The performance of calcium sulfoaluminate cement for preventing early-age frost damage10.1016/j.conbuildmat.2020.119322 ↗
14. Recent progress and technical challenges in using calcium sulfoaluminate (CSA) cement10.1016/j.cemconcomp.2022.104908 ↗
15. The performance of magnesium phosphate cement in negative temperature environment: a state-of-the-art review
16. Effects of pre-curing treatment and chemical accelerators on Portland cement mortars at low temperature (5 °C)10.1016/j.conbuildmat.2019.117893 ↗
17. The evaluation of chemical admixtures on the performance of cement stabilized materials in cold weather10.1016/j.trgeo.2021.100618 ↗
18. Calcium-silicate-hydrate seeds as an accelerator for saving energy in cold weather concreting10.1016/j.conbuildmat.2020.120191 ↗
19. Calcium sulphoaluminate cement used as mineral accelerator to improve the property of Portland cement at sub-zero temperature10.1016/j.cemconcomp.2019.103452 ↗
20. Flow ability of cemented paste backfill with chloride-free antifreeze additives in sub-zero environments10.1016/j.cemconcomp.2021.104359 ↗
21. Study of the effect of calcium nitrate, calcium formate, triethanolamine, and triisopropanolamine on compressive strength of Portland-pozzolana cement
22. Do chlorides qualify as accelerators for the cement of deepwater oil wells at low temperature?10.1016/j.conbuildmat.2016.12.089 ↗
23. Effect of sodium chloride concentration and pre-curing time on the properties of cemented paste backfill in a sub-zero environment10.1016/j.jclepro.2020.125310 ↗
24. Effect of surface preparation on corrosion of steel rebars coated with cement-polymer-composites (CPC) and embedded in concrete10.1016/j.conbuildmat.2019.117616 ↗
25. Modeling the corrosion of steel casing and the damage of well cement in a borehole system10.1016/j.conbuildmat.2020.119701 ↗
26. The effect of thiocyanates on the hydration of portland cement at low temperatures10.1016/0040-6031(95)02323-T ↗
27. New insights into the impact of inorganic salt on cement pastes mixed with alkali free liquid accelerator in low temperature
28. Early age performance of OPC-GGBFS-concretes containing Belite-CSA cement cured at sub-zero temperatures10.3390/buildings13092374 ↗
29. Accelerators for normal concrete: a critical review on hydration, microstructure and properties of cement-based materials10.1016/j.cemconcomp.2022.104762 ↗
30. Characterization of chemical accelerators for sustainable recycling of fresh electric-arc furnace dust in cement pastes10.1016/j.apt.2021.06.019 ↗
31. Effect of a Nitrite/Nitrate-Based Accelerator on the Strength Development and Hydrate Formation in Cold-Weather Cementitious Materials10.3390/ma14041006 ↗
32. Investigation of the relationship between compressive strength and hydrate formation behavior of low-temperature cured cement upon addition of a nitrite-based accelerator10.3390/ma12233936 ↗
33. Performance buildup of concrete cured under low-temperatures: use of a new nanocomposite accelerator and its application10.1016/j.conbuildmat.2022.127529 ↗
34. Low-temperature (−10 °C) curing of Portland cement paste – Synergetic effects of chloride-free antifreeze admixture, C–S–H seeds, and room-temperature pre-curing10.1016/j.cemconcomp.2021.104319 ↗
35. Study on the long-term chloride permeability of nano-silica modified cement pastes cured at negative temperature
36. Effect of nano-modified additives on properties of concrete mixtures during winter season10.1016/j.conbuildmat.2019.117527 ↗
37. Nano-modified concrete at sub-zero temperatures: experimental and statistical modelling10.1680/jmacr.19.00437 ↗
38. Physicochemical study on the strength development characteristics of cold weather concrete using a nitrite-nitrate based accelerator10.3390/ma12172706 ↗
39. GB/T 1346-2011 · Test Methods for Water Requirement of Normal Consistency, Setting Time and Soundness of the Portland Cement, Beijing · 2011
40. JTG 3420-2020 · Testing Methods of Cement and Concrete for Highway Engineering, BeiJing · 2020
41. GB/T 17671-2021 · 2021
42. Assessment of the influence of nano-silica on the behavior of mortar using factorial design of experiments10.1016/j.conbuildmat.2014.06.074 ↗
43. Effect of using nano-silica on the rheological, fresh and strength characteristics of cement-based grout for grouting columns
44. Effect of triisopropanolamine on the compressive strength and early hydration of cement at low temperature10.1007/s11595-020-2298-1 ↗
45. Assessment and mechanism study of bleeding process in cement paste by 1H low-field NMR10.1016/j.conbuildmat.2015.09.062 ↗
46. High performance green concrete (HPGC) with improved strength and chloride ion penetration resistance by synergistic action of fly ash, nanoparticles and corrosion inhibitor10.1016/j.conbuildmat.2018.11.266 ↗
47. Influence of nano-SiO2 on the Portland cement pastes10.1016/j.compositesb.2011.12.015 ↗
48. Strengthening mechanism of fracture properties by nano materials for cementitious materials subject to early-age frost attack10.1016/j.cemconcomp.2021.104025 ↗
49. Effect of Nano-SiO2 on the Hydration and Microstructure of Portland Cement10.3390/nano6120241 ↗
50. Investigation of self-healing ability of hydroxyapatite blended cement paste modified with graphene oxide and silver nanoparticles10.1016/j.conbuildmat.2021.126250 ↗
51. Evaluation of the phase composition, microstructure, mechanical performance, and resistance to acid attack of blended cement paste composed of binary trass-cement system10.1016/j.conbuildmat.2022.127356 ↗
52. Mechanical properties and durability of ternary blended cement paste containing rice husk ash and nano silica10.1016/j.conbuildmat.2022.127732 ↗
53. Beneficial role of nanosilica in cement based materials – a review10.1016/j.conbuildmat.2013.05.052 ↗
54. Impact of accelerating admixtures on the electrical properties of ordinary portland cement pastes10.1016/j.cemconcomp.2022.104651 ↗
55. The mechanical strength, degree of hydration, and electrical resistivity of cement pastes modified with superabsorbent polymers10.1016/j.conbuildmat.2015.12.082 ↗
56. An investigation into the influence of superabsorbent polymers on the properties of glass powder modified cement pastes10.1016/j.conbuildmat.2017.04.125 ↗
57. Hydration products in sulfoaluminate cements: evaluation of amorphous phases by XRD/solid-state NMR10.1016/j.cemconres.2016.05.014 ↗
58. Behavior of fresh and hardened concretes with antifreeze admixtures in deep-freeze low temperatures and exterior winter conditions10.1016/j.conbuildmat.2014.12.011 ↗
59. Effect of the early-age frost damage and nano-SiO2 modification on the properties of Portland cement paste10.1016/j.conbuildmat.2020.120098 ↗
60. Prediction of adiabatic temperature rise in conventional and high-performance concretes Using a 3-D microstructural model10.1016/S0008-8846(97)00264-0 ↗
61. Physicochemical effects of nanosilica on C3A/C3S hydration10.1111/jace.17364 ↗