Evaluation of the mechanical properties, microstructure, and environmental impact of mortar incorporating metakaolin, micro and nano-silica
Source abstract
Abstract
The optimized use of nanomaterials in concrete for developing resilient and eco-friendly infrastructure is vital for our built environment. Therefore, the current study aims to optimize the dosages and particle sizes of colloidal nano-silica in developing high-performance, sustainable cement mortar. For this purpose, compressive strength, water absorption, porosity, and microstructure tests were performed on mortars containing different dosages and particle sizes (NS80, NS250, NS250Al, NS500) of colloidal nano-silica. For comparison, tests were also performed on control mortars and mortars containing metakaolin and silica fume. The microstructure of cement pastes was examined through SEM-based BSE imaging with elemental mapping through EDS and FTIR analyses. Additionally, global warming potential (GWP) as well as embodied energy (EE) were also analyzed for all mortar mixtures. The results demonstrated that smaller nano-sized particles (NS500) at a lower dosage (3%) showed improved compressive strength and densified microstructure compared to all other mixes. However, larger nano-sized particles (NS80) at medium (5%) and high dosages (10%) had the highest impact on compressive strengths due to the formation of low and medium Ca-based C-S-H and C-A-S-H phases. Furthermore, the results of greater compressive strength of NS80 mortars under medium and high dosages were supported by their lowest water absorption and apparent porosity. When compared with the control and all other mixes, the mortar mixes containing medium and high doses of NS80 had lower embodied energy/MPa and CO2-eq intensity/MPa, indicating their significant contribution to producing green concrete with a lower environmental impact.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Building materials and conservation · Magnesium Oxide Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (92)
Show source-provided references
1. Effect of supplementary cementitious materials on reduction of CO2 emissions from concrete10.1016/j.jclepro.2014.03.018 ↗
2. Carbon dioxide reduction potential in the global cement industry by 205010.1016/j.cemconres.2017.08.026 ↗
3. Zhongming Z., Linong L., Xiaona Y., Wangqiang Z., Wei L. Cement technology roadmap shows how the path to achieve CO2 reductions up to 24% by 2050. 2018.
4. Anthropogenic carbon and ocean pH10.1038/425365a ↗
5. Irreversible climate change due to carbon dioxide emissions10.1073/pnas.0812721106 ↗
6. Eco-efficient cements: potential economically viable solutions for a low-CO2 cement-based materials industry10.1016/j.cemconres.2018.03.015 ↗
7. Towards sustainable concrete10.1038/nmat4930 ↗
8. Alternative pathways to the 1.5C target reduce the need for negative emission technologies10.1038/s41558-018-0119-8 ↗
9. An Empathetic Added Sustainability Index for cementitious based construction materials10.1016/j.jclepro.2019.02.160 ↗
10. Recent progress in low-carbon binders10.1016/j.cemconres.2019.05.009 ↗
11. Sbci · 2009 · 1
12. Towards ternary binders involving limestone additions—A review10.1016/j.cemconres.2021.106396 ↗
13. Mechanical properties and durability characteristics of SCC incorporating crushed limestone powder
14. Microstructural and thermal characterization of concretes prepared with the addition of raw and milled fly ashes10.1016/j.jmrt.2022.07.171 ↗
15. Steel slag and its applications in cement and concrete technology: a review10.1016/j.conbuildmat.2021.122783 ↗
16. Silica fume and waste glass in cement concrete production: A review
17. Review on the use of volcanic ashes for engineering applications10.1016/j.resconrec.2018.05.031 ↗
18. Evaluation of structural performances of metakaolin based geopolymer concrete10.1016/j.jmrt.2022.08.020 ↗
19. Recycling of rice husk waste for a sustainable concrete: a critical review10.1016/j.jclepro.2021.127734 ↗
20. Incorporation of agricultural residues as partial substitution for cement in concrete and mortar–A review
21. A critical review of waste glass powder–Multiple roles of utilization in cement-based materials and construction products10.1016/j.jenvman.2019.04.098 ↗
22. Influence of nano and micro-silica additions on the durability of a high-performance self compacting concrete10.1016/j.conbuildmat.2017.12.100 ↗
23. Nanotechnology in cement-based materials: A review of durability, modeling, and advanced characterization10.3390/nano9091213 ↗
24. Characteristics of cement mortar with nano-SiO2 particles10.1016/j.conbuildmat.2005.12.020 ↗
25. Durability studies of nano-engineered fly ash concrete10.1016/j.conbuildmat.2018.11.022 ↗
26. Nano-core effect in nano-engineered cementitious composites10.1016/j.compositesa.2017.01.008 ↗
27. Effect of nano-SiO2, nano-Al2O3 and nano-Fe2O3 powders on compressive strengths and capillary water absorption of cement mortar containing fly ash: a comparative study10.1016/j.enbuild.2012.12.014 ↗
28. The effect of nano-MgO on the setting time, autogenous shrinkage, microstructure and mechanical properties of high performance cement paste and mortar10.1016/j.conbuildmat.2017.08.168 ↗
29. Exploring the influence of SiO2 and TiO2 nanoparticles on the mechanical properties of concrete10.1016/j.conbuildmat.2018.04.181 ↗
30. Effect of nano-CaCO3 on Properties of Cement Paste10.1016/j.egypro.2012.01.158 ↗
31. Mohammed S. Al Jawahery, Salim T. Yousif. Optimization of sustainable concrete characteristics incorporating palm oil clinker and nano-palm oil fuel ash using response surface methodology10.1016/j.powtec.2022.118054 ↗
32. Hydration and properties of nano-TiO2 blended cement composites10.1016/j.cemconcomp.2012.02.009 ↗
33. Utilization of nano-metakaolin in concrete: a review
34. Utilizing nano-SiO2 for modifying the microstructure, strength and transport properties of sustainable cementitious materials with waste concrete powder
35. silica in cement hydration10.1016/j.matpr.2017.10.044 ↗
36. Quantification and characterization of C-S-H in silica nanoparticles incorporated cementitious system10.1016/j.cemconcomp.2017.02.004 ↗
37. Studies on optimization of silica nanoparticles dosage in cementitious system10.1016/j.cemconcomp.2016.03.006 ↗
38. Use of nano-silica to increase early strength and reduce setting time of concretes with high volumes of slag10.1016/j.cemconcomp.2012.02.005 ↗
39. A. Naji Givi, S. Abdul Rashid, F.N.A. Aziz, M.A.M. Salleh. Experimental investigation of the size effects of SiO2 nano-particles on the mechanical properties of binary blended concrete.
40. Behavior of colloidal nanosilica in an ultrahigh performance concrete environment using dynamic light scattering10.3390/ma12121976 ↗
41. Experimental investigation on nanomaterial concrete
42. Impact of nanosilica size and surface area on concrete properties
43. Properties of concrete incorporating nano-silica10.1016/j.conbuildmat.2012.06.044 ↗
44. Strength elastic and microstructural properties of SCCs’ with colloidal nano silica addition10.1016/j.conbuildmat.2017.10.041 ↗
45. ASTM C150/C150M-16e1, 2023. Standard Specification for Portland Cement. Available online: 〈www.astm.org〉 (Accessed on 10 Feb 2023).
46. Optimization of colloidal nano-silica based cementitious mortar composites using RSM and ANN approaches10.1016/j.rineng.2023.101390 ↗
47. AFNOR-Association Française de Normalisation-Standard NF P 18–513/2012-Pozzolanic Addition for Concrete-Metakaolin-Definitions, Specifications and Conformity Criteria; La Plaine Saint-Denis: AFNOR: Paris, France, 2012;
48. ASTM C305–14. Standard Practice for Mechanical Mixing of Hydraulic Cement Pastes and Mortars of Plastic Consistency. Available online: 〈http://www.astm.org〉 (Accessed on 10 Feb 2023).
49. ASTM C109/C109M-16a. Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens). Available online: 〈http://www.astm.org〉 (Accessed on 10 Feb 2023).
50. ASTM C948. Standard Test Method for Dry and Wet Bulk Density, Water Absorption, and Apparent Porosity of Thin Sections of Glass-Fiber Reinforced Concrete. Available online: 〈http://www.astm.org〉 (Accessed on 10 Feb 2023).
51. Life cycle assessment (LCA) of ultra-high performance concrete (UHPC) structures
52. O. Vennesland, O.E. Gjørv, Silica Concrete-Protection Against Corrosion of Embedded Steel, Fly Ash, Silica Fume, Slag, and Other Mineral By-Products in Concrete, in: V.M. Malhotra (Ed.), Proceedings of the 1st CANMET/ACI International Conference, SP-79, American Concrete Institute, Farmington Hills, Mich., pp. 719–730.
53. Performances evaluation of binary concrete designed with silica fume and metakaolin10.1016/j.conbuildmat.2018.01.138 ↗
54. Assessment of embodied energy in the production of Ultra High Performance Concrete (UHPC)
55. Rheology and workability of SCC
56. An environmental evaluation of geopolymer based concrete production: reviewing current research trends10.1016/j.jclepro.2011.03.012 ↗
57. NLK , 2002. "Ecosmart concrete project metakaolin pre-feasibility study". NLK Consultant Inc. vancouver, Canada (2002).
58. Influence of metakaolinization temperature on the formation of zeolite 4A from kaolin10.1180/claymin.1996.031.2.11 ↗
59. Minimising the global warming potential of clay based geopolymers10.1016/j.jclepro.2014.04.046 ↗
60. Comparative environmental assessment of limestone calcined clay cements and typical blended cements10.1088/2515-7620/acccd8 ↗
61. Utilization of agricultural, industrial waste and nanosilica as replacement for cementitious material and natural aggregates – Mechanical, microstructural and durability characteristics assessment
62. The effects of SiO2 nanoparticles on physical and mechanical properties of high strength compacting concrete10.1016/j.compositesb.2010.09.025 ↗
63. Satyajit, P., Effect of Nanosilica on the Compressive Strength of Concrete, B. Tech Civil Engineering Thesis. National Institute of Technology, Rourkela, (2015) 1–44.
64. Hydration and characteristics of metakaolin pozzolanic cement pastes
65. Properties of concrete incorporating nano-silica10.1016/j.conbuildmat.2012.06.044 ↗
66. Strength, elastic and microstructural properties of SCCs’ with colloidal nano silica addition10.1016/j.conbuildmat.2017.10.041 ↗
67. Incinerator residual ash metakaolin blended cement- effects on cement hydration and properties10.1016/j.conbuildmat.2019.02.060 ↗
68. Influence of metakaolin in concrete as partial replacement of cement. cementitious composites
69. Characterization of metakaolin and study on early age mechanical strength of hybrid cementitious composites10.1016/j.conbuildmat.2016.06.039 ↗
70. Towards ternary binders involving limestone additions—A review10.1016/j.cemconres.2021.106396 ↗
71. Effects of nanosilica on microstructure and durability of cement-based materials10.1016/j.powtec.2022.117447 ↗
72. Studies on enhanced thermally stable high strength concrete incorporating silica nanoparticles10.1016/j.conbuildmat.2017.07.057 ↗
73. Influence of nano and micro-silica additions on the durability of a high-performance self compacting concrete10.1016/j.conbuildmat.2017.12.100 ↗
74. Study of durability of Portland cement mortars blended with silica nanoparticles10.1016/j.conbuildmat.2014.12.074 ↗
75. Use of nano-silica to increase early strength and reduce setting time of concretes with high volumes of slag10.1016/j.cemconcomp.2012.02.005 ↗
76. Micro-macro characterizations of mortar containing construction waste fines as replacement of cement and sand: a comparative study10.1016/j.conbuildmat.2023.131328 ↗
77. Influence of colloidal silica sol on fresh properties of cement paste as compared to nano-silica powder with agglomerates in micron-scale10.1016/j.cemconcomp.2015.08.002 ↗
78. The micromechanical signature of high-volume natural pozzolan concrete by combined statistical nanoindentation and SEM-EDS analyses10.1016/j.cemconres.2016.10.004 ↗
79. Effect and mechanism of colloidal silica sol on properties and microstructure of the hardened cement-based materials as compared to nano-silica powder with agglomerates in micron-scale10.1016/j.cemconcomp.2019.02.015 ↗
80. Influence of mechanically activated electric arc furnace slag on compressive strength of mortars incorporating curing moisture and temperature effects10.3390/su9081178 ↗
81. Compatibility studies between N-A-S-H and C-A-S-H gels. Study in the ternary diagram Na2O–CaO–Al2O3–SiO2–H2O10.1016/j.cemconres.2011.05.006 ↗
82. Microstructure of cement paste with natural pozzolanic volcanic ash and Portland cement at different stages of curing10.1016/j.conbuildmat.2016.03.084 ↗
83. Hydration kinetics, microstructure and physicochemical performance of metakaolin-blended cementitious composites10.1016/j.conbuildmat.2023.133756 ↗
84. Comparative study of accelerated decalcification process among C3S, grey and white cement pastes10.1016/j.cemconcomp.2011.11.002 ↗
85. Physicochemical and cementitious properties of sludge from oil field effluent treatment plant10.1016/S0008-8846(01)00550-6 ↗
86. FTIR study of the effect of temperature and nanosilica on the nano structure of C–S–H gel formed by hydrating tricalcium silicate10.1016/j.conbuildmat.2013.10.056 ↗
87. Synthesis of calcium carbonate in alkali solution based on graphene oxide and reduced graphene oxide10.1016/j.jssc.2018.03.005 ↗
88. Carbonation of Portland cement studied by diffuse reflection Fourier transform infrared spectroscopy10.1007/s40069-013-0039-y ↗
89. A Fourier transform infrared spectroscopic investigation of the early hydration of Portland cement and the influence of sodium lignosulfonate10.1016/S0008-8846(99)00243-4 ↗
90. Determining cement composition by Fourier transform infrared spectroscopy10.1016/1065-7355(94)00031-X ↗
91. The effect of nanosilica addition on flowability, strength and transport properties of ultra high performance concrete10.1016/j.matdes.2014.02.051 ↗
92. Effective use of micro-silica extracted from rice husk ash for the production of high-performance and sustainable cement mortar10.1016/j.conbuildmat.2020.119589 ↗