Greening Pidgeon process with deoxidized diamond-wire sawing silicon waste

Diamond-wire sawing silicon waste (DWSSW) as a reductant of the Pidgeon process is beneficial for alleviating the high energy consumption of primary magnesium production. However, the oxygen in DWSSW exists in the form of SiO 2 coated on the Si surface, which is not conducive to the silicothermic reaction and thus affecting the yield of primary magnesium. In this study, we proposed a modified deoxidation method utilizing ammonium fluoride (NH 4 F) and hydrochloric acid (HCl) solutions to deoxidize the DWSSW. It was found that NH 4 F solution effectively reduced the oxygen content in DWSSW and the deoxidation efficiency increased with higher NH 4 F concentration. The addition of HCl further enhanced the deoxidation efficiency, leading to a minimum oxygen content of 1.31% in the deoxidized DWSSW. Transmission electron microscopy (TEM) images indicated a significant reduction in SiO 2 layer thickness, which improves the chemical reactivity of the material. The deoxidized DWSSW was subsequently employed as the reductant in the Pidgeon process to produce primary magnesium. Consequently, the reduction conversion of the Pidgeon process increased by 6.7% compared to raw DWSSW. This work not only provided an effective solution to reduce the oxygen content in DWSSW, but also expanded its application in Pidgeon process, promoting primary magnesium industry towards energy conservation and cost reduction.