Integration of tailored reduced graphene oxide nanosheets and electrospun polyamide-66 nanofabrics for a flexible supercapacitor with high-volume- and high-area-specific capacitance

Abstract Nanofiber fabric is firstly introduced to replace common microfiber fabrics as the platform for flexible supercapacitors. Nanofiber and microfiber electrodes can be simply fabricated using a dipping process that impregnates reduced graphene oxide (RGO) nanosheets into electrospun polyamide-66 (PA66) nanofiber and microfiber fabrics. RGO nanosheets are tailored to various sizes and only RGO with a medium diameter of 250–450 nm (denoted as M-RGO) can effectively penetrate the pores of nanofiber fabrics for constructing smooth conductive paths within PA66 nanofiber fabrics. The synergistic effect between suitable sizes of RGO nanosheets and nanofiber fabrics with a high specific area provides a symmetric supercapacitor composed of M-RGO/PA66 nanofiber fabric electrodes with high-volume and high-area specific capacitance ( C S,V and C S,A , equal to 38.79 F cm −3 and 0.931 F cm −2 at 0.5 A g −1 , respectively), which are much larger than that of a symmetric supercapacitor composed of RGO/PA66 microfiber fabric electrodes (8.52 F cm −3 and 0.213 F cm −2 at 0.5 A g −1 ). The effect of impregnating nanofiber fabrics with suitably sized RGO to promote C S,V and C S,A of flexible supercapacitors has been demonstrated.