Thermodynamic modeling of the Mg–Nd–Sr ternary system with key experimental investigation

The phase equilibria in the Mg-rich region of the Mg–Nd–Sr ternary system at 300 and 350 °C were established using equilibrated-sample method. Powder X-ray diffraction (XRD) technique and scanning electron microscopy (SEM) equipped with energy-dispersive spectroscopy (EDS) were used for phase composition determination. Four three-phase equilibria and four two-phase equilibria have been experimentally determined at both isothermal sections of 300 and 350 °C. The phase equilibria relationships in the Mg-rich side were studied. The major invariant reaction temperatures of vertical sections with 80 at. % Mg and 10 at. % Sr were determined with differential scanning calorimetry (DSC) test. Moreover, thermodynamic modeling of Mg–Nd–Sr ternary system has been carried out by CALPHAD method based on the present key experimental results. The liquid solution was described using the modified quasi-chemical model in the pair approximation (MQMPA). The compound energy formalism (CEF) was used for the solid phases. The present obtained thermodynamic database of Mg–Nd–Sr ternary system will provide an important support for the Mg-based biodegradable implant development.