Experimental investigation and thermodynamic assessment of the Mn–Zr system

Abstract The Mn–Zr binary system has been investigated via experimental measurements and thermodynamic calculations. In order to investigate phase equilibria in the Mn–Zr system, five alloys were prepared by arc melting under vacuum. All alloys were examined by means of X-ray diffraction, scanning electron microscopy and electron probe microanalysis after annealing at 650 °C for 70 days or 950 °C for 30 days. The homogeneity range of ZrMn2 was determined to be from 25.0 to 33.2 at.% Zr at 950 °C and from 26.7 to 34.3 at.% Zr at 650 °C. The solubility of Mn in (αZr) was 1.6 at.% Mn, while that of Zr in (αMn) was 0.2 at.% Zr at 650 °C. The invariant reaction temperatures of liquid → ZrMn2 + (βZr) and (βZr) → ZrMn2 + (αZr) were determined to be 1131 and 785 °C, respectively. A thermodynamic assessment of the Mn–Zr system was conducted by taking into account the present experimental results and reliable literature data. The calculated results using the presently obtained parameters can well reproduce the experimental data.