Experimental reinvestigation and thermodynamic description of Bi-Te binary system

Abstract The Bi-Te phase diagram was determined by equilibrium alloy method, combined with electron probe microanalysis (EPMA), X-ray diffraction (XRD) and thermal analysis (DSC). The experimental result shows that there is a β-phase with a large composition range at low temperature, while Bi2Te and Bi4Te3 are relatively stable in the solid-liquid region. A consistent phase diagram that covers the experimental findings has been achieved. Based on the new experimental phase diagram, coupling with the reported thermodynamic data, the thermodynamic optimization of the Bi-Te binary system was carried out with the help of CALPHAD approach. A group of reasonable thermodynamic parameters was obtained.