Studies on nanocrystalline zinc coating
Source abstract
Abstract
Nano zinc coatings were deposited on mild steel by electrodeposition. The effect of additive on the morphology of crystal size on zinc deposit surface and corrosion properties were investigated. Corrosion tests were performed for dull zinc deposits and bright zinc deposits in aqueous NaCl solution (3·5 wt.%) using electrochemical measurements. The results showed that addition of additive in the deposition process of zinc significantly increased the corrosion resistance. The surface morphology of the zinc deposits was studied by scanning electron microscopy (SEM). The preferred orientation and average size of the zinc electrodeposited particles were obtained by X-ray diffraction analysis. The particles size was also characterized by TEM analysis.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Electrodeposition and Electroless Coatings · Microstructure and mechanical properties · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (22)
Show source-provided references
1. Abou-Krisha M 2005 J. Appl. Surf. Sci. 252 103510.1016/j.apsusc.2005.01.161 ↗
2. Anderson P W and Hasegawa H 1955 Phys. Rev. 100 67510.1103/PhysRev.100.675 ↗
3. Arthoba Naik Y 2002 Development and optimization of brighteners for industrial zinc electroplating from acid and noncyanide alkaline baths, Ph.D. thesis, Kuvempu University, Shankaraghatta
4. Arthoba Naik Y and Venkatesha T V 2005 Bull. Mater. Sci. 28 49510.1007/BF02711243 ↗
5. Arthoba Naik Y, Venkatesha T V and Vasudeva Nayak P 2000 Bull. Electrochem. 16 481
6. Arthoba Naik Y, Venkatesha T V and Vasudeva Nayak P 2001 Indian J. Chem. Technol. 8 390
7. Cheung C, Wood D and Erb U 1996 in Processing and properties of nanocrystalline materials (ed.) C Suryanarayana (Warrendale, PA: TMS publication) p. 479
8. Ebrahimi F and Ahmed Z 2003 Mater. Charact. 49 37310.1016/S1044-5803(02)00305-4 ↗
9. Ebrahimi F and Li H Q 2003 Rev. Adv. Mater. Sci. 5 134
10. Ebrahimi F, Kong D, Matthews T E and Zhai Q 1998 in Processing and fabrication of advanced materials VII (eds) T S Srivastan and K A Khor (Warrendale, PA: TMS Publication) p. 509
11. Ebrahimi F, Bourne G R, Kelley M S and Matthews T E 1999 Nanostruct. Mater. 11 34310.1016/S0965-9773(99)00050-1 ↗
12. Erb U, Palumbo G, Zugic R and Aust K T 1996 in Processing and properties of nanocrystalline materials (ed.) C Suryanarayana (Warrendale, PA: TMS publication) p. 93
13. Ei-Sherrik A M and Erb U 1995 Mater. Sci. Eng. 30 5743
14. Inturi R B and Szklarska-Smialowska Z 1992 Corrosion 48 39810.5006/1.3315951 ↗
15. Juarez Beatriz H and Alonso Concepcion 2006 J. Appl. Electrochem. 36 49910.1007/s10800-005-9106-7 ↗
16. Muralidhara H B, Arthoba Naik Y and Venkatesha T V 2006 Bull. Mater. Sci. 29 49710.1007/BF02914081 ↗
17. Morgan K L, Ahmed Z and Ebrahimi F 2001 MRS Proc. 3.11.1 63410.1557/PROC-634-B3.11.1 ↗
18. Ohtsuka T, Kuwamura E, Komori A and Uchida T 1995 ISIJ Int. 35 89210.2355/isijinternational.35.892 ↗
19. Senthil Kumar A, Senthil Raja Pandian C, Ayyapparaju J and Ramesh Bapu G N K 2001 B. Electrochem. 17 379
20. Suryanarayana C 1995 Inter. Mater. Rev. 40 4110.1179/imr.1995.40.2.41 ↗
21. Tellkamp V and Lavernia E 1999 Nanostruct. Mater. 12 24910.1016/S0965-9773(99)00110-5 ↗
22. Zener C 1951 Phys. Rev. 82 40310.1103/PhysRev.82.403 ↗