Electrical and microstructural properties of CaTiO 3 -doped K 1/2 Na 1/2 NbO 3 -lead free ceramics
Source abstract
Abstract
Microstructure, electrical properties and dielectric behaviour of K1/2Na1/2NbO3 (KNN) and CaTiO3-modified K1/2Na1/2NbO3 (CTO-KNN) systems, were investigated. Discs doped with 0 to 0·55% mol of CaTiO3 (CTO) were sintered at 1125°C for 2 h. Although minority phases were found in doped samples, CaTiO3 was not detected. It was also observed that CTO changed the microstructure and grain size of KNN drastically. Also, the Curie temperature and permittivity values decreased. Addition of CTO between 0·15 and 0·45 mol% decreases the density and dielectric values. Samples prepared with higher content of CTO than 0·45 mol% showed better electrical properties.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Ferroelectric and Piezoelectric Materials · Microwave Dielectric Ceramics Synthesis · Multiferroics and related materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (28)
Show source-provided references
1. Alkoy E M and Papila M 2010 Ceram. Int. 36 192110.1016/j.ceramint.2010.03.018 ↗
2. Birol H, Damjanovic D and Setter B 2006 J. Eur. Ceram. Soc. 26 86110.1016/j.jeurceramsoc.2004.11.022 ↗
3. Bobnar V, Bernard J and Kosec M 2004 Appl. Phys. Lett. 85 99410.1063/1.1779947 ↗
4. Chandra A, Ranjan R, Singh D P, Khare N and Pandey D 2006 J. Phys. Condens. Matter 18 297710.1088/0953-8984/18/11/005 ↗
5. Chang R-C, Chu S-Y, Lin Y-F, Hong C-S, Kao P-C and Lu C-H 2007a Sensors Actuator A138 355
6. Chang R-C, Chu S-Y, Lin Y-F, Hong C-S and Wong Y-P 2007b J. Eur. Ceram. Soc. 27 445310.1016/j.jeurceramsoc.2007.02.218 ↗
7. Chang Y, Yang Z, Wei L and Liu B 2006 Mater. Sci. Eng. A437 30110.1016/j.msea.2006.08.046 ↗
8. Chu S Y, Water W, Juang Y D, Liaw J T and Dai S B 2003 Ferroelectrics 287 2310.1080/00150190390200767 ↗
9. Du H, Qu S, Che J, Liu Z, Wei X and Pei Z 2005 Mater. Sci. Eng. A393 3610.1016/j.msea.2004.09.046 ↗
10. Guo Y, Kakimoto K and Ohsato H 2004 Solid State Commun. 129 27910.1016/j.ssc.2003.10.026 ↗
11. Kosec M, Bobnar V, Hrovat M, Bernard J, Malic B and Holc J 2004 J. Mater. Res. 19 184910.1557/JMR.2004.0229 ↗
12. Maeder M D, Damjanovic D and Setter N 2004 J. Electroceram. 13 38510.1007/s10832-004-5130-y ↗
13. Malic B, Bernard J, Holc J, Jenko D and Kosec M 2005 J. Eur. Ceram. Soc. 25 270710.1016/j.jeurceramsoc.2005.03.127 ↗
14. Matsubara M, Yamaguchi T, Sakamoto W, Kikuta K, Yogo T and Hirano S 2005 J. Am. Ceram. Soc. 88 119010.1111/j.1551-2916.2005.00229.x ↗
15. Ringgaard E and Wurlitzer T 2005 J. Eur. Ceram. Soc. 25 270110.1016/j.jeurceramsoc.2005.03.126 ↗
16. Saito Y, Takao H, Tani T, Nonoyama T, Takatori K, Homma T, Nagaya T and Nakamura M 2004 Nature 432 8410.1038/nature03028 ↗
17. Sawada T, Ando A, Sakabe Y, Damjanovic D and Setter N 2003 Jpn. J. Appl. Phys. 42 609410.1143/JJAP.42.6094 ↗
18. Suzuki M, Nagata H, Ohara J, Funakubo H and Takenaka T 2003 Jpn. J. Appl. Phys. 42 609010.1143/JJAP.42.6090 ↗
19. Tang F S, Du H L, Liu D J, Luo F and Zhou W C 2007 J. Inorg. Mater. 22 0323
20. Wang K, Li J and Liu N F 2008 Appl. Phys. Lett. 93 09290410.1063/1.2977551 ↗
21. Wang X, Kwork K, Tang X, Chan H and Choy Z 2004 Solid State Commun. 129 31910.1016/j.ssc.2003.10.017 ↗
22. Wu J G, Xiao D, Wang Y, Zhu J, Yu P and Jiang Y 2007 J. Appl. Phys. 102 11411310.1063/1.2822454 ↗
23. Wu J G, Xiao D Q, Wang Y Y, Zhu J G and Yu P 2008a J. Appl. Phys. 103 02410210.1063/1.2830997 ↗
24. Wu J, Xiao D, Wang Y, Wu W, Zhang B, Li J and Zhu J 2008b Scr. Mater. 59 75010.1016/j.scriptamat.2008.06.011 ↗
25. Yang Z P, Chang Y F and Li H 2005 Mater. Res. Bull. 40 211010.1016/j.materresbull.2005.07.010 ↗
26. Yu Z, Ang C, Guo R and Bhalla A S 2002 J. Appl. Phys. 92 148910.1063/1.1487435 ↗
27. Zhou C-H and Xin X-Y 2007 Bull. Mater. Sci. 30 57510.1007/s12034-007-0090-x ↗
28. Zhou C-H, Liu X-Y, Li W-Z and Yuan C-L 2009 Bull. Mater. Sci. 32 9910.1007/s12034-009-0015-y ↗