AC conductivity and broadband dielectric spectroscopy of a poly(vinyl chloride)/poly(ethyl methacrylate) polymer blend

Alternating-current (ac) conductivity and dielectric relaxation behaviour of a poly(vinyl chloride)/poly(ethyl methacrylate) polymer blend have been investigated intensively in a frequency range from $$1 \times 10^-1$$ to $$2 \times 10⁷$$ Hz through a temperature range from 300 to 393 K. The variation of $$\sigma _{\mathrm{ac}}$$ of pure and polyblend samples showed a plateau region at high temperature and low frequency and this plateau region is decreased with decreasing temperature. Values of the exponent n are less than unity indicative of the correlated barrier hopping for conduction. The values of the exponent n are used to calculate the binding energy ( $$W_{\mathrm{m}})$$ of the charge carriers. The investigation of the frequency dependence of $$\varepsilon ^\prime $$ for pure and polyblend samples showed a dielectric dispersion. The high values of dielectric constant at a low frequency and high temperature are attributed to the effects of space charge due to the electrode polarization. The complex electric modulus (M*) of pure and polyblend samples has been investigated. It is found that the real part of the complex electric modulus, $$M^\prime $$ is increased non-linearly as the frequency increased and reached the steady state at higher frequencies for all samples. On the other hand, the imaginary part of the complex electric modulus, $$M^{\prime \prime} $$ is characterized by a relaxation peak. The different modes of relaxation, such as interfacial polarization and dipolar relaxation, are detected in low and high frequency regions in the variation plot of $$M^{\prime \prime} $$ against frequency. The activation energy values of both interfacial polarization and $$\upalpha $$ -relaxation are calculated.