Studies on electrical conductivity and dielectric behaviour of PVdF–HFP–PMMA–NaI polymer blend electrolyte

Polymer blend electrolytes composed of poly(vinylidene fluoride-co-hexafluoro-propylene), poly(methyl methacrylate) and 1·0 M NaI as salt have been synthesized using solution caste technique by varying the PVdF(HFP)–PMMA blend concentration ratio systematically. A.c. impedance studies were performed to evaluate the ionic conductivity of the polymer electrolyte films. The highest ionic conductivity at room temperature for [PVdF(HFP)–PMMA(4:1)](20 wt%) – [NaI(1·0 M)](80 wt%) system is found to be 1·67 × 10 − 2 S cm − 1. XRD studies reveal complete complexation of the salt in the polymeric blend systems. The temperature dependence conductivity has been performed in the range of 303–373 K and it is observed that it obeys the Arrhenius behaviour. It has been observed that the dielectric constant, e r and dielectric loss, e i, increases with temperature in the lower frequency region and is almost negligible in the higher frequency region. This behaviour can be explained on the basis of electrode polarization effects. Plot of real part, M r and imaginary part, M i vs frequency indicates that the systems are predominantly ionic conductors. The phenomenon suggests a plurality of relaxation mechanism.