Realizing NiO nanocrystals from a simple chemical method
Source abstract
Abstract
Nanocrystalline NiO has been prepared successfully by a simple chemical route using NiCl2·6H2O and NaOH aqueous solution at a temperature of 70°C. The prepared material has been characterized from XRD, SEM, and M–H characteristics. It has been found that NiO nanocrystals have been formed which shows a superparamagnetic/superantiferromagnetic behaviour.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Transition Metal Oxide Nanomaterials · Multiferroics and related materials · Magnesium Oxide Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. Anderson P W 1950 Phys. Rev. 79 35010.1103/PhysRev.79.350 ↗
2. Biju V and Khadar M A 2001 Mater. Sci. Engg. A304–306 81410.1016/S0921-5093(00)01581-1 ↗
3. Bødker F, Hansen M F, Bender Koch C, Lefmann K and Mørup S 2000a Phys. Rev. B61 682610.1103/PhysRevB.61.6826 ↗
4. Bødker F, Hansen M F, Koch C B and Mørup S 2000b J. Magn. Magn. Mater. 221 3210.1016/S0304-8853(00)00392-9 ↗
5. Chen Qi and Zhang Z John 1998 Appl. Phys. Lett. 73 315610.1063/1.122704 ↗
6. Deki S, Yanagimoto H, Hiraoka S, Akamatsu K and Gotoh K 2003 Chem. Mater. 15 491610.1021/cm021754a ↗
7. Eberhart J P 1989 Analyse Structurale et Chimiques des Matériaux (Paris: Ed. Dunod) 46 p. 407
8. Gleiter H 2000 Acta Mater. 48 110.1016/S1359-6454(99)00285-2 ↗
9. Khadar M Abdul, Biju V and Akihisa Inoue 2003 Mater. Res. Bull. 38 134110.1016/S0025-5408(03)00139-9 ↗
10. Kittel C 1974 Introduction to solid state physics (New Delhi: Wiley Eastern Private Limited) p. 570
11. Kodama R H, Makhlouf S A and Berkowitz A E 1997 Phys. Rev. Lett. 79 139310.1103/PhysRevLett.79.1393 ↗
12. McHenry M E and Laughlin D E 2000 Acta Mater. 48 22310.1016/S1359-6454(99)00296-7 ↗
13. Neel L 1961 C. R. Acad. Sci. Paris 252 4075, 253 9, 203, 1286
14. Neel L 1962 Low temperature physics (eds) C Dewitt et al (New York: Gordon and Breach) p. 413
15. Schuele W J and Deetscreek V D 1962 J. Appl. Phys. Suppl. 33 113610.1063/1.1728633 ↗
16. Singer J R 1956 Phys. Rev. 104 92910.1103/PhysRev.104.929 ↗
17. Wang X, Li L, Zhang Y, Wang S, Zhang Z, Fei L and Qian Y 2006 Cryst. Growth & Des. 6 216310.1021/cg060156w ↗
18. Wildpaner V 1974 Zeitschrift fur Physik A Hadrons and Nuclei 270 215
19. Xu C, Hong K, Liu S, Wang G and Zhao X 2003 J. Cryst. Growth 255 30810.1016/S0022-0248(03)01246-6 ↗
20. Zhang X X, Tejada J, Hernandez J M and Ziolo R F 1997 Nanostruct. Mater. 9 30110.1016/S0965-9773(97)90070-2 ↗
21. Zheng Y and Zhang M 2007 Mater. Lett. 61 396710.1016/j.matlet.2006.12.072 ↗