Influencia de la molienda en la energía superficial de fritas para esmaltes

A. Tamayo, F. Rubio, J. L. Oteo, J. Rubio

Abstract

In this work has been studied the influence of the milling process of two ceramic frits used in the ceramic tile industry. Both glass frits were of similar chemical composition changing SiO2 by 5% of B2O3 and both of them were water or dry milled. Glass frit surfaces were characterized by FT-IR, Karl-Fischer (K-F) titration and Inverse Gas Chromatography at Infinite Dilution (IGC-ID). By K-F titration it was observed that water milled frits presented 28 and 26 OH groups for 100 A2 if they do not contain or contain boron, respectively. These surface changes are also observed by IGC-ID. Thus, the glass frit without boron and dry milled presented the highest dispersive surface energy (44 mJ.m-2) and the less acidic constant (0.13 kJ.mol-1). Both glass frits are amphoteric with acidic and base surface active sites, and that frit without boron presents the higher basicity. Milling process influences in the acid-base surface characteristics of both frits by increasing the basicity for the one without boron and increasing for the other one. This has been assigned to the different location of hydroxyl groups where the higher interaction is the one that does not contain boron and dry milled as K-F results. Se ha estudiado el proceso de molienda en dos fritas de la industria cerámica. Las dos fritas, de composiciones similares pero en una se ha sustituido parte de la sílice por 5% de óxido de boro, fueron molidas por vía seca o húmeda y se caracterizaron mediante FT-IR, valoración Karl-Fischer e IGC-ID. Mediante valoración se han determinado los contenidos en moléculas de agua e hidroxilos. El mayor contenido en hidroxilos lo posee la frita sin boro seguida de la de boro ambas molidas en húmedo, poseyendo 28 y 26 grupos OH por cada 100 A2, respectivamente. Estos resultados coinciden con IGC-ID, sin embargo es la frita sin boro molida en seco la de mayor energía superficial (44 mJ.m-2) y constante ácida (0.13 kJ.mol-1). Aunque las dos fritas tienen centros ácidos y básicos, la que no contiene boro presenta mayor basicidad que la de boro. La molienda influye de forma diferente en las dos fritas aumentando la basicidad en la que no tiene boro y disminuyendo en la que lo contiene. Esto se debe a la localización de los grupos hidroxilo en la superficie de la frita, poseyendo mayor interacción con los grupos hidroxilo la frita sin boro molida en húmedo.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Adsorption, diffusion, and thermodynamic properties of materials · Chemical and Environmental Engineering Research · Scientific Measurement and Uncertainty Evaluation

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (24)

Show source-provided references
1. 1. J. R. Taylor, A. C. Bull. Ceramic Glaze Technology. Institute of Ceramics. 1986
2. 3. R. Galindo. Pastas y Vidriados en la fabricación de pavimentos y revestimientos cerámicos. Faenza Editrice Iberica. Castellón. 1994
3. 10.3989/cyv.2001.v40.i2.75410.3989/cyv.2001.v40.i2.754 ↗
4. 10.1016/0021-9797(83)90314-410.1016/0021-9797(83)90314-4 ↗
5. 10.1016/S0021-9673(00)00487-810.1016/S0021-9673(00)00487-8 ↗
6. 10. A. Tamayo, S. Pérez-Villar, F. Rubio, M. A. Rodríguez, J. Rubio, J.L. Oteo. Caracterización estructural de vidrios del sistema SiO2- B2O3-Na2O mediante espectroscopías IR y Raman. Bol. Soc. Esp. Ceram. Vidrio. 48, 5, 237-243, 2009.
7. 10.3989/cyv.2008.v47.i2.20010.3989/cyv.2008.v47.i2.200 ↗
8. 10.1016/j.powtec.2005.05.02910.1016/j.powtec.2005.05.029 ↗
9. 13. R. Pe-a-Alonso, L. Téllez, J. Rubio, F. Rubio. Surface Chemicals and physical properties of TEOS-TBOT-PDMS hybrid materials. J. Sol-Gel Sci. Tech. 38, 133-145, 2006
10. 10.1007/BF0226238510.1007/BF02262385 ↗
11. 10.1111/j.1151-2916.1969.tb11199.x10.1111/j.1151-2916.1969.tb11199.x ↗
12. 16. J. C. Díez-Masa. Incorporación de átomos de nitrógeno a la superficie del vidrio Pyrex y su aplicación a la cromatografía de gases. Tesis Doc. U.Complutense. Madrid. 1977
13. 17. M.C. Bautista, J. Rubio, J. L. Oteo. Adsorción de n-alcanos sobre fibras de vidrio silicoalauminosas (tratadas térmicamente) en la zona de recubrimiento cero. Bol. Soc. Esp. Ceram. Vidrio. 31 (3) 349-352, 1992
14. 10.1021/i300008a03110.1021/i300008a031 ↗
15. 10.1007/BF0141042110.1007/BF01410421 ↗
16. 10.1016/j.jcis.2010.09.02810.1016/j.jcis.2010.09.028 ↗
17. 10.1016/S0927-7757(98)00563-910.1016/S0927-7757(98)00563-9 ↗
18. 22. I. Ulkem, H. P. Schreiber. The role of interactions at interfaces of glass-fiber reinforced composites. Comp. Interfaces. 2 (4) 253-263, 199410.1163/156855494X00111 ↗
19. 10.1111/j.1551-2916.2011.04810.x10.1111/j.1551-2916.2011.04810.x ↗
20. 10.1016/S0001-8686(03)00066-610.1016/S0001-8686(03)00066-6 ↗
21. 2. E. Sanchez, J. E. Enrique. Materias primas empleadas en la fabricación de fritas cerámicas. I Jornadas sobre materias primas en la industria cerámica. ATC. Castellón. 22 y 23 Mayo, 199610.1016/S0001-8686(03)00066-6 ↗
22. 4. F. Sanmiguel, V. Ferrando, J. L. Amorós, M. J. Orts, M. F.Gazulla, P. Gómez. Solubilidad de fritas en suspensiones de esmalte. Influencia de algunas variables de operación sobre la cinética del proceso. Pp. 81 – 95 en Qualicer 199810.1016/S0001-8686(03)00066-6 ↗
23. 6. J. L. Amorós.Vidriados para pavimentos y revestimientos cerámicos. Evolución y perspectivas. Pp. 11-15 en Qualicer-199210.1016/S0001-8686(03)00066-6 ↗
24. 7. Martos, C; Rubio, F; Rubio, J; Oteo, J. L. Surface energy of silica-TEOS-PDMS ormosils. journal of sol-gel science and technology. 20 (2) 197-210, 200110.1016/S0001-8686(03)00066-6 ↗